- W2753204467 abstract "A functionally graded Cu–10Sn–5Ni metal matrix composite (MMC) reinforced with 10 wt % of Al2O3 particles was fabricated using the centrifugal casting process with dimension Φout100 × Φin85 × 100 mm. The mechanical and wear resistance of the composite has been enhanced through heat treatment. Samples from of the inner zone (9–15 mm) were considered for heat treatment, as this zone has higher concentration of less dense hard reinforcement particles. The samples were solutionized (620 °C/60 min) and water quenched followed by aging at different temperatures (400, 450, and 550 °C) and time (1–3 h). Optimum parametric combination (450 °C, 3 h) with maximum hardness (269 HV) was considered for further analysis. Dry sliding wear experiments were conducted based on Taguchi's L27 array using parameters such as applied loads (10, 20, and 30 N), sliding distances (500, 1000, and 1500 m), and sliding velocities (1, 2, and 3 m/s). Results revealed that the wear rate increased with load and distance whereas it decreased initially and then increased with velocity. Optimum condition for maximum wear resistance was determined using signal-to-noise (S/N) ratio. Analysis of variance (ANOVA) predicted the major influential parameter as load, followed by velocity and distance. Scanning electron microscope (SEM) analysis of worn surfaces predicted the wear mechanism, observing more delamination due to increase in contact patch when applied load increased. Results infer 8% increase in hardness after heat treatment, making it suitable for load bearing applications." @default.
- W2753204467 created "2017-09-15" @default.
- W2753204467 creator A5038697826 @default.
- W2753204467 creator A5082283877 @default.
- W2753204467 date "2017-10-06" @default.
- W2753204467 modified "2023-10-03" @default.
- W2753204467 title "Effect of Heat Treatment on Mechanical and Tribological Properties of Centrifugally Cast Functionally Graded Cu/Al2O3 Composite" @default.
- W2753204467 cites W1968213851 @default.
- W2753204467 cites W1976007606 @default.
- W2753204467 cites W1979130338 @default.
- W2753204467 cites W1987715815 @default.
- W2753204467 cites W1988875013 @default.
- W2753204467 cites W1996620157 @default.
- W2753204467 cites W2005085205 @default.
- W2753204467 cites W2023486527 @default.
- W2753204467 cites W2045234323 @default.
- W2753204467 cites W2058234339 @default.
- W2753204467 cites W2080895021 @default.
- W2753204467 cites W2082951640 @default.
- W2753204467 cites W2096032151 @default.
- W2753204467 cites W266440703 @default.
- W2753204467 doi "https://doi.org/10.1115/1.4037767" @default.
- W2753204467 hasPublicationYear "2017" @default.
- W2753204467 type Work @default.
- W2753204467 sameAs 2753204467 @default.
- W2753204467 citedByCount "20" @default.
- W2753204467 countsByYear W27532044672018 @default.
- W2753204467 countsByYear W27532044672019 @default.
- W2753204467 countsByYear W27532044672020 @default.
- W2753204467 countsByYear W27532044672021 @default.
- W2753204467 countsByYear W27532044672022 @default.
- W2753204467 countsByYear W27532044672023 @default.
- W2753204467 crossrefType "journal-article" @default.
- W2753204467 hasAuthorship W2753204467A5038697826 @default.
- W2753204467 hasAuthorship W2753204467A5082283877 @default.
- W2753204467 hasConcept C104779481 @default.
- W2753204467 hasConcept C151730666 @default.
- W2753204467 hasConcept C159985019 @default.
- W2753204467 hasConcept C167310744 @default.
- W2753204467 hasConcept C192562407 @default.
- W2753204467 hasConcept C26771246 @default.
- W2753204467 hasConcept C2777925586 @default.
- W2753204467 hasConcept C2779153048 @default.
- W2753204467 hasConcept C2780566776 @default.
- W2753204467 hasConcept C30239060 @default.
- W2753204467 hasConcept C42632107 @default.
- W2753204467 hasConcept C58097730 @default.
- W2753204467 hasConcept C77928131 @default.
- W2753204467 hasConcept C83469408 @default.
- W2753204467 hasConcept C86803240 @default.
- W2753204467 hasConceptScore W2753204467C104779481 @default.
- W2753204467 hasConceptScore W2753204467C151730666 @default.
- W2753204467 hasConceptScore W2753204467C159985019 @default.
- W2753204467 hasConceptScore W2753204467C167310744 @default.
- W2753204467 hasConceptScore W2753204467C192562407 @default.
- W2753204467 hasConceptScore W2753204467C26771246 @default.
- W2753204467 hasConceptScore W2753204467C2777925586 @default.
- W2753204467 hasConceptScore W2753204467C2779153048 @default.
- W2753204467 hasConceptScore W2753204467C2780566776 @default.
- W2753204467 hasConceptScore W2753204467C30239060 @default.
- W2753204467 hasConceptScore W2753204467C42632107 @default.
- W2753204467 hasConceptScore W2753204467C58097730 @default.
- W2753204467 hasConceptScore W2753204467C77928131 @default.
- W2753204467 hasConceptScore W2753204467C83469408 @default.
- W2753204467 hasConceptScore W2753204467C86803240 @default.
- W2753204467 hasIssue "2" @default.
- W2753204467 hasLocation W27532044671 @default.
- W2753204467 hasOpenAccess W2753204467 @default.
- W2753204467 hasPrimaryLocation W27532044671 @default.
- W2753204467 hasRelatedWork W2038461032 @default.
- W2753204467 hasRelatedWork W2054113325 @default.
- W2753204467 hasRelatedWork W2152205008 @default.
- W2753204467 hasRelatedWork W2806112502 @default.
- W2753204467 hasRelatedWork W2883783394 @default.
- W2753204467 hasRelatedWork W3105583209 @default.
- W2753204467 hasRelatedWork W3119505933 @default.
- W2753204467 hasRelatedWork W3163359645 @default.
- W2753204467 hasRelatedWork W3168151352 @default.
- W2753204467 hasRelatedWork W4225136231 @default.
- W2753204467 hasVolume "140" @default.
- W2753204467 isParatext "false" @default.
- W2753204467 isRetracted "false" @default.
- W2753204467 magId "2753204467" @default.
- W2753204467 workType "article" @default.