• W2783412150 abstract "Abstract An Fe-10Cr-2.7B-5.5Al-13Mn alloy has been fabricated by the combination of mechanical alloying (MA) and spark plasma sintering (SPS). Microstructure and phase evolution of the alloy powder and sintered specimen were investigated by using scanning electron microscopy (SEM), X-ray diffractometer (XRD) and transmission electron microscopy (TEM). The resultant mechanical properties were determined in Rockwell hardness and compressive strength. The corrosion behavior was tested by investigated test in 750 °C molten pure aluminum for 1 h and 4 h. Results have shown that the sintered specimen is mainly composed of Fe2AlCr intermetallic, CrFeB-type boride and Mn2B-type boride uniformly distributed in the γ matrix. The sintered specimen achieves Rockwell Hardness and compressive strength of 59.7 ± 0.2 HRC and 2823 ± 21.0 MPa at room temperature, respectively. Especially, compressive strength of the sintered specimen at 600 °C reaches 902 ± 15.5 MPa. The high hardness and compressive strength can be attributed to solid solution of Al, Cr and Mn, precipitation of CrFeB, Mn2B and Fe2AlCr in the γ-Fe matrix and nanocrystalline microstructure produced by the combine of MA and SPS. The corrosion rate of the sintered Fe-10Cr-2.7B-5.5Al-13Mn in molten aluminum is ～ 36% of that of H13. CrFeB, Mn2B and Fe2AlCr play a key role in improving the corrosion resistance of the sintered specimen in molten aluminum. They are embedded in the corrosion products (intermetallics) and act as roots to capture the intermetallics from falling off." @default.
• W2783412150 created "2018-01-26" @default.
• W2783412150 creator A5026047135 @default.
• W2783412150 creator A5066659835 @default.
• W2783412150 date "2018-04-01" @default.
• W2783412150 modified "2023-10-14" @default.
• W2783412150 title "Microstructure, mechanical properties and corrosion behavior of an Fe-10Cr-2.7B-5.5Al-13Mn alloy prepared by spark plasma sintering" @default.
• W2783412150 cites W1747352374 @default.
• W2783412150 cites W1970381289 @default.
• W2783412150 cites W1972941709 @default.
• W2783412150 cites W1982821150 @default.
• W2783412150 cites W1987285649 @default.
• W2783412150 cites W1993656487 @default.
• W2783412150 cites W1995699220 @default.
• W2783412150 cites W2000462717 @default.
• W2783412150 cites W2009373498 @default.
• W2783412150 cites W2009895859 @default.
• W2783412150 cites W2010519493 @default.
• W2783412150 cites W2017414000 @default.
• W2783412150 cites W2020735276 @default.
• W2783412150 cites W2026815165 @default.
• W2783412150 cites W2027835321 @default.
• W2783412150 cites W2028820908 @default.
• W2783412150 cites W2032329598 @default.
• W2783412150 cites W2038115883 @default.
• W2783412150 cites W2042083384 @default.
• W2783412150 cites W2043293833 @default.
• W2783412150 cites W2046745132 @default.
• W2783412150 cites W2047923100 @default.
• W2783412150 cites W2051082125 @default.
• W2783412150 cites W2051124913 @default.
• W2783412150 cites W2051391436 @default.
• W2783412150 cites W2054193266 @default.
• W2783412150 cites W2061225545 @default.
• W2783412150 cites W2063120921 @default.
• W2783412150 cites W2074994347 @default.
• W2783412150 cites W2083400479 @default.
• W2783412150 cites W2087428388 @default.
• W2783412150 cites W2092553210 @default.
• W2783412150 cites W2094269418 @default.
• W2783412150 cites W2189723472 @default.
• W2783412150 cites W2191248634 @default.
• W2783412150 cites W2324671925 @default.
• W2783412150 cites W2420214643 @default.
• W2783412150 cites W2470246674 @default.
• W2783412150 cites W2481840381 @default.
• W2783412150 cites W2491243921 @default.
• W2783412150 cites W2516069532 @default.
• W2783412150 cites W2565353100 @default.
• W2783412150 cites W2622573047 @default.
• W2783412150 doi "https://doi.org/10.1016/j.jallcom.2018.01.132" @default.
• W2783412150 hasPublicationYear "2018" @default.
• W2783412150 type Work @default.
• W2783412150 sameAs 2783412150 @default.
• W2783412150 citedByCount "8" @default.
• W2783412150 countsByYear W27834121502018 @default.
• W2783412150 countsByYear W27834121502019 @default.
• W2783412150 countsByYear W27834121502021 @default.
• W2783412150 countsByYear W27834121502022 @default.
• W2783412150 countsByYear W27834121502023 @default.
• W2783412150 crossrefType "journal-article" @default.
• W2783412150 hasAuthorship W2783412150A5026047135 @default.
• W2783412150 hasAuthorship W2783412150A5066659835 @default.
• W2783412150 hasConcept C121332964 @default.
• W2783412150 hasConcept C191897082 @default.
• W2783412150 hasConcept C192562407 @default.
• W2783412150 hasConcept C199360897 @default.
• W2783412150 hasConcept C20625102 @default.
• W2783412150 hasConcept C2776014600 @default.
• W2783412150 hasConcept C2777581544 @default.
• W2783412150 hasConcept C2780026712 @default.
• W2783412150 hasConcept C2781215313 @default.
• W2783412150 hasConcept C41008148 @default.
• W2783412150 hasConcept C62520636 @default.
• W2783412150 hasConcept C82706917 @default.
• W2783412150 hasConcept C87976508 @default.
• W2783412150 hasConceptScore W2783412150C121332964 @default.
• W2783412150 hasConceptScore W2783412150C191897082 @default.
• W2783412150 hasConceptScore W2783412150C192562407 @default.
• W2783412150 hasConceptScore W2783412150C199360897 @default.
• W2783412150 hasConceptScore W2783412150C20625102 @default.
• W2783412150 hasConceptScore W2783412150C2776014600 @default.
• W2783412150 hasConceptScore W2783412150C2777581544 @default.
• W2783412150 hasConceptScore W2783412150C2780026712 @default.
• W2783412150 hasConceptScore W2783412150C2781215313 @default.
• W2783412150 hasConceptScore W2783412150C41008148 @default.
• W2783412150 hasConceptScore W2783412150C62520636 @default.
• W2783412150 hasConceptScore W2783412150C82706917 @default.
• W2783412150 hasConceptScore W2783412150C87976508 @default.
• W2783412150 hasFunder F4320321001 @default.
• W2783412150 hasLocation W27834121501 @default.
• W2783412150 hasOpenAccess W2783412150 @default.
• W2783412150 hasPrimaryLocation W27834121501 @default.
• W2783412150 hasRelatedWork W1999962534 @default.
• W2783412150 hasRelatedWork W2348021511 @default.
• W2783412150 hasRelatedWork W2351555806 @default.
• W2783412150 hasRelatedWork W2355624270 @default.
• W2783412150 hasRelatedWork W2377428937 @default.

• next