- W2793545179 abstract "Vacuum diffusion bonding (DB) of as-extruded Ti-47.5Al-Cr-V (at.%) alloy was carried out at 1000–1100 °C at a pressure of 10–30 MPa for 1–3 h, and the bonded joints were post-bond heat treated (PBHT) at 1360 °C for 0.5 h. Subsequently, the shear strength of all the joints was measured, and the microstructure was observed. The results showed that the shear strength and bonding interface quality of joints increased under as-bonded and PBHT conditions with the increase of each bonding parameter (temperature, pressure, and time). The shear strength of the base material was 486 MPa, and it was 665 MPa after PBHT. Furthermore, the maximum shear strength of the as-bonded joints was over 80% of that of the base material. After PBHT, the maximum strength of the joints was nearly equal to that of the base material. The fracture morphologies of the as-bonded and PBHT joints were analyzed, and the fracture mode was changed from transgranular fracture to intergranular fracture. The optimal bonding parameters were proposed: T ≥ 1050 °C, p ≥ 20 MPa, and t ≥ 2 h." @default.
- W2793545179 created "2018-03-29" @default.
- W2793545179 creator A5005249011 @default.
- W2793545179 creator A5081219089 @default.
- W2793545179 creator A5090288992 @default.
- W2793545179 creator A5091397957 @default.
- W2793545179 date "2018-04-01" @default.
- W2793545179 modified "2023-10-01" @default.
- W2793545179 title "Microstructure and mechanical properties of vacuum diffusion bonding joints for γ-TiAl based alloy" @default.
- W2793545179 cites W1964063220 @default.
- W2793545179 cites W1972348129 @default.
- W2793545179 cites W1972470926 @default.
- W2793545179 cites W1972560513 @default.
- W2793545179 cites W1973147703 @default.
- W2793545179 cites W1984861527 @default.
- W2793545179 cites W1987615425 @default.
- W2793545179 cites W1989629335 @default.
- W2793545179 cites W1991872686 @default.
- W2793545179 cites W1998694220 @default.
- W2793545179 cites W2000384931 @default.
- W2793545179 cites W2009066746 @default.
- W2793545179 cites W2009976463 @default.
- W2793545179 cites W2011703771 @default.
- W2793545179 cites W2014394820 @default.
- W2793545179 cites W2016309369 @default.
- W2793545179 cites W2023914344 @default.
- W2793545179 cites W2030403962 @default.
- W2793545179 cites W2060692049 @default.
- W2793545179 cites W2061562577 @default.
- W2793545179 cites W2075318382 @default.
- W2793545179 cites W2075868561 @default.
- W2793545179 cites W2076925161 @default.
- W2793545179 cites W2093186681 @default.
- W2793545179 cites W2136749837 @default.
- W2793545179 cites W2144767248 @default.
- W2793545179 cites W2157391576 @default.
- W2793545179 cites W2185166758 @default.
- W2793545179 cites W2188219885 @default.
- W2793545179 cites W4236840542 @default.
- W2793545179 cites W4376849354 @default.
- W2793545179 doi "https://doi.org/10.1016/j.vacuum.2018.01.035" @default.
- W2793545179 hasPublicationYear "2018" @default.
- W2793545179 type Work @default.
- W2793545179 sameAs 2793545179 @default.
- W2793545179 citedByCount "24" @default.
- W2793545179 countsByYear W27935451792018 @default.
- W2793545179 countsByYear W27935451792019 @default.
- W2793545179 countsByYear W27935451792020 @default.
- W2793545179 countsByYear W27935451792021 @default.
- W2793545179 countsByYear W27935451792022 @default.
- W2793545179 countsByYear W27935451792023 @default.
- W2793545179 crossrefType "journal-article" @default.
- W2793545179 hasAuthorship W2793545179A5005249011 @default.
- W2793545179 hasAuthorship W2793545179A5081219089 @default.
- W2793545179 hasAuthorship W2793545179A5090288992 @default.
- W2793545179 hasAuthorship W2793545179A5091397957 @default.
- W2793545179 hasConcept C127893833 @default.
- W2793545179 hasConcept C159390177 @default.
- W2793545179 hasConcept C159750122 @default.
- W2793545179 hasConcept C159985019 @default.
- W2793545179 hasConcept C184102282 @default.
- W2793545179 hasConcept C191897082 @default.
- W2793545179 hasConcept C192562407 @default.
- W2793545179 hasConcept C2777820655 @default.
- W2793545179 hasConcept C2778856520 @default.
- W2793545179 hasConcept C2779930716 @default.
- W2793545179 hasConcept C2780026712 @default.
- W2793545179 hasConcept C39432304 @default.
- W2793545179 hasConcept C43369102 @default.
- W2793545179 hasConcept C87976508 @default.
- W2793545179 hasConcept C96035792 @default.
- W2793545179 hasConceptScore W2793545179C127893833 @default.
- W2793545179 hasConceptScore W2793545179C159390177 @default.
- W2793545179 hasConceptScore W2793545179C159750122 @default.
- W2793545179 hasConceptScore W2793545179C159985019 @default.
- W2793545179 hasConceptScore W2793545179C184102282 @default.
- W2793545179 hasConceptScore W2793545179C191897082 @default.
- W2793545179 hasConceptScore W2793545179C192562407 @default.
- W2793545179 hasConceptScore W2793545179C2777820655 @default.
- W2793545179 hasConceptScore W2793545179C2778856520 @default.
- W2793545179 hasConceptScore W2793545179C2779930716 @default.
- W2793545179 hasConceptScore W2793545179C2780026712 @default.
- W2793545179 hasConceptScore W2793545179C39432304 @default.
- W2793545179 hasConceptScore W2793545179C43369102 @default.
- W2793545179 hasConceptScore W2793545179C87976508 @default.
- W2793545179 hasConceptScore W2793545179C96035792 @default.
- W2793545179 hasFunder F4320323019 @default.
- W2793545179 hasLocation W27935451791 @default.
- W2793545179 hasOpenAccess W2793545179 @default.
- W2793545179 hasPrimaryLocation W27935451791 @default.
- W2793545179 hasRelatedWork W2006655165 @default.
- W2793545179 hasRelatedWork W2007194129 @default.
- W2793545179 hasRelatedWork W2030530812 @default.
- W2793545179 hasRelatedWork W2075158516 @default.
- W2793545179 hasRelatedWork W2356474439 @default.
- W2793545179 hasRelatedWork W2375392305 @default.
- W2793545179 hasRelatedWork W2382617490 @default.
- W2793545179 hasRelatedWork W2500383359 @default.