- W2802074450 abstract "The micro-mechanism of creep-fatigue interaction of novel 9% chromium tempered martensitic steel, G115, was investigated after creep-fatigue crack growth experiment using compact tension (CT) specimens. It indicated that the mode of crack growth changed from transgranular to intergranular when the crack growth stage changed from the initial to the accelerated region. At the initial crack growth region, fatigue striations and fatigue bands were observed. Then, creep voids were nucleated and the number increased. In addition, many secondary cracks were generated at the second stage and the number of cracks were increased steeply when the crack growth rate was accelerated at the tertiary crack growth stage. Furthermore, the variation of the creep, fatigue and the interaction damage during the crack growth process was analyzed using numerical simulation. The results agreed with experiment which illustrated that creep damage increased and fatigue damage reduced from the initial to the third crack growth stage and the increased interaction damage aggravated the crack propagation." @default.
- W2802074450 created "2018-05-17" @default.
- W2802074450 creator A5038657036 @default.
- W2802074450 creator A5056994271 @default.
- W2802074450 creator A5068130877 @default.
- W2802074450 creator A5075233046 @default.
- W2802074450 creator A5081728670 @default.
- W2802074450 date "2018-05-01" @default.
- W2802074450 modified "2023-09-27" @default.
- W2802074450 title "Creep-fatigue crack growth behavior of G115 steel at 650 °C" @default.
- W2802074450 cites W1431434712 @default.
- W2802074450 cites W1547535964 @default.
- W2802074450 cites W1965221057 @default.
- W2802074450 cites W1965764258 @default.
- W2802074450 cites W1971290298 @default.
- W2802074450 cites W1971590772 @default.
- W2802074450 cites W1976161994 @default.
- W2802074450 cites W1981553177 @default.
- W2802074450 cites W1985093844 @default.
- W2802074450 cites W1989407345 @default.
- W2802074450 cites W1989611345 @default.
- W2802074450 cites W2000335607 @default.
- W2802074450 cites W2001130040 @default.
- W2802074450 cites W2001446198 @default.
- W2802074450 cites W2001886687 @default.
- W2802074450 cites W2003345364 @default.
- W2802074450 cites W2003525673 @default.
- W2802074450 cites W2004491319 @default.
- W2802074450 cites W2004998051 @default.
- W2802074450 cites W2006278547 @default.
- W2802074450 cites W2009810034 @default.
- W2802074450 cites W2018349514 @default.
- W2802074450 cites W2022938880 @default.
- W2802074450 cites W2026899283 @default.
- W2802074450 cites W2028476694 @default.
- W2802074450 cites W2032390362 @default.
- W2802074450 cites W2035467092 @default.
- W2802074450 cites W2035610689 @default.
- W2802074450 cites W2040266098 @default.
- W2802074450 cites W2041961436 @default.
- W2802074450 cites W2042721673 @default.
- W2802074450 cites W2043418681 @default.
- W2802074450 cites W2053004010 @default.
- W2802074450 cites W2057406397 @default.
- W2802074450 cites W2071750376 @default.
- W2802074450 cites W2087713882 @default.
- W2802074450 cites W2092597489 @default.
- W2802074450 cites W2094930911 @default.
- W2802074450 cites W2097157852 @default.
- W2802074450 cites W2128412801 @default.
- W2802074450 cites W2142042712 @default.
- W2802074450 cites W2190415160 @default.
- W2802074450 cites W2400680652 @default.
- W2802074450 cites W2475067848 @default.
- W2802074450 cites W2510930909 @default.
- W2802074450 cites W2568740657 @default.
- W2802074450 cites W2621424966 @default.
- W2802074450 cites W2736317587 @default.
- W2802074450 cites W2743084535 @default.
- W2802074450 cites W2758988044 @default.
- W2802074450 cites W2763495419 @default.
- W2802074450 doi "https://doi.org/10.1016/j.msea.2018.04.083" @default.
- W2802074450 hasPublicationYear "2018" @default.
- W2802074450 type Work @default.
- W2802074450 sameAs 2802074450 @default.
- W2802074450 citedByCount "9" @default.
- W2802074450 countsByYear W28020744502018 @default.
- W2802074450 countsByYear W28020744502019 @default.
- W2802074450 countsByYear W28020744502021 @default.
- W2802074450 countsByYear W28020744502022 @default.
- W2802074450 countsByYear W28020744502023 @default.
- W2802074450 crossrefType "journal-article" @default.
- W2802074450 hasAuthorship W2802074450A5038657036 @default.
- W2802074450 hasAuthorship W2802074450A5056994271 @default.
- W2802074450 hasAuthorship W2802074450A5068130877 @default.
- W2802074450 hasAuthorship W2802074450A5075233046 @default.
- W2802074450 hasAuthorship W2802074450A5081728670 @default.
- W2802074450 hasConcept C112950240 @default.
- W2802074450 hasConcept C127413603 @default.
- W2802074450 hasConcept C149912024 @default.
- W2802074450 hasConcept C159985019 @default.
- W2802074450 hasConcept C184102282 @default.
- W2802074450 hasConcept C186068551 @default.
- W2802074450 hasConcept C18747287 @default.
- W2802074450 hasConcept C191897082 @default.
- W2802074450 hasConcept C192562407 @default.
- W2802074450 hasConcept C2777820655 @default.
- W2802074450 hasConcept C2779930716 @default.
- W2802074450 hasConcept C2781194970 @default.
- W2802074450 hasConcept C59085676 @default.
- W2802074450 hasConcept C66938386 @default.
- W2802074450 hasConcept C69809600 @default.
- W2802074450 hasConcept C75512024 @default.
- W2802074450 hasConcept C87976508 @default.
- W2802074450 hasConceptScore W2802074450C112950240 @default.
- W2802074450 hasConceptScore W2802074450C127413603 @default.
- W2802074450 hasConceptScore W2802074450C149912024 @default.
- W2802074450 hasConceptScore W2802074450C159985019 @default.