- W2734398488 abstract "Abstract In this work, the effects of tempering at three high temperatures (660, 680 and 700 °C) for different holding times (5 min to 16 h) on the secondary hardening in Nb-bearing and Nb-Mo-bearing bainitic steel strips were investigated. It was found that with 0.3 wt% Mo addition in Nb-Mo-bearing bainitic steel strip, the peak hardening occurred with a significant increment in hardness (up to 40 HV) after approximately 10 min of tempering at all temperatures (660, 680 and 700 °C). In contrast, for the Nb-bearing steel strip, the corresponding increment in hardness was small (about 15 HV). The microstructural evolutions of Nb-bearing and Nb-Mo-bearing steel strips during tempering at 700 °C were investigated with scanning electron microscopy, electron backscattered diffraction, and transmission electron microscopy. It was found that during tempering, bainitic ferrite platelets in Nb-Mo-bearing steel strips remained much more stable and had a higher dislocation density than those in Nb-bearing steel strips. High-resolution transmission electron microscopy provided strong evidence that the Mo addition had significant effects on suppressing the annihilation rate of dislocations and retarding the coarsening rate of nanometer-sized carbides at higher temperatures, leading to a remarkable resistance to softening after secondary hardening." @default.
- W2734398488 created "2017-07-21" @default.
- W2734398488 creator A5027080363 @default.
- W2734398488 creator A5051096110 @default.
- W2734398488 creator A5055739237 @default.
- W2734398488 creator A5065801579 @default.
- W2734398488 creator A5068209077 @default.
- W2734398488 creator A5076412762 @default.
- W2734398488 date "2017-09-01" @default.
- W2734398488 modified "2023-09-30" @default.
- W2734398488 title "Microstructural evolutions of low carbon Nb/Mo-containing bainitic steels during high-temperature tempering" @default.
- W2734398488 cites W1965773325 @default.
- W2734398488 cites W1985473822 @default.
- W2734398488 cites W1988217236 @default.
- W2734398488 cites W1988294676 @default.
- W2734398488 cites W1990795912 @default.
- W2734398488 cites W1996249420 @default.
- W2734398488 cites W2003358250 @default.
- W2734398488 cites W2009396020 @default.
- W2734398488 cites W2010954387 @default.
- W2734398488 cites W2022856784 @default.
- W2734398488 cites W2035168730 @default.
- W2734398488 cites W2043199679 @default.
- W2734398488 cites W2047200655 @default.
- W2734398488 cites W2047343695 @default.
- W2734398488 cites W2052590000 @default.
- W2734398488 cites W2054078790 @default.
- W2734398488 cites W2065600241 @default.
- W2734398488 cites W2076537938 @default.
- W2734398488 cites W2084506336 @default.
- W2734398488 cites W2086523882 @default.
- W2734398488 cites W2094966985 @default.
- W2734398488 cites W2149322030 @default.
- W2734398488 cites W2169615048 @default.
- W2734398488 cites W2196162646 @default.
- W2734398488 cites W2402253374 @default.
- W2734398488 cites W2519067532 @default.
- W2734398488 cites W2554205323 @default.
- W2734398488 cites W4211167975 @default.
- W2734398488 cites W600542335 @default.
- W2734398488 cites W616413802 @default.
- W2734398488 cites W765751610 @default.
- W2734398488 doi "https://doi.org/10.1016/j.matchar.2017.07.022" @default.
- W2734398488 hasPublicationYear "2017" @default.
- W2734398488 type Work @default.
- W2734398488 sameAs 2734398488 @default.
- W2734398488 citedByCount "42" @default.
- W2734398488 countsByYear W27343984882018 @default.
- W2734398488 countsByYear W27343984882019 @default.
- W2734398488 countsByYear W27343984882020 @default.
- W2734398488 countsByYear W27343984882021 @default.
- W2734398488 countsByYear W27343984882022 @default.
- W2734398488 countsByYear W27343984882023 @default.
- W2734398488 crossrefType "journal-article" @default.
- W2734398488 hasAuthorship W2734398488A5027080363 @default.
- W2734398488 hasAuthorship W2734398488A5051096110 @default.
- W2734398488 hasAuthorship W2734398488A5055739237 @default.
- W2734398488 hasAuthorship W2734398488A5065801579 @default.
- W2734398488 hasAuthorship W2734398488A5068209077 @default.
- W2734398488 hasAuthorship W2734398488A5076412762 @default.
- W2734398488 hasConcept C104779481 @default.
- W2734398488 hasConcept C140205800 @default.
- W2734398488 hasConcept C159985019 @default.
- W2734398488 hasConcept C191897082 @default.
- W2734398488 hasConcept C192562407 @default.
- W2734398488 hasConcept C207948433 @default.
- W2734398488 hasConceptScore W2734398488C104779481 @default.
- W2734398488 hasConceptScore W2734398488C140205800 @default.
- W2734398488 hasConceptScore W2734398488C159985019 @default.
- W2734398488 hasConceptScore W2734398488C191897082 @default.
- W2734398488 hasConceptScore W2734398488C192562407 @default.
- W2734398488 hasConceptScore W2734398488C207948433 @default.
- W2734398488 hasFunder F4320322108 @default.
- W2734398488 hasLocation W27343984881 @default.
- W2734398488 hasOpenAccess W2734398488 @default.
- W2734398488 hasPrimaryLocation W27343984881 @default.
- W2734398488 hasRelatedWork W1597859513 @default.
- W2734398488 hasRelatedWork W2042588148 @default.
- W2734398488 hasRelatedWork W2071847995 @default.
- W2734398488 hasRelatedWork W2170822008 @default.
- W2734398488 hasRelatedWork W2335087113 @default.
- W2734398488 hasRelatedWork W2335400378 @default.
- W2734398488 hasRelatedWork W2502187989 @default.
- W2734398488 hasRelatedWork W2612994787 @default.
- W2734398488 hasRelatedWork W4283766749 @default.
- W2734398488 hasRelatedWork W821857315 @default.
- W2734398488 hasVolume "131" @default.
- W2734398488 isParatext "false" @default.
- W2734398488 isRetracted "false" @default.
- W2734398488 magId "2734398488" @default.
- W2734398488 workType "article" @default.