- W2790981799 abstract "Aluminum doped zinc oxide (AZO) thin films for electrode applications were deposited on glass substrates using chemical bath deposition (CBD) method. The influence of deposition time on the structural, morphological, and opto-electrical properties of AZO films were investigated. Structural studies confirmed that all the deposited films were hexagonal wurtzite structure with polycrystalline nature and exhibited (002) preferential orientation. There is no other impurity phases were detected for different deposition time. Surface morphological images shows the spherically shaped grains are uniformly arranged on to the entire film surface. The EDS spectrum confirms the presence of Zn, O and Al elements in deposited AZO film. The observed optical transmittance is high (87%) in the visible region, and the calculated band gap value is 3.27 eV. In this study, the transmittance value is decreased with increasing deposition time. The room temperature PL spectrum exposed that AZO thin film deposited at (60 min) has good optical quality with less defect density. The minimum electrical resistivity and maximum carrier concentration values were observed as 8.53 × 10−3(Ω cm) and 3.53 × 1018 cm−3 for 60 min deposited film, respectively. The obtained figure of merit (ϕ) value 3.05 × 10−3(Ω/sq)- 1 is suggested for an optoelectronic device." @default.
- W2790981799 created "2018-03-29" @default.
- W2790981799 creator A5010489562 @default.
- W2790981799 creator A5022549410 @default.
- W2790981799 creator A5032116740 @default.
- W2790981799 creator A5034465865 @default.
- W2790981799 creator A5039428066 @default.
- W2790981799 creator A5058610221 @default.
- W2790981799 creator A5066850882 @default.
- W2790981799 date "2018-04-01" @default.
- W2790981799 modified "2023-09-23" @default.
- W2790981799 title "Evaluation of the structural, optical and electrical properties of AZO thin films prepared by chemical bath deposition for optoelectronics" @default.
- W2790981799 cites W1649333840 @default.
- W2790981799 cites W1967652077 @default.
- W2790981799 cites W1974286248 @default.
- W2790981799 cites W1976149429 @default.
- W2790981799 cites W1978418537 @default.
- W2790981799 cites W1979056121 @default.
- W2790981799 cites W1980960645 @default.
- W2790981799 cites W1985012819 @default.
- W2790981799 cites W2002159152 @default.
- W2790981799 cites W2003894252 @default.
- W2790981799 cites W2006434183 @default.
- W2790981799 cites W2014976987 @default.
- W2790981799 cites W2015566956 @default.
- W2790981799 cites W2021898183 @default.
- W2790981799 cites W2024745050 @default.
- W2790981799 cites W2029945349 @default.
- W2790981799 cites W2032334297 @default.
- W2790981799 cites W2038189835 @default.
- W2790981799 cites W2040875144 @default.
- W2790981799 cites W2052344653 @default.
- W2790981799 cites W2060009161 @default.
- W2790981799 cites W2061202348 @default.
- W2790981799 cites W2068746295 @default.
- W2790981799 cites W2071350038 @default.
- W2790981799 cites W2071593002 @default.
- W2790981799 cites W2075157799 @default.
- W2790981799 cites W2075563702 @default.
- W2790981799 cites W2077836727 @default.
- W2790981799 cites W2083230046 @default.
- W2790981799 cites W2085774152 @default.
- W2790981799 cites W2092034885 @default.
- W2790981799 cites W2092429450 @default.
- W2790981799 cites W2098496098 @default.
- W2790981799 cites W2111826330 @default.
- W2790981799 cites W2115170047 @default.
- W2790981799 cites W2141979520 @default.
- W2790981799 cites W2169569347 @default.
- W2790981799 cites W2243960803 @default.
- W2790981799 cites W2301688338 @default.
- W2790981799 cites W2337626438 @default.
- W2790981799 cites W2547718175 @default.
- W2790981799 cites W2656240048 @default.
- W2790981799 cites W2740505795 @default.
- W2790981799 cites W2745233720 @default.
- W2790981799 cites W2756875373 @default.
- W2790981799 cites W2768159666 @default.
- W2790981799 cites W2770041802 @default.
- W2790981799 cites W3100455648 @default.
- W2790981799 cites W3105050841 @default.
- W2790981799 cites W4238847701 @default.
- W2790981799 doi "https://doi.org/10.1016/j.solidstatesciences.2018.02.003" @default.
- W2790981799 hasPublicationYear "2018" @default.
- W2790981799 type Work @default.
- W2790981799 sameAs 2790981799 @default.
- W2790981799 citedByCount "30" @default.
- W2790981799 countsByYear W27909817992018 @default.
- W2790981799 countsByYear W27909817992019 @default.
- W2790981799 countsByYear W27909817992020 @default.
- W2790981799 countsByYear W27909817992021 @default.
- W2790981799 countsByYear W27909817992022 @default.
- W2790981799 countsByYear W27909817992023 @default.
- W2790981799 crossrefType "journal-article" @default.
- W2790981799 hasAuthorship W2790981799A5010489562 @default.
- W2790981799 hasAuthorship W2790981799A5022549410 @default.
- W2790981799 hasAuthorship W2790981799A5032116740 @default.
- W2790981799 hasAuthorship W2790981799A5034465865 @default.
- W2790981799 hasAuthorship W2790981799A5039428066 @default.
- W2790981799 hasAuthorship W2790981799A5058610221 @default.
- W2790981799 hasAuthorship W2790981799A5066850882 @default.
- W2790981799 hasConcept C113196181 @default.
- W2790981799 hasConcept C119599485 @default.
- W2790981799 hasConcept C127413603 @default.
- W2790981799 hasConcept C137637335 @default.
- W2790981799 hasConcept C150493377 @default.
- W2790981799 hasConcept C151730666 @default.
- W2790981799 hasConcept C171250308 @default.
- W2790981799 hasConcept C181966813 @default.
- W2790981799 hasConcept C185592680 @default.
- W2790981799 hasConcept C19067145 @default.
- W2790981799 hasConcept C191897082 @default.
- W2790981799 hasConcept C192562407 @default.
- W2790981799 hasConcept C2780228366 @default.
- W2790981799 hasConcept C2816523 @default.
- W2790981799 hasConcept C3045981 @default.
- W2790981799 hasConcept C43617362 @default.
- W2790981799 hasConcept C49040817 @default.