- W2734547859 abstract "Microstructural evolution on sintering of porcelain powder compacts using microwave radiation was compared with that in conventionally sintered samples. Using microwaves sintering temperature was reduced by ~ 75 °C and dwell time from 15 min to 5 min while retaining comparable physical properties i.e. apparent bulk density, water absorption to conventionally sintered porcelain. Porcelain powder absorbed microwave energy above 600 °C due to a rapid increase in its loss tangent. Mullite and glass were used as indicators of the microwave effect: mullite produced using microwaves had a nanofibre morphology with high aspect ratio (~ 32 ± 3:1) believed associated with a vapour-liquid-solid (VLS) formation mechanism not previously reported. Microwaves also produced mullite with different chemistry having ~ 63 mol% alumina content compared to ~ 60 mol% alumina in conventional sintered porcelain. This was likely due to accelerated Al+3 diffusion in mullite under microwave radiation. Liquid glass was observed to form at relatively low temperature (~ 900–1000 °C) using microwaves when compared to conventional sintering which promoted the porcelains ability to absorb them." @default.
- W2734547859 created "2017-07-21" @default.
- W2734547859 creator A5001314918 @default.
- W2734547859 creator A5031827719 @default.
- W2734547859 creator A5048222625 @default.
- W2734547859 creator A5062834977 @default.
- W2734547859 creator A5071221436 @default.
- W2734547859 creator A5081985183 @default.
- W2734547859 date "2017-11-01" @default.
- W2734547859 modified "2023-10-14" @default.
- W2734547859 title "Impact of microwave processing on porcelain microstructure" @default.
- W2734547859 cites W1144866944 @default.
- W2734547859 cites W1963935071 @default.
- W2734547859 cites W1964053261 @default.
- W2734547859 cites W1968022548 @default.
- W2734547859 cites W1971512174 @default.
- W2734547859 cites W1982768412 @default.
- W2734547859 cites W1984496600 @default.
- W2734547859 cites W2010832607 @default.
- W2734547859 cites W2018644279 @default.
- W2734547859 cites W2024954986 @default.
- W2734547859 cites W2040175526 @default.
- W2734547859 cites W2047950042 @default.
- W2734547859 cites W2069382202 @default.
- W2734547859 cites W2091707193 @default.
- W2734547859 cites W2105710151 @default.
- W2734547859 cites W2132677591 @default.
- W2734547859 cites W2152702989 @default.
- W2734547859 cites W2162211801 @default.
- W2734547859 cites W2172088722 @default.
- W2734547859 cites W2175714443 @default.
- W2734547859 cites W2504068018 @default.
- W2734547859 cites W2514387782 @default.
- W2734547859 cites W2797657389 @default.
- W2734547859 doi "https://doi.org/10.1016/j.ceramint.2017.07.090" @default.
- W2734547859 hasPublicationYear "2017" @default.
- W2734547859 type Work @default.
- W2734547859 sameAs 2734547859 @default.
- W2734547859 citedByCount "16" @default.
- W2734547859 countsByYear W27345478592018 @default.
- W2734547859 countsByYear W27345478592019 @default.
- W2734547859 countsByYear W27345478592020 @default.
- W2734547859 countsByYear W27345478592021 @default.
- W2734547859 countsByYear W27345478592022 @default.
- W2734547859 crossrefType "journal-article" @default.
- W2734547859 hasAuthorship W2734547859A5001314918 @default.
- W2734547859 hasAuthorship W2734547859A5031827719 @default.
- W2734547859 hasAuthorship W2734547859A5048222625 @default.
- W2734547859 hasAuthorship W2734547859A5062834977 @default.
- W2734547859 hasAuthorship W2734547859A5071221436 @default.
- W2734547859 hasAuthorship W2734547859A5081985183 @default.
- W2734547859 hasBestOaLocation W27345478592 @default.
- W2734547859 hasConcept C110738630 @default.
- W2734547859 hasConcept C121332964 @default.
- W2734547859 hasConcept C134132462 @default.
- W2734547859 hasConcept C151637689 @default.
- W2734547859 hasConcept C159985019 @default.
- W2734547859 hasConcept C185592680 @default.
- W2734547859 hasConcept C192562407 @default.
- W2734547859 hasConcept C199289684 @default.
- W2734547859 hasConcept C2775943645 @default.
- W2734547859 hasConcept C2777581544 @default.
- W2734547859 hasConcept C2779227376 @default.
- W2734547859 hasConcept C2781436864 @default.
- W2734547859 hasConcept C44838205 @default.
- W2734547859 hasConcept C62520636 @default.
- W2734547859 hasConcept C70410870 @default.
- W2734547859 hasConcept C71924100 @default.
- W2734547859 hasConcept C87976508 @default.
- W2734547859 hasConceptScore W2734547859C110738630 @default.
- W2734547859 hasConceptScore W2734547859C121332964 @default.
- W2734547859 hasConceptScore W2734547859C134132462 @default.
- W2734547859 hasConceptScore W2734547859C151637689 @default.
- W2734547859 hasConceptScore W2734547859C159985019 @default.
- W2734547859 hasConceptScore W2734547859C185592680 @default.
- W2734547859 hasConceptScore W2734547859C192562407 @default.
- W2734547859 hasConceptScore W2734547859C199289684 @default.
- W2734547859 hasConceptScore W2734547859C2775943645 @default.
- W2734547859 hasConceptScore W2734547859C2777581544 @default.
- W2734547859 hasConceptScore W2734547859C2779227376 @default.
- W2734547859 hasConceptScore W2734547859C2781436864 @default.
- W2734547859 hasConceptScore W2734547859C44838205 @default.
- W2734547859 hasConceptScore W2734547859C62520636 @default.
- W2734547859 hasConceptScore W2734547859C70410870 @default.
- W2734547859 hasConceptScore W2734547859C71924100 @default.
- W2734547859 hasConceptScore W2734547859C87976508 @default.
- W2734547859 hasFunder F4320320283 @default.
- W2734547859 hasFunder F4320321837 @default.
- W2734547859 hasIssue "16" @default.
- W2734547859 hasLocation W27345478591 @default.
- W2734547859 hasLocation W27345478592 @default.
- W2734547859 hasLocation W27345478593 @default.
- W2734547859 hasOpenAccess W2734547859 @default.
- W2734547859 hasPrimaryLocation W27345478591 @default.
- W2734547859 hasRelatedWork W1590371294 @default.
- W2734547859 hasRelatedWork W2035049163 @default.
- W2734547859 hasRelatedWork W2051355164 @default.
- W2734547859 hasRelatedWork W2070399915 @default.