- W2784198626 abstract "In this paper, the activation energy of intermetallic layer growth was investigated for SAC305 (Sn/3Ag/0.5Cu) and Innolot (Sn/3.8Ag/0.7Cu/3Bi/1.5Sb/0.2Ni) lead-free solder alloys. A testboard was designed, which contained 50 pieces of 0603 size (1.5 × 0.75 mm) chip resistors. The solder paste was deposited by stencil printing, and the solder joints were formed with vapour phase soldering. The intermetallic layer growth was accelerated after soldering with HTSL (High Temperature Storage Life) testing at two different elevated temperatures; 100 and 150 °C. The HTSL testing was carried out for up to 1500 hours. In every 500 hours, samples were taken out from the test to measure the thickness of the intermetallic layer by analysing cross-sections with Scanning Electron Microscopy. It was found that the determined value of activation energy is influenced by the length of the HTSL testing. Since the uncertainty of the layer thickness measurements is higher at lower thicknesses (i.e. at the beginning of the HTSL testing), longer duration of testing (1500 hours at minimum) is recommended. Besides, the results showed that higher activation energy belongs to the layer growth in the Innolot alloy compared to the SAC305 alloy." @default.
- W2784198626 created "2018-01-26" @default.
- W2784198626 creator A5032052327 @default.
- W2784198626 creator A5032748749 @default.
- W2784198626 creator A5033913018 @default.
- W2784198626 date "2017-10-01" @default.
- W2784198626 modified "2023-09-25" @default.
- W2784198626 title "Investigating the activation energy of intermetallic layer growth in SAC305 and Innolot alloys" @default.
- W2784198626 cites W1492102692 @default.
- W2784198626 cites W1861504041 @default.
- W2784198626 cites W2012359014 @default.
- W2784198626 cites W2018730125 @default.
- W2784198626 cites W2067514682 @default.
- W2784198626 cites W2080086911 @default.
- W2784198626 cites W2090380067 @default.
- W2784198626 cites W2098684321 @default.
- W2784198626 cites W2158708207 @default.
- W2784198626 cites W2215276946 @default.
- W2784198626 cites W2278241798 @default.
- W2784198626 cites W2314638307 @default.
- W2784198626 cites W2501424599 @default.
- W2784198626 cites W2555206010 @default.
- W2784198626 cites W2556619361 @default.
- W2784198626 cites W2581150299 @default.
- W2784198626 cites W2581774905 @default.
- W2784198626 cites W2604812290 @default.
- W2784198626 cites W2617068013 @default.
- W2784198626 doi "https://doi.org/10.1109/siitme.2017.8259860" @default.
- W2784198626 hasPublicationYear "2017" @default.
- W2784198626 type Work @default.
- W2784198626 sameAs 2784198626 @default.
- W2784198626 citedByCount "1" @default.
- W2784198626 countsByYear W27841986262020 @default.
- W2784198626 crossrefType "proceedings-article" @default.
- W2784198626 hasAuthorship W2784198626A5032052327 @default.
- W2784198626 hasAuthorship W2784198626A5032748749 @default.
- W2784198626 hasAuthorship W2784198626A5033913018 @default.
- W2784198626 hasConcept C159985019 @default.
- W2784198626 hasConcept C178790620 @default.
- W2784198626 hasConcept C185592680 @default.
- W2784198626 hasConcept C191897082 @default.
- W2784198626 hasConcept C192562407 @default.
- W2784198626 hasConcept C26771246 @default.
- W2784198626 hasConcept C27501479 @default.
- W2784198626 hasConcept C2779227376 @default.
- W2784198626 hasConcept C2780026712 @default.
- W2784198626 hasConcept C50296614 @default.
- W2784198626 hasConcept C95121573 @default.
- W2784198626 hasConceptScore W2784198626C159985019 @default.
- W2784198626 hasConceptScore W2784198626C178790620 @default.
- W2784198626 hasConceptScore W2784198626C185592680 @default.
- W2784198626 hasConceptScore W2784198626C191897082 @default.
- W2784198626 hasConceptScore W2784198626C192562407 @default.
- W2784198626 hasConceptScore W2784198626C26771246 @default.
- W2784198626 hasConceptScore W2784198626C27501479 @default.
- W2784198626 hasConceptScore W2784198626C2779227376 @default.
- W2784198626 hasConceptScore W2784198626C2780026712 @default.
- W2784198626 hasConceptScore W2784198626C50296614 @default.
- W2784198626 hasConceptScore W2784198626C95121573 @default.
- W2784198626 hasLocation W27841986261 @default.
- W2784198626 hasOpenAccess W2784198626 @default.
- W2784198626 hasPrimaryLocation W27841986261 @default.
- W2784198626 hasRelatedWork W1538680351 @default.
- W2784198626 hasRelatedWork W1907908258 @default.
- W2784198626 hasRelatedWork W1911316188 @default.
- W2784198626 hasRelatedWork W2002632946 @default.
- W2784198626 hasRelatedWork W2020076017 @default.
- W2784198626 hasRelatedWork W2084879493 @default.
- W2784198626 hasRelatedWork W226665456 @default.
- W2784198626 hasRelatedWork W2610646289 @default.
- W2784198626 hasRelatedWork W2742535772 @default.
- W2784198626 hasRelatedWork W2789334033 @default.
- W2784198626 hasRelatedWork W2804937110 @default.
- W2784198626 hasRelatedWork W2809778628 @default.
- W2784198626 hasRelatedWork W2886251612 @default.
- W2784198626 hasRelatedWork W2887563250 @default.
- W2784198626 hasRelatedWork W2970144284 @default.
- W2784198626 hasRelatedWork W3022502358 @default.
- W2784198626 hasRelatedWork W3036238324 @default.
- W2784198626 hasRelatedWork W3043721633 @default.
- W2784198626 hasRelatedWork W3088500585 @default.
- W2784198626 hasRelatedWork W55600921 @default.
- W2784198626 isParatext "false" @default.
- W2784198626 isRetracted "false" @default.
- W2784198626 magId "2784198626" @default.
- W2784198626 workType "article" @default.