- W2802070070 abstract "Reflective pigment was prepared by using Fe 2 O 3 and Al 2 O 3 as starting materials. Fe 2 O 3 and Al 2 O 3 powders were mixed at 0.8:2, 1:2 and 1.2:2 mole ratio using ball milling. The mixed powders were dried and calcined at temperature of 1500°C, 1600°C and 1700°C for various soaking time at 2, 8 and 20 h. Phase data were analyzed by x-ray diffractometry. It was found that (Al 1-x , Fe x ) 2 O 3 presented as a new phase in calcined powders at temperature of 1500°C to 1700°C for 2 h. The other new phase such as FeAl 2 O 4 was detected in calcined powders at temperature of 1700°C for 8 and 20 h. From the experimental results indicated that complete reaction was occurred when higher calcination temperature and longer soaking time were used, resulting in spinel structure (FeAl 2 O 4 ) generated. Then, the synthesized powders were mixed with exterior paint by mass ratio of 0:100, 10:90, 20:80, 30:70 and 40:60, respectively. The mixed paints were sprayed on metal sheets. Then the coated metal sheets were exposed under 200 watts lamb and measured the temperature difference between the exposed side and opposite side. The result showed that at the ratio of 30:70 exhibited the highest temperature difference of 14°C approximately. From the result, we concluded that spinel structure (FeAl 2 O 4 ) is a candidate for near-infrared (NIR) reflective pigment of exterior paint." @default.
- W2802070070 created "2018-05-17" @default.
- W2802070070 creator A5001330358 @default.
- W2802070070 creator A5012320133 @default.
- W2802070070 creator A5019188923 @default.
- W2802070070 creator A5034954488 @default.
- W2802070070 creator A5045202930 @default.
- W2802070070 creator A5071457731 @default.
- W2802070070 date "2018-04-01" @default.
- W2802070070 modified "2023-09-24" @default.
- W2802070070 title "Preparation of Near-Infrared (NIR) Reflective Pigment by Solid State Reaction between Fe<sub>2</sub>O<sub>3</sub> and Al<sub>2</sub>O<sub>3</sub>" @default.
- W2802070070 cites W1964376555 @default.
- W2802070070 cites W1970911600 @default.
- W2802070070 cites W1987018115 @default.
- W2802070070 cites W2062781703 @default.
- W2802070070 cites W2070320056 @default.
- W2802070070 cites W2079494230 @default.
- W2802070070 cites W2141119394 @default.
- W2802070070 cites W2145917317 @default.
- W2802070070 cites W2396572089 @default.
- W2802070070 cites W2529857801 @default.
- W2802070070 cites W2556072152 @default.
- W2802070070 cites W2575379537 @default.
- W2802070070 doi "https://doi.org/10.4028/www.scientific.net/kem.766.127" @default.
- W2802070070 hasPublicationYear "2018" @default.
- W2802070070 type Work @default.
- W2802070070 sameAs 2802070070 @default.
- W2802070070 citedByCount "3" @default.
- W2802070070 countsByYear W28020700702019 @default.
- W2802070070 countsByYear W28020700702021 @default.
- W2802070070 countsByYear W28020700702023 @default.
- W2802070070 crossrefType "journal-article" @default.
- W2802070070 hasAuthorship W2802070070A5001330358 @default.
- W2802070070 hasAuthorship W2802070070A5012320133 @default.
- W2802070070 hasAuthorship W2802070070A5019188923 @default.
- W2802070070 hasAuthorship W2802070070A5034954488 @default.
- W2802070070 hasAuthorship W2802070070A5045202930 @default.
- W2802070070 hasAuthorship W2802070070A5071457731 @default.
- W2802070070 hasConcept C107814960 @default.
- W2802070070 hasConcept C113196181 @default.
- W2802070070 hasConcept C13965031 @default.
- W2802070070 hasConcept C147789679 @default.
- W2802070070 hasConcept C161790260 @default.
- W2802070070 hasConcept C185592680 @default.
- W2802070070 hasConcept C191897082 @default.
- W2802070070 hasConcept C192562407 @default.
- W2802070070 hasConcept C199289684 @default.
- W2802070070 hasConcept C27501479 @default.
- W2802070070 hasConcept C2775924341 @default.
- W2802070070 hasConcept C2776230739 @default.
- W2802070070 hasConcept C2780026712 @default.
- W2802070070 hasConcept C43617362 @default.
- W2802070070 hasConcept C544153396 @default.
- W2802070070 hasConcept C55493867 @default.
- W2802070070 hasConcept C7082614 @default.
- W2802070070 hasConceptScore W2802070070C107814960 @default.
- W2802070070 hasConceptScore W2802070070C113196181 @default.
- W2802070070 hasConceptScore W2802070070C13965031 @default.
- W2802070070 hasConceptScore W2802070070C147789679 @default.
- W2802070070 hasConceptScore W2802070070C161790260 @default.
- W2802070070 hasConceptScore W2802070070C185592680 @default.
- W2802070070 hasConceptScore W2802070070C191897082 @default.
- W2802070070 hasConceptScore W2802070070C192562407 @default.
- W2802070070 hasConceptScore W2802070070C199289684 @default.
- W2802070070 hasConceptScore W2802070070C27501479 @default.
- W2802070070 hasConceptScore W2802070070C2775924341 @default.
- W2802070070 hasConceptScore W2802070070C2776230739 @default.
- W2802070070 hasConceptScore W2802070070C2780026712 @default.
- W2802070070 hasConceptScore W2802070070C43617362 @default.
- W2802070070 hasConceptScore W2802070070C544153396 @default.
- W2802070070 hasConceptScore W2802070070C55493867 @default.
- W2802070070 hasConceptScore W2802070070C7082614 @default.
- W2802070070 hasLocation W28020700701 @default.
- W2802070070 hasOpenAccess W2802070070 @default.
- W2802070070 hasPrimaryLocation W28020700701 @default.
- W2802070070 hasRelatedWork W2023478225 @default.
- W2802070070 hasRelatedWork W2043638660 @default.
- W2802070070 hasRelatedWork W2078868717 @default.
- W2802070070 hasRelatedWork W2116153407 @default.
- W2802070070 hasRelatedWork W2374760632 @default.
- W2802070070 hasRelatedWork W2380549929 @default.
- W2802070070 hasRelatedWork W2771802591 @default.
- W2802070070 hasRelatedWork W2802070070 @default.
- W2802070070 hasRelatedWork W2950882598 @default.
- W2802070070 hasRelatedWork W2773026377 @default.
- W2802070070 hasVolume "766" @default.
- W2802070070 isParatext "false" @default.
- W2802070070 isRetracted "false" @default.
- W2802070070 magId "2802070070" @default.
- W2802070070 workType "article" @default.