- W2758902880 abstract "Annealing behavior of AlCoCrFeNiTi0.5 high entropy alloy coatings prepared by laser cladding was investigated. The specimens were annealed at 900 °C for 5 h. The microstructure and wear resistance of the as-annealed and as-cast specimens were investigated. The XRD results indicate that the as-annealed AlCoCrFeNiTi0.5 high entropy alloy coating is composed of Al80Cr13Co7, Co3Ti, and AlFe solid solution phase. The SEM results and EDS data show that a typical spinodal decomposition structure with uniform composition is formed after annealing treatment. The average Vickers micro-hardness of the as-annealed coatings could reach 9890 MPa which is increased by about 73.5% compared with that of the as-cast coatings. The abrasion resistance testing shows that the abrasion loss of the as-annealed coatings is reduced by 92.5% and the wear width is reduced by 50% compared with the values of as-cast coatings." @default.
- W2758902880 created "2017-10-06" @default.
- W2758902880 creator A5002446862 @default.
- W2758902880 creator A5003100427 @default.
- W2758902880 creator A5063496433 @default.
- W2758902880 creator A5068930979 @default.
- W2758902880 creator A5086226329 @default.
- W2758902880 creator A5090100367 @default.
- W2758902880 date "2017-05-01" @default.
- W2758902880 modified "2023-09-24" @default.
- W2758902880 title "Effects of Annealing on the Microstructure and Wear Resistance of AlCoCrFeNiTi 0.5 High-entropy Alloy Coating Prepared by Laser Cladding" @default.
- W2758902880 cites W1594823077 @default.
- W2758902880 cites W1976120875 @default.
- W2758902880 cites W1979161432 @default.
- W2758902880 cites W2002960475 @default.
- W2758902880 cites W2013141943 @default.
- W2758902880 cites W2058085399 @default.
- W2758902880 cites W2067543317 @default.
- W2758902880 cites W2071212235 @default.
- W2758902880 cites W2091037363 @default.
- W2758902880 cites W2103109670 @default.
- W2758902880 cites W2442131019 @default.
- W2758902880 cites W63376992 @default.
- W2758902880 doi "https://doi.org/10.1016/s1875-5372(17)30143-1" @default.
- W2758902880 hasPublicationYear "2017" @default.
- W2758902880 type Work @default.
- W2758902880 sameAs 2758902880 @default.
- W2758902880 citedByCount "24" @default.
- W2758902880 countsByYear W27589028802018 @default.
- W2758902880 countsByYear W27589028802019 @default.
- W2758902880 countsByYear W27589028802020 @default.
- W2758902880 countsByYear W27589028802021 @default.
- W2758902880 countsByYear W27589028802022 @default.
- W2758902880 countsByYear W27589028802023 @default.
- W2758902880 crossrefType "journal-article" @default.
- W2758902880 hasAuthorship W2758902880A5002446862 @default.
- W2758902880 hasAuthorship W2758902880A5003100427 @default.
- W2758902880 hasAuthorship W2758902880A5063496433 @default.
- W2758902880 hasAuthorship W2758902880A5068930979 @default.
- W2758902880 hasAuthorship W2758902880A5086226329 @default.
- W2758902880 hasAuthorship W2758902880A5090100367 @default.
- W2758902880 hasBestOaLocation W27589028802 @default.
- W2758902880 hasConcept C133392424 @default.
- W2758902880 hasConcept C159985019 @default.
- W2758902880 hasConcept C178790620 @default.
- W2758902880 hasConcept C185592680 @default.
- W2758902880 hasConcept C191897082 @default.
- W2758902880 hasConcept C192562407 @default.
- W2758902880 hasConcept C2777855556 @default.
- W2758902880 hasConcept C2780026712 @default.
- W2758902880 hasConcept C2780299837 @default.
- W2758902880 hasConcept C2781448156 @default.
- W2758902880 hasConcept C29234059 @default.
- W2758902880 hasConcept C2983445633 @default.
- W2758902880 hasConcept C44280652 @default.
- W2758902880 hasConcept C87976508 @default.
- W2758902880 hasConceptScore W2758902880C133392424 @default.
- W2758902880 hasConceptScore W2758902880C159985019 @default.
- W2758902880 hasConceptScore W2758902880C178790620 @default.
- W2758902880 hasConceptScore W2758902880C185592680 @default.
- W2758902880 hasConceptScore W2758902880C191897082 @default.
- W2758902880 hasConceptScore W2758902880C192562407 @default.
- W2758902880 hasConceptScore W2758902880C2777855556 @default.
- W2758902880 hasConceptScore W2758902880C2780026712 @default.
- W2758902880 hasConceptScore W2758902880C2780299837 @default.
- W2758902880 hasConceptScore W2758902880C2781448156 @default.
- W2758902880 hasConceptScore W2758902880C29234059 @default.
- W2758902880 hasConceptScore W2758902880C2983445633 @default.
- W2758902880 hasConceptScore W2758902880C44280652 @default.
- W2758902880 hasConceptScore W2758902880C87976508 @default.
- W2758902880 hasIssue "5" @default.
- W2758902880 hasLocation W27589028801 @default.
- W2758902880 hasLocation W27589028802 @default.
- W2758902880 hasOpenAccess W2758902880 @default.
- W2758902880 hasPrimaryLocation W27589028801 @default.
- W2758902880 hasRelatedWork W1765587454 @default.
- W2758902880 hasRelatedWork W1959169792 @default.
- W2758902880 hasRelatedWork W1974163541 @default.
- W2758902880 hasRelatedWork W2020660716 @default.
- W2758902880 hasRelatedWork W2358135274 @default.
- W2758902880 hasRelatedWork W2379355790 @default.
- W2758902880 hasRelatedWork W2755090871 @default.
- W2758902880 hasRelatedWork W2797168729 @default.
- W2758902880 hasRelatedWork W2947176019 @default.
- W2758902880 hasRelatedWork W4295763135 @default.
- W2758902880 hasVolume "46" @default.
- W2758902880 isParatext "false" @default.
- W2758902880 isRetracted "false" @default.
- W2758902880 magId "2758902880" @default.
- W2758902880 workType "article" @default.