- W2783608640 abstract "Abstract Two compositions of CuPd-V system filler alloy were designed for joining the Cf/SiBCN composite. Their dynamic wettability on the Cf/SiBCN composite was studied with the sessile drop method. The CuPd-8V alloy exhibited a contact angle of 57° after holding at 1170 °C for 30 min, whereas for CuPd-13V alloy, a lower contact angle of 28° can be achieved after heating at 1200 °C for 20 min. Sound Cf/SiBCN joints were successfully produced using the latter filler alloy under the brazing condition of (1170-1230)°C for 10 min. The results showed that the active element V strongly diffused to the surface of Cf/SiBCN composite, with the formation of V2C/VN reaction layer. The microstructure in the central part of the joint brazed at 1200 °C was characterized by the V2C/VN particles distributing scatteringly in CuPd matrix. The corresponding joints showed the maximum three-point bend strength of 82.4 MPa at room temperature. When the testing temperature was increased to 600 °C, the joint strength was even elevated to 108.8 MPa. Furthermore, the joints exhibited the strength of 92.4 MPa and 39.8 MPa at 800 °C and 900 °C, respectively." @default.
- W2783608640 created "2018-01-26" @default.
- W2783608640 creator A5013412329 @default.
- W2783608640 creator A5013442463 @default.
- W2783608640 creator A5015154135 @default.
- W2783608640 creator A5049839471 @default.
- W2783608640 creator A5062895384 @default.
- W2783608640 creator A5069377878 @default.
- W2783608640 date "2018-09-01" @default.
- W2783608640 modified "2023-10-16" @default.
- W2783608640 title "Joining of C f /SiBCN composite with CuPd-V filler alloy" @default.
- W2783608640 cites W1965626762 @default.
- W2783608640 cites W1993686518 @default.
- W2783608640 cites W1995185245 @default.
- W2783608640 cites W2003031777 @default.
- W2783608640 cites W2004029320 @default.
- W2783608640 cites W2006412423 @default.
- W2783608640 cites W2009739812 @default.
- W2783608640 cites W2010384392 @default.
- W2783608640 cites W2018044166 @default.
- W2783608640 cites W2023302040 @default.
- W2783608640 cites W2033579855 @default.
- W2783608640 cites W2034486542 @default.
- W2783608640 cites W2042367586 @default.
- W2783608640 cites W2044002018 @default.
- W2783608640 cites W2062566454 @default.
- W2783608640 cites W2066498418 @default.
- W2783608640 cites W2066888424 @default.
- W2783608640 cites W2071319701 @default.
- W2783608640 cites W2087738967 @default.
- W2783608640 cites W2148042987 @default.
- W2783608640 cites W2585494968 @default.
- W2783608640 cites W307305070 @default.
- W2783608640 doi "https://doi.org/10.1016/j.jmst.2018.01.001" @default.
- W2783608640 hasPublicationYear "2018" @default.
- W2783608640 type Work @default.
- W2783608640 sameAs 2783608640 @default.
- W2783608640 citedByCount "18" @default.
- W2783608640 countsByYear W27836086402019 @default.
- W2783608640 countsByYear W27836086402020 @default.
- W2783608640 countsByYear W27836086402021 @default.
- W2783608640 countsByYear W27836086402022 @default.
- W2783608640 countsByYear W27836086402023 @default.
- W2783608640 crossrefType "journal-article" @default.
- W2783608640 hasAuthorship W2783608640A5013412329 @default.
- W2783608640 hasAuthorship W2783608640A5013442463 @default.
- W2783608640 hasAuthorship W2783608640A5015154135 @default.
- W2783608640 hasAuthorship W2783608640A5049839471 @default.
- W2783608640 hasAuthorship W2783608640A5062895384 @default.
- W2783608640 hasAuthorship W2783608640A5069377878 @default.
- W2783608640 hasConcept C104779481 @default.
- W2783608640 hasConcept C127413603 @default.
- W2783608640 hasConcept C134514944 @default.
- W2783608640 hasConcept C159985019 @default.
- W2783608640 hasConcept C18555067 @default.
- W2783608640 hasConcept C192562407 @default.
- W2783608640 hasConcept C2778223994 @default.
- W2783608640 hasConcept C2780026712 @default.
- W2783608640 hasConcept C54517805 @default.
- W2783608640 hasConcept C6556556 @default.
- W2783608640 hasConcept C66938386 @default.
- W2783608640 hasConcept C86171150 @default.
- W2783608640 hasConcept C87976508 @default.
- W2783608640 hasConceptScore W2783608640C104779481 @default.
- W2783608640 hasConceptScore W2783608640C127413603 @default.
- W2783608640 hasConceptScore W2783608640C134514944 @default.
- W2783608640 hasConceptScore W2783608640C159985019 @default.
- W2783608640 hasConceptScore W2783608640C18555067 @default.
- W2783608640 hasConceptScore W2783608640C192562407 @default.
- W2783608640 hasConceptScore W2783608640C2778223994 @default.
- W2783608640 hasConceptScore W2783608640C2780026712 @default.
- W2783608640 hasConceptScore W2783608640C54517805 @default.
- W2783608640 hasConceptScore W2783608640C6556556 @default.
- W2783608640 hasConceptScore W2783608640C66938386 @default.
- W2783608640 hasConceptScore W2783608640C86171150 @default.
- W2783608640 hasConceptScore W2783608640C87976508 @default.
- W2783608640 hasFunder F4320321001 @default.
- W2783608640 hasFunder F4320322857 @default.
- W2783608640 hasIssue "9" @default.
- W2783608640 hasLocation W27836086401 @default.
- W2783608640 hasOpenAccess W2783608640 @default.
- W2783608640 hasPrimaryLocation W27836086401 @default.
- W2783608640 hasRelatedWork W1072657899 @default.
- W2783608640 hasRelatedWork W1982314687 @default.
- W2783608640 hasRelatedWork W2005496670 @default.
- W2783608640 hasRelatedWork W2075412258 @default.
- W2783608640 hasRelatedWork W2075449049 @default.
- W2783608640 hasRelatedWork W2358283384 @default.
- W2783608640 hasRelatedWork W2387193083 @default.
- W2783608640 hasRelatedWork W2970925637 @default.
- W2783608640 hasRelatedWork W3043268847 @default.
- W2783608640 hasRelatedWork W3048672776 @default.
- W2783608640 hasVolume "34" @default.
- W2783608640 isParatext "false" @default.
- W2783608640 isRetracted "false" @default.
- W2783608640 magId "2783608640" @default.
- W2783608640 workType "article" @default.