- W2802206076 abstract "A study has been made of the hydrogen absorbed by a high-strength steel during cathodic polarization in near-neutral solutions using rigidly controlled experimental conditions. Direct hydrogen analysis by the vacuum heating technique has been utilized and it has been established that use of high extraction temperatures (i.e. > 300°C) can lead to errors which are probably associated with a reaction between adsorbed water and the steel. Extraction at 200°C has been found to give satisfactory results free from this error. The linear relationship between hydrogen absorption and time observed during the early stages of polarization in solutions above pH 4.0 was considered to be characteristic of a rate-controlled slow discharge mechanism of hydrogen evolution. The relationship between hydrogen absorption and overvoltage has been studied in the range pH 4 - 10; the results were found to conform with those anticipated from the kinetics of hydrogen evolution. Metallurgical structure was found to exert a strong influence on the ability of the steel to absorb hydrogen, and a modification of previous theories on delayed failure due to hydrogen has been proposed on the basis of the present study. The influence of arsenic additions to the solution on hydrogen absorption during cathodic polarization have been studied. It has been found that there is a region of pH and overvoltage where hydrogen uptake is inhibited and these results have been correlated with sustained load experiments. The results of this study have been utilized in an attempt to establish whether delayed failure may result from galvanic action produced by discontinuous coatings of electronegative metals (Cd and Zn) on high-tensile steels." @default.
- W2802206076 created "2018-05-17" @default.
- W2802206076 creator A5061252354 @default.
- W2802206076 date "1964-01-01" @default.
- W2802206076 modified "2023-09-26" @default.
- W2802206076 title "The absorption of hydrogen by high tensile steels during cathodic polarization in aqueous solutions." @default.
- W2802206076 hasPublicationYear "1964" @default.
- W2802206076 type Work @default.
- W2802206076 sameAs 2802206076 @default.
- W2802206076 citedByCount "0" @default.
- W2802206076 crossrefType "dissertation" @default.
- W2802206076 hasAuthorship W2802206076A5061252354 @default.
- W2802206076 hasConcept C113196181 @default.
- W2802206076 hasConcept C147789679 @default.
- W2802206076 hasConcept C150394285 @default.
- W2802206076 hasConcept C17525397 @default.
- W2802206076 hasConcept C178790620 @default.
- W2802206076 hasConcept C179104552 @default.
- W2802206076 hasConcept C184651966 @default.
- W2802206076 hasConcept C185592680 @default.
- W2802206076 hasConcept C191897082 @default.
- W2802206076 hasConcept C192562407 @default.
- W2802206076 hasConcept C205049153 @default.
- W2802206076 hasConcept C205871581 @default.
- W2802206076 hasConcept C43617362 @default.
- W2802206076 hasConcept C512968161 @default.
- W2802206076 hasConcept C52859227 @default.
- W2802206076 hasConceptScore W2802206076C113196181 @default.
- W2802206076 hasConceptScore W2802206076C147789679 @default.
- W2802206076 hasConceptScore W2802206076C150394285 @default.
- W2802206076 hasConceptScore W2802206076C17525397 @default.
- W2802206076 hasConceptScore W2802206076C178790620 @default.
- W2802206076 hasConceptScore W2802206076C179104552 @default.
- W2802206076 hasConceptScore W2802206076C184651966 @default.
- W2802206076 hasConceptScore W2802206076C185592680 @default.
- W2802206076 hasConceptScore W2802206076C191897082 @default.
- W2802206076 hasConceptScore W2802206076C192562407 @default.
- W2802206076 hasConceptScore W2802206076C205049153 @default.
- W2802206076 hasConceptScore W2802206076C205871581 @default.
- W2802206076 hasConceptScore W2802206076C43617362 @default.
- W2802206076 hasConceptScore W2802206076C512968161 @default.
- W2802206076 hasConceptScore W2802206076C52859227 @default.
- W2802206076 hasLocation W28022060761 @default.
- W2802206076 hasOpenAccess W2802206076 @default.
- W2802206076 hasPrimaryLocation W28022060761 @default.
- W2802206076 hasRelatedWork W195267851 @default.
- W2802206076 hasRelatedWork W1977954615 @default.
- W2802206076 hasRelatedWork W1986914671 @default.
- W2802206076 hasRelatedWork W2008299858 @default.
- W2802206076 hasRelatedWork W2043681489 @default.
- W2802206076 hasRelatedWork W2058058558 @default.
- W2802206076 hasRelatedWork W2070109962 @default.
- W2802206076 hasRelatedWork W2094978531 @default.
- W2802206076 hasRelatedWork W2185310095 @default.
- W2802206076 hasRelatedWork W2613405646 @default.
- W2802206076 hasRelatedWork W2751539758 @default.
- W2802206076 hasRelatedWork W2767537070 @default.
- W2802206076 hasRelatedWork W2903807604 @default.
- W2802206076 hasRelatedWork W2952876355 @default.
- W2802206076 hasRelatedWork W2998157356 @default.
- W2802206076 hasRelatedWork W3036858026 @default.
- W2802206076 hasRelatedWork W3147224632 @default.
- W2802206076 hasRelatedWork W3151813385 @default.
- W2802206076 hasRelatedWork W7902989 @default.
- W2802206076 hasRelatedWork W923735050 @default.
- W2802206076 isParatext "false" @default.
- W2802206076 isRetracted "false" @default.
- W2802206076 magId "2802206076" @default.
- W2802206076 workType "dissertation" @default.