• W2769915618 abstract "As a transient and localized heating joining process, the self-propagating reaction joining (SPRJ) method can confine the heat at the joint itself formed by adjacent materials. By proper joint design and heat control from SPRJ, this advantage can be utilized to develop a kind of low-temperature joining approach, which is greatly required by thermal-sensitive device packaging. In this paper, the SPRJ process based on the Al/Ni multilayer film was investigated to join copper substrates electroplated with thin tin solder layers of different thicknesses under the pressure of 5 MPa at room temperature. It showed that the thickness of tin solder layer was a very critical parameter for forming high-quality joints. It was found that the thickness of Cu6Sn5 intermetallic compound (IMC) layer at Cu/Sn interface increased greatly along with tin solder layer thickening from 1 to 4 μm, and then tended to be stabilized with the further increase of tin layer thickness. Meanwhile, the change of the shear strength of the CuCu joints showed the same trend with the variation of Cu6Sn5 layer thickness. The defects were easily formed when the tin layer was too thin, while too thick tin layer may not be further beneficial for the reduce of defects and the formation of IMC due to the limited heat release of the Al/Ni multilayer film and the rapid cool process." @default.
• W2769915618 created "2017-12-04" @default.
• W2769915618 creator A5011472059 @default.
• W2769915618 creator A5012670199 @default.
• W2769915618 creator A5013330870 @default.
• W2769915618 creator A5015676739 @default.
• W2769915618 creator A5032400858 @default.
• W2769915618 creator A5036405372 @default.
• W2769915618 creator A5055435127 @default.
• W2769915618 creator A5059799647 @default.
• W2769915618 date "2018-02-01" @default.
• W2769915618 modified "2023-10-14" @default.
• W2769915618 title "The Cu Cu self-propagating reaction joining with different thickness of tin" @default.
• W2769915618 cites W1980693559 @default.
• W2769915618 cites W1988631867 @default.
• W2769915618 cites W1989005340 @default.
• W2769915618 cites W2000833862 @default.
• W2769915618 cites W2001649361 @default.
• W2769915618 cites W2007380163 @default.
• W2769915618 cites W2011657230 @default.
• W2769915618 cites W2020277404 @default.
• W2769915618 cites W2023070535 @default.
• W2769915618 cites W2035578823 @default.
• W2769915618 cites W2041969392 @default.
• W2769915618 cites W2048128314 @default.
• W2769915618 cites W2066467648 @default.
• W2769915618 cites W2068762353 @default.
• W2769915618 cites W2083260984 @default.
• W2769915618 cites W2095150730 @default.
• W2769915618 cites W2117019713 @default.
• W2769915618 cites W2138950636 @default.
• W2769915618 cites W2314409771 @default.
• W2769915618 cites W2315045050 @default.
• W2769915618 cites W2342864267 @default.
• W2769915618 cites W2514960441 @default.
• W2769915618 cites W2515752671 @default.
• W2769915618 cites W2551988149 @default.
• W2769915618 cites W831259431 @default.
• W2769915618 doi "https://doi.org/10.1016/j.jallcom.2017.11.265" @default.
• W2769915618 hasPublicationYear "2018" @default.
• W2769915618 type Work @default.
• W2769915618 sameAs 2769915618 @default.
• W2769915618 citedByCount "8" @default.
• W2769915618 countsByYear W27699156182018 @default.
• W2769915618 countsByYear W27699156182020 @default.
• W2769915618 countsByYear W27699156182021 @default.
• W2769915618 countsByYear W27699156182022 @default.
• W2769915618 crossrefType "journal-article" @default.
• W2769915618 hasAuthorship W2769915618A5011472059 @default.
• W2769915618 hasAuthorship W2769915618A5012670199 @default.
• W2769915618 hasAuthorship W2769915618A5013330870 @default.
• W2769915618 hasAuthorship W2769915618A5015676739 @default.
• W2769915618 hasAuthorship W2769915618A5032400858 @default.
• W2769915618 hasAuthorship W2769915618A5036405372 @default.
• W2769915618 hasAuthorship W2769915618A5055435127 @default.
• W2769915618 hasAuthorship W2769915618A5059799647 @default.
• W2769915618 hasConcept C127413603 @default.
• W2769915618 hasConcept C127893833 @default.
• W2769915618 hasConcept C159390177 @default.
• W2769915618 hasConcept C159750122 @default.
• W2769915618 hasConcept C159985019 @default.
• W2769915618 hasConcept C18555067 @default.
• W2769915618 hasConcept C191897082 @default.
• W2769915618 hasConcept C192562407 @default.
• W2769915618 hasConcept C27501479 @default.
• W2769915618 hasConcept C2779227376 @default.
• W2769915618 hasConcept C2780026712 @default.
• W2769915618 hasConcept C39432304 @default.
• W2769915618 hasConcept C50296614 @default.
• W2769915618 hasConcept C51807945 @default.
• W2769915618 hasConcept C525849907 @default.
• W2769915618 hasConcept C544778455 @default.
• W2769915618 hasConcept C66938386 @default.
• W2769915618 hasConceptScore W2769915618C127413603 @default.
• W2769915618 hasConceptScore W2769915618C127893833 @default.
• W2769915618 hasConceptScore W2769915618C159390177 @default.
• W2769915618 hasConceptScore W2769915618C159750122 @default.
• W2769915618 hasConceptScore W2769915618C159985019 @default.
• W2769915618 hasConceptScore W2769915618C18555067 @default.
• W2769915618 hasConceptScore W2769915618C191897082 @default.
• W2769915618 hasConceptScore W2769915618C192562407 @default.
• W2769915618 hasConceptScore W2769915618C27501479 @default.
• W2769915618 hasConceptScore W2769915618C2779227376 @default.
• W2769915618 hasConceptScore W2769915618C2780026712 @default.
• W2769915618 hasConceptScore W2769915618C39432304 @default.
• W2769915618 hasConceptScore W2769915618C50296614 @default.
• W2769915618 hasConceptScore W2769915618C51807945 @default.
• W2769915618 hasConceptScore W2769915618C525849907 @default.
• W2769915618 hasConceptScore W2769915618C544778455 @default.
• W2769915618 hasConceptScore W2769915618C66938386 @default.
• W2769915618 hasLocation W27699156181 @default.
• W2769915618 hasOpenAccess W2769915618 @default.
• W2769915618 hasPrimaryLocation W27699156181 @default.
• W2769915618 hasRelatedWork W2141697063 @default.
• W2769915618 hasRelatedWork W2360807830 @default.
• W2769915618 hasRelatedWork W2366354700 @default.
• W2769915618 hasRelatedWork W2369201096 @default.
• W2769915618 hasRelatedWork W2541086319 @default.

• next