- W2766703405 abstract "The change of microstructure during reverse transformation by continuous heating and isothermal holding above Af temperature were studied in Fe-11, 18 and 23 Ni (mass %) alloys. In-situ observation by using confocal laser scanning microscopy (CLSM) and in-situ/ex-situ electron backscatter diffraction (EBSD) analysis were used for direct observation of reverse transformation. It was found that the start temperatures (As) for austenite reversion decrease with increasing of Ni content while they are higher than T0 temperatures. Reverse transformation in the Fe-23 Ni alloy is accompanied with a sharp surface relief indicating that reverse transformation occurs martensitically in this alloy. EBSD measurements show that reversed austenite grains in this alloy are formed with nearly identical crystallographic orientations to the prior one, which means orientations and boundaries of prior austenite grains are preserved due to the austenite memory effect. By further holding above Af temperature spontaneous recrystallization of reverted austenite proceeds. The Fe-18 Ni alloy also shows similar microstructure change during reversion. Near Kurdjamov-Sachs (K-S) orientation relationship is found between reversed austenite and initial martensite during reversion of the Fe-18 and 23 Ni alloys. However, when the Ni content is decreased to 11%, no specific orientation relationship is found between reversed austenite and initial martensite, indicating that the reversion mechanism is changed from martensitic to partitionless diffusional (massive) mechanism." @default.
- W2766703405 created "2017-11-10" @default.
- W2766703405 creator A5010482135 @default.
- W2766703405 creator A5018933317 @default.
- W2766703405 creator A5034851707 @default.
- W2766703405 creator A5035439854 @default.
- W2766703405 creator A5074598380 @default.
- W2766703405 creator A5079438399 @default.
- W2766703405 date "2018-02-01" @default.
- W2766703405 modified "2023-10-18" @default.
- W2766703405 title "Microstructure evolution during austenite reversion in Fe-Ni martensitic alloys" @default.
- W2766703405 cites W1619564613 @default.
- W2766703405 cites W1689253152 @default.
- W2766703405 cites W1968392911 @default.
- W2766703405 cites W1970705976 @default.
- W2766703405 cites W1973785660 @default.
- W2766703405 cites W1976389711 @default.
- W2766703405 cites W1978392161 @default.
- W2766703405 cites W1980466511 @default.
- W2766703405 cites W1985322493 @default.
- W2766703405 cites W1995042188 @default.
- W2766703405 cites W1995983047 @default.
- W2766703405 cites W1996255013 @default.
- W2766703405 cites W1996549880 @default.
- W2766703405 cites W2001026297 @default.
- W2766703405 cites W2006876145 @default.
- W2766703405 cites W2009330879 @default.
- W2766703405 cites W2009637260 @default.
- W2766703405 cites W2012380779 @default.
- W2766703405 cites W2012779056 @default.
- W2766703405 cites W2027198066 @default.
- W2766703405 cites W2049572086 @default.
- W2766703405 cites W2050763058 @default.
- W2766703405 cites W2051201213 @default.
- W2766703405 cites W2058205990 @default.
- W2766703405 cites W2070809637 @default.
- W2766703405 cites W2072254982 @default.
- W2766703405 cites W2074726951 @default.
- W2766703405 cites W2075408663 @default.
- W2766703405 cites W2076677832 @default.
- W2766703405 cites W2078871424 @default.
- W2766703405 cites W2090962626 @default.
- W2766703405 cites W2092423634 @default.
- W2766703405 cites W2094675695 @default.
- W2766703405 cites W2102813696 @default.
- W2766703405 cites W2107575205 @default.
- W2766703405 cites W2114938642 @default.
- W2766703405 cites W2135811774 @default.
- W2766703405 cites W2145339655 @default.
- W2766703405 cites W2607466504 @default.
- W2766703405 cites W2993914751 @default.
- W2766703405 cites W2997349779 @default.
- W2766703405 doi "https://doi.org/10.1016/j.actamat.2017.10.068" @default.
- W2766703405 hasPublicationYear "2018" @default.
- W2766703405 type Work @default.
- W2766703405 sameAs 2766703405 @default.
- W2766703405 citedByCount "56" @default.
- W2766703405 countsByYear W27667034052018 @default.
- W2766703405 countsByYear W27667034052019 @default.
- W2766703405 countsByYear W27667034052020 @default.
- W2766703405 countsByYear W27667034052021 @default.
- W2766703405 countsByYear W27667034052022 @default.
- W2766703405 countsByYear W27667034052023 @default.
- W2766703405 crossrefType "journal-article" @default.
- W2766703405 hasAuthorship W2766703405A5010482135 @default.
- W2766703405 hasAuthorship W2766703405A5018933317 @default.
- W2766703405 hasAuthorship W2766703405A5034851707 @default.
- W2766703405 hasAuthorship W2766703405A5035439854 @default.
- W2766703405 hasAuthorship W2766703405A5074598380 @default.
- W2766703405 hasAuthorship W2766703405A5079438399 @default.
- W2766703405 hasConcept C104317684 @default.
- W2766703405 hasConcept C127716648 @default.
- W2766703405 hasConcept C151730666 @default.
- W2766703405 hasConcept C185592680 @default.
- W2766703405 hasConcept C18747287 @default.
- W2766703405 hasConcept C191897082 @default.
- W2766703405 hasConcept C192562407 @default.
- W2766703405 hasConcept C195702682 @default.
- W2766703405 hasConcept C2780026712 @default.
- W2766703405 hasConcept C27805521 @default.
- W2766703405 hasConcept C55493867 @default.
- W2766703405 hasConcept C70883133 @default.
- W2766703405 hasConcept C73170135 @default.
- W2766703405 hasConcept C86803240 @default.
- W2766703405 hasConcept C87976508 @default.
- W2766703405 hasConcept C96288455 @default.
- W2766703405 hasConceptScore W2766703405C104317684 @default.
- W2766703405 hasConceptScore W2766703405C127716648 @default.
- W2766703405 hasConceptScore W2766703405C151730666 @default.
- W2766703405 hasConceptScore W2766703405C185592680 @default.
- W2766703405 hasConceptScore W2766703405C18747287 @default.
- W2766703405 hasConceptScore W2766703405C191897082 @default.
- W2766703405 hasConceptScore W2766703405C192562407 @default.
- W2766703405 hasConceptScore W2766703405C195702682 @default.
- W2766703405 hasConceptScore W2766703405C2780026712 @default.
- W2766703405 hasConceptScore W2766703405C27805521 @default.
- W2766703405 hasConceptScore W2766703405C55493867 @default.
- W2766703405 hasConceptScore W2766703405C70883133 @default.