- W2746246051 abstract "We created and synthesized luminescent composite of the in type, based on the lead-silicate matrix and fine-dispersed powder of cerium-activated yttrium-aluminum garnet crystal. Lead-silicate system (40SiO220PbO-(40-x) PbF2-xAlF3, x = 0-25) was chosen as the glassy matrix. Initial glass was reduced to powder (frit) for in composite with a particle size about 50 μm. Glass frit and powder of commercial YAG:Ce phosphor were mixed in a ratio of 30 to 70 (wt %). Then this composite was pressed in a tablet and sintered on a quartz substrate at 823 К for 30 minutes. Thus, the plane parallel sheet for composite of the in was obtained with a diameter equal to 10 mm. For the purpose to reduce the loss of light in the presence of dispersion at a glass-phosphor boundary, optimization of glass mixture was done by adjusting the refractive index. X-ray phase and spectral-luminescent analysis of the derived composite were done. The results of these studies showed that there was no degradation of YAG: Ce powder during sintering. Dependence of luminescence intensity from temperature in the range from room temperature to 473 К was studied. It was shown, that with the phosphor in glass usage thermal quenching of luminescence was reduced in comparison with the silicone. The model of white LED was created with the in composite based on lead-silicate glasses with low temperature of vitrifying. The derived LED emits white light with a color temperature of 4370 K, and the luminous efficiency is equal to 58 lm/W. The developed luminescent composite based on the lead-silicate matrix can be used for the production of high-power white light LED." @default.
- W2746246051 created "2017-08-31" @default.
- W2746246051 creator A5005208465 @default.
- W2746246051 creator A5006662245 @default.
- W2746246051 creator A5027579862 @default.
- W2746246051 creator A5030249292 @default.
- W2746246051 creator A5032325944 @default.
- W2746246051 creator A5058994041 @default.
- W2746246051 creator A5085045894 @default.
- W2746246051 creator A5089300838 @default.
- W2746246051 date "2014-10-15" @default.
- W2746246051 modified "2023-09-27" @default.
- W2746246051 title "INORGANIC PHOSPHORS IN GLASS BASED ON LEAD SILICATE GLASSES" @default.
- W2746246051 cites W1564087868 @default.
- W2746246051 cites W1990995288 @default.
- W2746246051 cites W2016136311 @default.
- W2746246051 cites W2031620448 @default.
- W2746246051 cites W2044616284 @default.
- W2746246051 cites W2061898482 @default.
- W2746246051 cites W2095094482 @default.
- W2746246051 cites W2109476923 @default.
- W2746246051 cites W2141992519 @default.
- W2746246051 cites W2147489359 @default.
- W2746246051 cites W2153915332 @default.
- W2746246051 cites W2468357802 @default.
- W2746246051 cites W2157917720 @default.
- W2746246051 hasPublicationYear "2014" @default.
- W2746246051 type Work @default.
- W2746246051 sameAs 2746246051 @default.
- W2746246051 citedByCount "0" @default.
- W2746246051 crossrefType "journal-article" @default.
- W2746246051 hasAuthorship W2746246051A5005208465 @default.
- W2746246051 hasAuthorship W2746246051A5006662245 @default.
- W2746246051 hasAuthorship W2746246051A5027579862 @default.
- W2746246051 hasAuthorship W2746246051A5030249292 @default.
- W2746246051 hasAuthorship W2746246051A5032325944 @default.
- W2746246051 hasAuthorship W2746246051A5058994041 @default.
- W2746246051 hasAuthorship W2746246051A5085045894 @default.
- W2746246051 hasAuthorship W2746246051A5089300838 @default.
- W2746246051 hasConcept C104779481 @default.
- W2746246051 hasConcept C124385694 @default.
- W2746246051 hasConcept C148869448 @default.
- W2746246051 hasConcept C159985019 @default.
- W2746246051 hasConcept C185592680 @default.
- W2746246051 hasConcept C192562407 @default.
- W2746246051 hasConcept C199289684 @default.
- W2746246051 hasConcept C49040817 @default.
- W2746246051 hasConcept C68930688 @default.
- W2746246051 hasConceptScore W2746246051C104779481 @default.
- W2746246051 hasConceptScore W2746246051C124385694 @default.
- W2746246051 hasConceptScore W2746246051C148869448 @default.
- W2746246051 hasConceptScore W2746246051C159985019 @default.
- W2746246051 hasConceptScore W2746246051C185592680 @default.
- W2746246051 hasConceptScore W2746246051C192562407 @default.
- W2746246051 hasConceptScore W2746246051C199289684 @default.
- W2746246051 hasConceptScore W2746246051C49040817 @default.
- W2746246051 hasConceptScore W2746246051C68930688 @default.
- W2746246051 hasIssue "5" @default.
- W2746246051 hasLocation W27462460511 @default.
- W2746246051 hasOpenAccess W2746246051 @default.
- W2746246051 hasPrimaryLocation W27462460511 @default.
- W2746246051 hasRelatedWork W1572430238 @default.
- W2746246051 hasRelatedWork W16261261 @default.
- W2746246051 hasRelatedWork W1964533130 @default.
- W2746246051 hasRelatedWork W1966100140 @default.
- W2746246051 hasRelatedWork W2061613916 @default.
- W2746246051 hasRelatedWork W2601829836 @default.
- W2746246051 hasRelatedWork W2756434861 @default.
- W2746246051 hasRelatedWork W2886906040 @default.
- W2746246051 hasRelatedWork W3036749714 @default.
- W2746246051 hasRelatedWork W3139245807 @default.
- W2746246051 hasRelatedWork W2813041834 @default.
- W2746246051 hasRelatedWork W2825488324 @default.
- W2746246051 hasRelatedWork W2826504826 @default.
- W2746246051 hasRelatedWork W2846095137 @default.
- W2746246051 hasRelatedWork W2847326674 @default.
- W2746246051 hasRelatedWork W2861128542 @default.
- W2746246051 hasRelatedWork W2882931220 @default.
- W2746246051 hasRelatedWork W2925769189 @default.
- W2746246051 hasRelatedWork W2934831274 @default.
- W2746246051 hasRelatedWork W3123996353 @default.
- W2746246051 hasVolume "110" @default.
- W2746246051 isParatext "false" @default.
- W2746246051 isRetracted "false" @default.
- W2746246051 magId "2746246051" @default.
- W2746246051 workType "article" @default.