- W2796222594 abstract "A broken missile radome made of cordierite-based glass–ceramic was analyzed to identify the root cause and the mechanism of the fracture. In the fractographic analysis, the calculated critical flaw size, 144 μm, was larger than the actual flaw size at the fracture origin, 65 μm. Numerous microcracks were also found throughout the radome. In the physicochemical analysis, silanol (Si–OH) groups were detected at all the investigated sites on the fracture surface. The stress analysis verified that the tensile stress, driving the crack growth, is generated at the inner layer of the radome during flight. All these results strongly suggest that the failure of the radome was attributable to slow crack growth, the key mechanism of which was stress corrosion. It is highly probable that the widely distributed microcracks helped water to permeate the radome, thereby providing conditions for stress corrosion. This study demonstrates that the combined and synergistic interaction of mechanical stress and corrosion reactions iteratively occurred inside the radome through repeated flights and prolonged exposure to atmospheric moisture, consequently resulting in the radome failure." @default.
- W2796222594 created "2018-04-13" @default.
- W2796222594 creator A5005052064 @default.
- W2796222594 creator A5010027331 @default.
- W2796222594 creator A5010266051 @default.
- W2796222594 date "2018-11-01" @default.
- W2796222594 modified "2023-10-18" @default.
- W2796222594 title "Slow crack growth in a cordierite-based glass–ceramic missile radome due to stress corrosion" @default.
- W2796222594 cites W1968850951 @default.
- W2796222594 cites W1969970543 @default.
- W2796222594 cites W1972949788 @default.
- W2796222594 cites W1987601752 @default.
- W2796222594 cites W1987709410 @default.
- W2796222594 cites W2024104616 @default.
- W2796222594 cites W2035478663 @default.
- W2796222594 cites W2045064685 @default.
- W2796222594 cites W2072216894 @default.
- W2796222594 cites W2097141594 @default.
- W2796222594 cites W2101108516 @default.
- W2796222594 cites W2114601214 @default.
- W2796222594 cites W2119262882 @default.
- W2796222594 cites W2130852116 @default.
- W2796222594 cites W2131300332 @default.
- W2796222594 cites W2153007638 @default.
- W2796222594 cites W2159749952 @default.
- W2796222594 cites W2162357431 @default.
- W2796222594 cites W2164681197 @default.
- W2796222594 cites W2169352784 @default.
- W2796222594 doi "https://doi.org/10.1016/j.engfailanal.2018.04.007" @default.
- W2796222594 hasPublicationYear "2018" @default.
- W2796222594 type Work @default.
- W2796222594 sameAs 2796222594 @default.
- W2796222594 citedByCount "4" @default.
- W2796222594 countsByYear W27962225942021 @default.
- W2796222594 countsByYear W27962225942022 @default.
- W2796222594 countsByYear W27962225942023 @default.
- W2796222594 crossrefType "journal-article" @default.
- W2796222594 hasAuthorship W2796222594A5005052064 @default.
- W2796222594 hasAuthorship W2796222594A5010027331 @default.
- W2796222594 hasAuthorship W2796222594A5010266051 @default.
- W2796222594 hasConcept C127413603 @default.
- W2796222594 hasConcept C134132462 @default.
- W2796222594 hasConcept C138885662 @default.
- W2796222594 hasConcept C153159894 @default.
- W2796222594 hasConcept C159985019 @default.
- W2796222594 hasConcept C192562407 @default.
- W2796222594 hasConcept C20625102 @default.
- W2796222594 hasConcept C21036866 @default.
- W2796222594 hasConcept C21822782 @default.
- W2796222594 hasConcept C41895202 @default.
- W2796222594 hasConcept C43369102 @default.
- W2796222594 hasConcept C76155785 @default.
- W2796222594 hasConcept C77595967 @default.
- W2796222594 hasConceptScore W2796222594C127413603 @default.
- W2796222594 hasConceptScore W2796222594C134132462 @default.
- W2796222594 hasConceptScore W2796222594C138885662 @default.
- W2796222594 hasConceptScore W2796222594C153159894 @default.
- W2796222594 hasConceptScore W2796222594C159985019 @default.
- W2796222594 hasConceptScore W2796222594C192562407 @default.
- W2796222594 hasConceptScore W2796222594C20625102 @default.
- W2796222594 hasConceptScore W2796222594C21036866 @default.
- W2796222594 hasConceptScore W2796222594C21822782 @default.
- W2796222594 hasConceptScore W2796222594C41895202 @default.
- W2796222594 hasConceptScore W2796222594C43369102 @default.
- W2796222594 hasConceptScore W2796222594C76155785 @default.
- W2796222594 hasConceptScore W2796222594C77595967 @default.
- W2796222594 hasLocation W27962225941 @default.
- W2796222594 hasOpenAccess W2796222594 @default.
- W2796222594 hasPrimaryLocation W27962225941 @default.
- W2796222594 hasRelatedWork W2137307547 @default.
- W2796222594 hasRelatedWork W2281145519 @default.
- W2796222594 hasRelatedWork W2380293314 @default.
- W2796222594 hasRelatedWork W2610509641 @default.
- W2796222594 hasRelatedWork W2943188944 @default.
- W2796222594 hasRelatedWork W3082440218 @default.
- W2796222594 hasRelatedWork W3097783663 @default.
- W2796222594 hasRelatedWork W3135117324 @default.
- W2796222594 hasRelatedWork W4285802202 @default.
- W2796222594 hasRelatedWork W4366262926 @default.
- W2796222594 hasVolume "93" @default.
- W2796222594 isParatext "false" @default.
- W2796222594 isRetracted "false" @default.
- W2796222594 magId "2796222594" @default.
- W2796222594 workType "article" @default.