- W2625561906 abstract "Compaction, sintering and physical properties of silver powder were investigated. The silver powder was uniaxially compacted into a cylindrical specimen using compaction pressures of 13.79, 27.58, 41.37 and 55.16 MPa. Compacted parts were sintered at 700, 800 and 900°C in argon atmospheres. In addition, compacted parts were also sintered in vacuum at 900°C. For the sintering temperatures of 700 and 800°C, it was found that the sintered density increased as the compaction pressure increased below 40 MPa, while the sintered density decreased at a compaction pressure above 40 MPa. At the sintering temperature of 900°C, the sintered density decreased with increasing compaction pressure. The highest sintered density of 10.22 g⋅cm-3 (67.41 % relative density) was obtained at a temperature of 900°C under argon atmosphere for compaction pressure of 13.79 MPa. At this sintering temperature, vacuum sintering gave a slightly higher sintered density than argon atmosphere. Moreover, the difference in shrinkage of thickness and diameter of the sintered parts was observed. The diameter has higher shrinkage than the thickness. The weight of the specimen did not affect the sintered density, whereas the compaction pressure, sintering temperature and atmosphere influenced the sintered density." @default.
- W2625561906 created "2017-06-23" @default.
- W2625561906 creator A5016186196 @default.
- W2625561906 creator A5036679358 @default.
- W2625561906 date "2010-01-01" @default.
- W2625561906 modified "2023-09-26" @default.
- W2625561906 title "Study of process parameters in conventional powder metallurgy of silver" @default.
- W2625561906 cites W1481490178 @default.
- W2625561906 cites W1650538669 @default.
- W2625561906 cites W1964294953 @default.
- W2625561906 cites W2011016961 @default.
- W2625561906 cites W2016388302 @default.
- W2625561906 cites W2024215809 @default.
- W2625561906 cites W2412228358 @default.
- W2625561906 hasPublicationYear "2010" @default.
- W2625561906 type Work @default.
- W2625561906 sameAs 2625561906 @default.
- W2625561906 citedByCount "0" @default.
- W2625561906 crossrefType "journal-article" @default.
- W2625561906 hasAuthorship W2625561906A5016186196 @default.
- W2625561906 hasAuthorship W2625561906A5036679358 @default.
- W2625561906 hasConcept C121332964 @default.
- W2625561906 hasConcept C159985019 @default.
- W2625561906 hasConcept C180145272 @default.
- W2625561906 hasConcept C184779094 @default.
- W2625561906 hasConcept C191897082 @default.
- W2625561906 hasConcept C192562407 @default.
- W2625561906 hasConcept C196715460 @default.
- W2625561906 hasConcept C2777581544 @default.
- W2625561906 hasConcept C547737533 @default.
- W2625561906 hasConcept C7794659 @default.
- W2625561906 hasConcept C82455628 @default.
- W2625561906 hasConceptScore W2625561906C121332964 @default.
- W2625561906 hasConceptScore W2625561906C159985019 @default.
- W2625561906 hasConceptScore W2625561906C180145272 @default.
- W2625561906 hasConceptScore W2625561906C184779094 @default.
- W2625561906 hasConceptScore W2625561906C191897082 @default.
- W2625561906 hasConceptScore W2625561906C192562407 @default.
- W2625561906 hasConceptScore W2625561906C196715460 @default.
- W2625561906 hasConceptScore W2625561906C2777581544 @default.
- W2625561906 hasConceptScore W2625561906C547737533 @default.
- W2625561906 hasConceptScore W2625561906C7794659 @default.
- W2625561906 hasConceptScore W2625561906C82455628 @default.
- W2625561906 hasIssue "1" @default.
- W2625561906 hasLocation W26255619061 @default.
- W2625561906 hasOpenAccess W2625561906 @default.
- W2625561906 hasPrimaryLocation W26255619061 @default.
- W2625561906 hasRelatedWork W1662288042 @default.
- W2625561906 hasRelatedWork W1973174957 @default.
- W2625561906 hasRelatedWork W1997798599 @default.
- W2625561906 hasRelatedWork W2013213288 @default.
- W2625561906 hasRelatedWork W2107918688 @default.
- W2625561906 hasRelatedWork W2108435275 @default.
- W2625561906 hasRelatedWork W2111681516 @default.
- W2625561906 hasRelatedWork W2127059975 @default.
- W2625561906 hasRelatedWork W2184923834 @default.
- W2625561906 hasRelatedWork W2242991906 @default.
- W2625561906 hasRelatedWork W2258746273 @default.
- W2625561906 hasRelatedWork W2328006341 @default.
- W2625561906 hasRelatedWork W2361984538 @default.
- W2625561906 hasRelatedWork W2369880666 @default.
- W2625561906 hasRelatedWork W2547505582 @default.
- W2625561906 hasRelatedWork W2884908378 @default.
- W2625561906 hasRelatedWork W2897458713 @default.
- W2625561906 hasRelatedWork W2915663279 @default.
- W2625561906 hasRelatedWork W2968952854 @default.
- W2625561906 hasRelatedWork W3100629084 @default.
- W2625561906 hasVolume "20" @default.
- W2625561906 isParatext "false" @default.
- W2625561906 isRetracted "false" @default.
- W2625561906 magId "2625561906" @default.
- W2625561906 workType "article" @default.