- W2800329137 abstract "Fe-8Mn alloys may form the basis of a cryogenic steel similar to Fe-9Ni steels, but at a cost much more economical as manganese is cheaper than nickel. However, Fe-Mn alloys are susceptible to temper embrittlement through segregation of Mn, N and P to prior austenite grain boundaries. The present investigation shows that impact toughness can be improved by tempering to produce small amounts of reverted austenite into the structure. In quantifying the percentages of reverted austenite in these structures. X-ray and Mossbauer studies have shown that the phase analysis of these alloys varies from the surface of specimens into the bulk, and is thought to be due to deformation induced transformation of gamma→epsilon during sample preparation. It was concluded that bulk austenite and epsilon concentrations are best obtained after 2 minutes electro--polishing. Additions of 0.1%Ti and 0.1%Al to 'pure' alloys, in order to getter nitrogen, have been found to improve impact properties by reducing intergranular embrittlement. These additions also lead to a 'massive ferrite' structure not previously found in alloys of this manganese level. This is thought to be due to the lower interstitial levels in solid solution favouring formation of massive ferrite rather than lath martensite at a higher cooling rate and lower transformation temperature. A further considerable improvement in toughness has been achieved by water quenching rather than air cooling from the austenitisation temparature. Auger electron spectroscopy studies have shown that air cooling results in segregation of phosphorus and nitrogen to prior austenite grain boundaries. An addition of 0.5%Mo to these alloys was found not to be completely effective in reducing intergranular embrittlement.Commercially 'impure' alloys were found to exhibit inferior impact properties compared to 'pure' alloys. A further comparison with 9% nickel and 5% nickel steels has shown that pure Fe-8Mn alloys could be used as a low temperature steel down to ~ -100°C. A 'novel' heat treatment to an Fe-8Mn-G.2V alloy, consisting of a solution treatment followed by low temperature ageing has shown that vanadium carbide precipitation produces a significant reduction in grain size upon re-austenitisation due to particle pinning of grain boundaries." @default.
- W2800329137 created "2018-05-17" @default.
- W2800329137 creator A5009919125 @default.
- W2800329137 date "1989-01-01" @default.
- W2800329137 modified "2023-09-27" @default.
- W2800329137 title "The impact toughness of iron manganese alloys" @default.
- W2800329137 hasPublicationYear "1989" @default.
- W2800329137 type Work @default.
- W2800329137 sameAs 2800329137 @default.
- W2800329137 citedByCount "0" @default.
- W2800329137 crossrefType "dissertation" @default.
- W2800329137 hasAuthorship W2800329137A5009919125 @default.
- W2800329137 hasConcept C121332964 @default.
- W2800329137 hasConcept C121745418 @default.
- W2800329137 hasConcept C142282041 @default.
- W2800329137 hasConcept C159985019 @default.
- W2800329137 hasConcept C18747287 @default.
- W2800329137 hasConcept C191897082 @default.
- W2800329137 hasConcept C192562407 @default.
- W2800329137 hasConcept C207948433 @default.
- W2800329137 hasConcept C37210646 @default.
- W2800329137 hasConcept C47908070 @default.
- W2800329137 hasConcept C528890316 @default.
- W2800329137 hasConcept C62520636 @default.
- W2800329137 hasConcept C87976508 @default.
- W2800329137 hasConcept C91881484 @default.
- W2800329137 hasConcept C96288455 @default.
- W2800329137 hasConcept C99595764 @default.
- W2800329137 hasConceptScore W2800329137C121332964 @default.
- W2800329137 hasConceptScore W2800329137C121745418 @default.
- W2800329137 hasConceptScore W2800329137C142282041 @default.
- W2800329137 hasConceptScore W2800329137C159985019 @default.
- W2800329137 hasConceptScore W2800329137C18747287 @default.
- W2800329137 hasConceptScore W2800329137C191897082 @default.
- W2800329137 hasConceptScore W2800329137C192562407 @default.
- W2800329137 hasConceptScore W2800329137C207948433 @default.
- W2800329137 hasConceptScore W2800329137C37210646 @default.
- W2800329137 hasConceptScore W2800329137C47908070 @default.
- W2800329137 hasConceptScore W2800329137C528890316 @default.
- W2800329137 hasConceptScore W2800329137C62520636 @default.
- W2800329137 hasConceptScore W2800329137C87976508 @default.
- W2800329137 hasConceptScore W2800329137C91881484 @default.
- W2800329137 hasConceptScore W2800329137C96288455 @default.
- W2800329137 hasConceptScore W2800329137C99595764 @default.
- W2800329137 hasLocation W28003291371 @default.
- W2800329137 hasOpenAccess W2800329137 @default.
- W2800329137 hasPrimaryLocation W28003291371 @default.
- W2800329137 hasRelatedWork W116416471 @default.
- W2800329137 hasRelatedWork W1541321989 @default.
- W2800329137 hasRelatedWork W1973205113 @default.
- W2800329137 hasRelatedWork W1982064697 @default.
- W2800329137 hasRelatedWork W2000472627 @default.
- W2800329137 hasRelatedWork W2002491799 @default.
- W2800329137 hasRelatedWork W2008900151 @default.
- W2800329137 hasRelatedWork W2010205005 @default.
- W2800329137 hasRelatedWork W2032091105 @default.
- W2800329137 hasRelatedWork W2032350192 @default.
- W2800329137 hasRelatedWork W2032469200 @default.
- W2800329137 hasRelatedWork W2045127556 @default.
- W2800329137 hasRelatedWork W2061519685 @default.
- W2800329137 hasRelatedWork W2142341898 @default.
- W2800329137 hasRelatedWork W2309914051 @default.
- W2800329137 hasRelatedWork W2796703529 @default.
- W2800329137 hasRelatedWork W2980037370 @default.
- W2800329137 hasRelatedWork W3013485693 @default.
- W2800329137 hasRelatedWork W3014114562 @default.
- W2800329137 hasRelatedWork W3138877423 @default.
- W2800329137 isParatext "false" @default.
- W2800329137 isRetracted "false" @default.
- W2800329137 magId "2800329137" @default.
- W2800329137 workType "dissertation" @default.