- W2753241409 abstract "Acrylic resin with a fast curable property has been used in low temperature ACFs applications. However, its poor thermo-mechanical property was a concern for solder ACFs applications. In this study, a novel thermomechanical analysis (TMA) method was introduced to measure its polymer rebound amounts due to pressures removal after a thermo-compression (TC) bonding process. Polymer resin was laminated between two silicon chips (7 ∗ 7 mm2), and then a compressive mode TMA measurement was done on the prepared samples. Constant compressive pressures were applied until the temperature was gradually increased to target temperature, and the forces were removed at the target temperatures. The polymer rebound was measured by monitoring the z-axis dimension change after the compressive forces was removed. In addition, the effects of bonding temperatures (from 150 to 250 °C) and the bonding pressures (1, 2 and 3 MPa) on the SnBi58 (139 °C melting point) solder joints morphologies and joint resistances were evaluated to investigate acrylic resin property and find out the optimized bonding conditions for low Tg acrylic-based solder ACFs applications." @default.
- W2753241409 created "2017-09-15" @default.
- W2753241409 creator A5026879812 @default.
- W2753241409 creator A5067223853 @default.
- W2753241409 creator A5070848500 @default.
- W2753241409 creator A5085811214 @default.
- W2753241409 date "2017-11-01" @default.
- W2753241409 modified "2023-10-14" @default.
- W2753241409 title "Effects of acrylic adhesives property and optimized bonding parameters on Sn 58Bi solder joint morphology for flex-on-board assembly" @default.
- W2753241409 cites W2010883406 @default.
- W2753241409 cites W2041749478 @default.
- W2753241409 cites W2059523013 @default.
- W2753241409 cites W2063410602 @default.
- W2753241409 cites W2068115462 @default.
- W2753241409 cites W2083107725 @default.
- W2753241409 cites W2084455449 @default.
- W2753241409 cites W2180519826 @default.
- W2753241409 cites W2324913251 @default.
- W2753241409 cites W2515173589 @default.
- W2753241409 doi "https://doi.org/10.1016/j.microrel.2017.08.009" @default.
- W2753241409 hasPublicationYear "2017" @default.
- W2753241409 type Work @default.
- W2753241409 sameAs 2753241409 @default.
- W2753241409 citedByCount "21" @default.
- W2753241409 countsByYear W27532414092017 @default.
- W2753241409 countsByYear W27532414092018 @default.
- W2753241409 countsByYear W27532414092019 @default.
- W2753241409 countsByYear W27532414092020 @default.
- W2753241409 countsByYear W27532414092022 @default.
- W2753241409 countsByYear W27532414092023 @default.
- W2753241409 crossrefType "journal-article" @default.
- W2753241409 hasAuthorship W2753241409A5026879812 @default.
- W2753241409 hasAuthorship W2753241409A5067223853 @default.
- W2753241409 hasAuthorship W2753241409A5070848500 @default.
- W2753241409 hasAuthorship W2753241409A5085811214 @default.
- W2753241409 hasConcept C112950240 @default.
- W2753241409 hasConcept C127413603 @default.
- W2753241409 hasConcept C13530604 @default.
- W2753241409 hasConcept C140013486 @default.
- W2753241409 hasConcept C159985019 @default.
- W2753241409 hasConcept C180478085 @default.
- W2753241409 hasConcept C18555067 @default.
- W2753241409 hasConcept C192562407 @default.
- W2753241409 hasConcept C2779227376 @default.
- W2753241409 hasConcept C2781448156 @default.
- W2753241409 hasConcept C50296614 @default.
- W2753241409 hasConcept C521977710 @default.
- W2753241409 hasConcept C66938386 @default.
- W2753241409 hasConcept C68928338 @default.
- W2753241409 hasConceptScore W2753241409C112950240 @default.
- W2753241409 hasConceptScore W2753241409C127413603 @default.
- W2753241409 hasConceptScore W2753241409C13530604 @default.
- W2753241409 hasConceptScore W2753241409C140013486 @default.
- W2753241409 hasConceptScore W2753241409C159985019 @default.
- W2753241409 hasConceptScore W2753241409C180478085 @default.
- W2753241409 hasConceptScore W2753241409C18555067 @default.
- W2753241409 hasConceptScore W2753241409C192562407 @default.
- W2753241409 hasConceptScore W2753241409C2779227376 @default.
- W2753241409 hasConceptScore W2753241409C2781448156 @default.
- W2753241409 hasConceptScore W2753241409C50296614 @default.
- W2753241409 hasConceptScore W2753241409C521977710 @default.
- W2753241409 hasConceptScore W2753241409C66938386 @default.
- W2753241409 hasConceptScore W2753241409C68928338 @default.
- W2753241409 hasFunder F4320321001 @default.
- W2753241409 hasFunder F4320322120 @default.
- W2753241409 hasLocation W27532414091 @default.
- W2753241409 hasOpenAccess W2753241409 @default.
- W2753241409 hasPrimaryLocation W27532414091 @default.
- W2753241409 hasRelatedWork W1963684115 @default.
- W2753241409 hasRelatedWork W2028434337 @default.
- W2753241409 hasRelatedWork W2041821732 @default.
- W2753241409 hasRelatedWork W2062276134 @default.
- W2753241409 hasRelatedWork W2076361664 @default.
- W2753241409 hasRelatedWork W2141697063 @default.
- W2753241409 hasRelatedWork W2366970374 @default.
- W2753241409 hasRelatedWork W2514058477 @default.
- W2753241409 hasRelatedWork W4368370722 @default.
- W2753241409 hasRelatedWork W763220558 @default.
- W2753241409 hasVolume "78" @default.
- W2753241409 isParatext "false" @default.
- W2753241409 isRetracted "false" @default.
- W2753241409 magId "2753241409" @default.
- W2753241409 workType "article" @default.