• W2669373982 abstract "Eutectic Sn-Zn alloy is considered as one of the best lead free solder alloys in microelectronic industry. That motivates our group to select different weight percentage of Antimony (Sb) (0.5, 1.0, and 1.5 wt%) as an alloying to Sn-9.0Zn-0.5 Al solder alloy. The thermal behavior, microstructure modification as well as tensile properties of the new developed solder alloys were investigated. A slight increment of the melting temperature (∼ 1 °C) was recorded using differential scanning calorimetry (DSC) after additions of Sb. For 1.5 wt% of Sb, two endothermic peaks at 200.8 °C and 201.5 °C were observed, which are assigned as hypoeutectic Sn-Zn composition. X-ray diffraction (XRD) measurements confirm the existence of β-Sn phase, α-Zn phase, and Sb-Sn intermetallic compounds (IMCs). Scanning electron microscope (SEM) images indicate that the Sb additives refine the microstructure and form a uniform distribution of IMCs in the matrix of solder. The road-like α-Zn phase, Al6Zn3Sn and SbSn IMCs were clearly appeared in β-Sn matrix, which are responsible of the enhancement in tensile strength. Moreover, α-Zn phases in the Sn-9Zn-0.5Al-1.5Sb alloy were modified as needle-like, broken enormously, depleted, and circle shapes. Generally, The Sb-containing alloys have higher ultimate tensile strength (UTS) and lower elongation than Sb-free solder alloy due to the solid solution and second phase dispersion strengthening effect. The relationship between UTS and temperature follow the Arrhenius law. The average activation energies (Q) were found to be 44.4 ± 1.0 kJ/mol, and the average stress exponents (n) were usually around 5.3 ± 0.45, which are close to pipe diffusion controlled creep in β-Sn matrix." @default.
• W2669373982 created "2017-06-30" @default.
• W2669373982 creator A5077741331 @default.
• W2669373982 creator A5084336160 @default.
• W2669373982 creator A5091063418 @default.
• W2669373982 date "2017-07-01" @default.
• W2669373982 modified "2023-09-27" @default.
• W2669373982 title "Influence of small addition of antimony (Sb) on thermal behavior, microstructural and tensile properties of Sn-9.0Zn-0.5Al Pb-free solder alloy" @default.
• W2669373982 cites W185935660 @default.
• W2669373982 cites W1965592548 @default.
• W2669373982 cites W1965780255 @default.
• W2669373982 cites W1979064607 @default.
• W2669373982 cites W1984148845 @default.
• W2669373982 cites W1993167814 @default.
• W2669373982 cites W1996270776 @default.
• W2669373982 cites W2002550303 @default.
• W2669373982 cites W2003806385 @default.
• W2669373982 cites W2008044737 @default.
• W2669373982 cites W2010748940 @default.
• W2669373982 cites W2016506311 @default.
• W2669373982 cites W2017762857 @default.
• W2669373982 cites W2018468235 @default.
• W2669373982 cites W2024053326 @default.
• W2669373982 cites W2025122868 @default.
• W2669373982 cites W2029490398 @default.
• W2669373982 cites W2031686472 @default.
• W2669373982 cites W2039346819 @default.
• W2669373982 cites W2040512552 @default.
• W2669373982 cites W2041698616 @default.
• W2669373982 cites W2049114376 @default.
• W2669373982 cites W2050231231 @default.
• W2669373982 cites W2052534747 @default.
• W2669373982 cites W2052690499 @default.
• W2669373982 cites W2061796877 @default.
• W2669373982 cites W2069190096 @default.
• W2669373982 cites W2072854364 @default.
• W2669373982 cites W2074857244 @default.
• W2669373982 cites W2078766094 @default.
• W2669373982 cites W2091280772 @default.
• W2669373982 cites W2099537633 @default.
• W2669373982 cites W2125928419 @default.
• W2669373982 cites W2132605765 @default.
• W2669373982 cites W2164838859 @default.
• W2669373982 cites W2165611332 @default.
• W2669373982 cites W2168111264 @default.
• W2669373982 cites W2563303337 @default.
• W2669373982 doi "https://doi.org/10.1016/j.msea.2017.06.092" @default.
• W2669373982 hasPublicationYear "2017" @default.
• W2669373982 type Work @default.
• W2669373982 sameAs 2669373982 @default.
• W2669373982 citedByCount "20" @default.
• W2669373982 countsByYear W26693739822017 @default.
• W2669373982 countsByYear W26693739822018 @default.
• W2669373982 countsByYear W26693739822019 @default.
• W2669373982 countsByYear W26693739822020 @default.
• W2669373982 countsByYear W26693739822021 @default.
• W2669373982 countsByYear W26693739822022 @default.
• W2669373982 countsByYear W26693739822023 @default.
• W2669373982 crossrefType "journal-article" @default.
• W2669373982 hasAuthorship W2669373982A5077741331 @default.
• W2669373982 hasAuthorship W2669373982A5084336160 @default.
• W2669373982 hasAuthorship W2669373982A5091063418 @default.
• W2669373982 hasConcept C112950240 @default.
• W2669373982 hasConcept C121332964 @default.
• W2669373982 hasConcept C159985019 @default.
• W2669373982 hasConcept C178790620 @default.
• W2669373982 hasConcept C18168003 @default.
• W2669373982 hasConcept C185592680 @default.
• W2669373982 hasConcept C191897082 @default.
• W2669373982 hasConcept C192562407 @default.
• W2669373982 hasConcept C26771246 @default.
• W2669373982 hasConcept C27501479 @default.
• W2669373982 hasConcept C2780026712 @default.
• W2669373982 hasConcept C39519442 @default.
• W2669373982 hasConcept C44280652 @default.
• W2669373982 hasConcept C50296614 @default.
• W2669373982 hasConcept C541565711 @default.
• W2669373982 hasConcept C87976508 @default.
• W2669373982 hasConcept C97355855 @default.
• W2669373982 hasConceptScore W2669373982C112950240 @default.
• W2669373982 hasConceptScore W2669373982C121332964 @default.
• W2669373982 hasConceptScore W2669373982C159985019 @default.
• W2669373982 hasConceptScore W2669373982C178790620 @default.
• W2669373982 hasConceptScore W2669373982C18168003 @default.
• W2669373982 hasConceptScore W2669373982C185592680 @default.
• W2669373982 hasConceptScore W2669373982C191897082 @default.
• W2669373982 hasConceptScore W2669373982C192562407 @default.
• W2669373982 hasConceptScore W2669373982C26771246 @default.
• W2669373982 hasConceptScore W2669373982C27501479 @default.
• W2669373982 hasConceptScore W2669373982C2780026712 @default.
• W2669373982 hasConceptScore W2669373982C39519442 @default.
• W2669373982 hasConceptScore W2669373982C44280652 @default.
• W2669373982 hasConceptScore W2669373982C50296614 @default.
• W2669373982 hasConceptScore W2669373982C541565711 @default.
• W2669373982 hasConceptScore W2669373982C87976508 @default.
• W2669373982 hasConceptScore W2669373982C97355855 @default.
• W2669373982 hasLocation W26693739821 @default.
• W2669373982 hasOpenAccess W2669373982 @default.

• next