- W2752133095 abstract "Dental ceramics exhibit great optical properties and better esthetics due to their translucency. Concern with this material is its brittleness, which accounts for its failure. Feldspathic ceramic is the most widely used veneering ceramic.To evaluate and compare the fracture toughness of pressable feldspathic ceramics reinforced with zirconia silica nano-fibres with conventional pressable feldspathic ceramics.According to ISO 6872, a master die was prepared from which, Bar shaped samples were formed in acrylic resin with the specified dimensions of 4.0 mm in width ×1.2 mm thickness ×25.0 mm. The zirconia silica nano-fibres were prepared by sol gel electro-spinning followed by calcination then they were incorporated into feldspathic ceramic through ball milling process. The samples were prepared with addition of 0, 2.5, 5, 7.5 weight % nano-fibres. The fracture toughnes was evaluated using the indentation strength method. The values were statistically analysed using the one sample Kolmogorov-Smirnoff test, Kruskal Wallis test and pair wise group comparison was done using Mann Whitney test with Bonferroni correction.The fracture toughness values for 2.5 wt% and 5 wt% groups were higher than control group, while the values for 7.5 wt% groups were lower compared to control group.The fracture toughness values of feldspathic ceramic samples reinforced with zirconia silica nanofibers by 2.5 and 5 wt% were statistically significant when compared to samples reinforced with 7.5 wt%." @default.
- W2752133095 created "2017-09-15" @default.
- W2752133095 creator A5000891680 @default.
- W2752133095 creator A5070942430 @default.
- W2752133095 creator A5080728921 @default.
- W2752133095 date "2018-09-01" @default.
- W2752133095 modified "2023-09-29" @default.
- W2752133095 title "Evaluation of fracture toughness of zirconia silica nano-fibres reinforced feldespathic ceramic" @default.
- W2752133095 cites W1970805228 @default.
- W2752133095 cites W2020062268 @default.
- W2752133095 cites W2030026732 @default.
- W2752133095 cites W2055970561 @default.
- W2752133095 cites W2058181989 @default.
- W2752133095 cites W2061547164 @default.
- W2752133095 cites W2073987787 @default.
- W2752133095 cites W2078470663 @default.
- W2752133095 cites W2079041599 @default.
- W2752133095 cites W2083415035 @default.
- W2752133095 cites W2099412187 @default.
- W2752133095 cites W2113511817 @default.
- W2752133095 cites W2131964412 @default.
- W2752133095 cites W2141115733 @default.
- W2752133095 cites W2144434458 @default.
- W2752133095 cites W2158570505 @default.
- W2752133095 cites W2158833660 @default.
- W2752133095 cites W2170326240 @default.
- W2752133095 cites W2352829991 @default.
- W2752133095 doi "https://doi.org/10.1016/j.jobcr.2017.09.003" @default.
- W2752133095 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/6107928" @default.
- W2752133095 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/30191113" @default.
- W2752133095 hasPublicationYear "2018" @default.
- W2752133095 type Work @default.
- W2752133095 sameAs 2752133095 @default.
- W2752133095 citedByCount "4" @default.
- W2752133095 countsByYear W27521330952022 @default.
- W2752133095 crossrefType "journal-article" @default.
- W2752133095 hasAuthorship W2752133095A5000891680 @default.
- W2752133095 hasAuthorship W2752133095A5070942430 @default.
- W2752133095 hasAuthorship W2752133095A5080728921 @default.
- W2752133095 hasBestOaLocation W27521330952 @default.
- W2752133095 hasConcept C123609680 @default.
- W2752133095 hasConcept C134132462 @default.
- W2752133095 hasConcept C136478896 @default.
- W2752133095 hasConcept C159985019 @default.
- W2752133095 hasConcept C192562407 @default.
- W2752133095 hasConcept C97549433 @default.
- W2752133095 hasConceptScore W2752133095C123609680 @default.
- W2752133095 hasConceptScore W2752133095C134132462 @default.
- W2752133095 hasConceptScore W2752133095C136478896 @default.
- W2752133095 hasConceptScore W2752133095C159985019 @default.
- W2752133095 hasConceptScore W2752133095C192562407 @default.
- W2752133095 hasConceptScore W2752133095C97549433 @default.
- W2752133095 hasIssue "3" @default.
- W2752133095 hasLocation W27521330951 @default.
- W2752133095 hasLocation W27521330952 @default.
- W2752133095 hasLocation W27521330953 @default.
- W2752133095 hasLocation W27521330954 @default.
- W2752133095 hasOpenAccess W2752133095 @default.
- W2752133095 hasPrimaryLocation W27521330951 @default.
- W2752133095 hasRelatedWork W1982565681 @default.
- W2752133095 hasRelatedWork W2039999818 @default.
- W2752133095 hasRelatedWork W2075576573 @default.
- W2752133095 hasRelatedWork W2281145519 @default.
- W2752133095 hasRelatedWork W2286781514 @default.
- W2752133095 hasRelatedWork W2391612727 @default.
- W2752133095 hasRelatedWork W2891562802 @default.
- W2752133095 hasRelatedWork W3001224890 @default.
- W2752133095 hasRelatedWork W4239534552 @default.
- W2752133095 hasRelatedWork W4252921449 @default.
- W2752133095 hasVolume "8" @default.
- W2752133095 isParatext "false" @default.
- W2752133095 isRetracted "false" @default.
- W2752133095 magId "2752133095" @default.
- W2752133095 workType "article" @default.