- W2802992442 abstract "In this paper, phase transitions and microstructure evolution in titanium Ti-6Al-4V alloy parts produced by electron beam melting (EBM) under hydrogenation was investigated. Hydrogenation was carried out at the temperature of 650 °C to the absolute hydrogen concentrations in the samples of 0.29, 0.58, and 0.90 wt. %. Comparative analysis of microstructure changes in Ti-6Al-4V alloy parts was performed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). Furthermore, in-situ XRD was used to investigate the phase transitions in the samples during hydrogenation. The structure of Ti-6Al-4V parts produced by EBM is represented by the α phase plates with the transverse length of 0.2 μm, the β phase both in the form of plates and globular grains, and metastable α″ and ω phases. Hydrogenation to the concentration of 0.29 wt. % leads to the formation of intermetallic Ti3Al phase. The dimensions of intermetallic Ti3Al plates and their volume fraction increase significantly with hydrogen concentration up to 0.58 wt. % along with precipitation of nano-sized crystals of titanium δ hydrides. Individual Ti3Al plates decay into nanocrystals with increasing hydrogen concentration up to 0.9 wt. % accompanied by the increase of proportion and size of hydride plates. Hardness of EBM Ti-6Al-4V alloy decreases with hydrogen content." @default.
- W2802992442 created "2018-05-17" @default.
- W2802992442 creator A5023978109 @default.
- W2802992442 creator A5024596976 @default.
- W2802992442 creator A5027915908 @default.
- W2802992442 creator A5041010892 @default.
- W2802992442 creator A5047201301 @default.
- W2802992442 creator A5056877271 @default.
- W2802992442 creator A5066527098 @default.
- W2802992442 creator A5069142813 @default.
- W2802992442 creator A5088214651 @default.
- W2802992442 date "2018-04-26" @default.
- W2802992442 modified "2023-10-18" @default.
- W2802992442 title "Hydrogen-Induced Phase Transformation and Microstructure Evolution for Ti-6Al-4V Parts Produced by Electron Beam Melting" @default.
- W2802992442 cites W115330213 @default.
- W2802992442 cites W1606437612 @default.
- W2802992442 cites W1966904572 @default.
- W2802992442 cites W1975467670 @default.
- W2802992442 cites W1978616107 @default.
- W2802992442 cites W1984620721 @default.
- W2802992442 cites W1985998804 @default.
- W2802992442 cites W1994803044 @default.
- W2802992442 cites W2001586289 @default.
- W2802992442 cites W2011106345 @default.
- W2802992442 cites W2016504762 @default.
- W2802992442 cites W2019287063 @default.
- W2802992442 cites W2021009371 @default.
- W2802992442 cites W2023381719 @default.
- W2802992442 cites W2024051017 @default.
- W2802992442 cites W2025865162 @default.
- W2802992442 cites W2033323010 @default.
- W2802992442 cites W2036486347 @default.
- W2802992442 cites W2042601644 @default.
- W2802992442 cites W2043561770 @default.
- W2802992442 cites W2050869396 @default.
- W2802992442 cites W2055148452 @default.
- W2802992442 cites W2061027358 @default.
- W2802992442 cites W2062434465 @default.
- W2802992442 cites W2068309205 @default.
- W2802992442 cites W2074402847 @default.
- W2802992442 cites W2080508008 @default.
- W2802992442 cites W2082888867 @default.
- W2802992442 cites W2084492973 @default.
- W2802992442 cites W2086058904 @default.
- W2802992442 cites W2095253380 @default.
- W2802992442 cites W2126626261 @default.
- W2802992442 cites W2148849016 @default.
- W2802992442 cites W2321894092 @default.
- W2802992442 cites W2430006432 @default.
- W2802992442 cites W2557717068 @default.
- W2802992442 cites W2561187213 @default.
- W2802992442 cites W2565608234 @default.
- W2802992442 cites W2566285183 @default.
- W2802992442 cites W2578495235 @default.
- W2802992442 cites W2616801167 @default.
- W2802992442 cites W2621308248 @default.
- W2802992442 cites W2622394107 @default.
- W2802992442 cites W2760017239 @default.
- W2802992442 cites W4243219699 @default.
- W2802992442 cites W828403382 @default.
- W2802992442 doi "https://doi.org/10.3390/met8050301" @default.
- W2802992442 hasPublicationYear "2018" @default.
- W2802992442 type Work @default.
- W2802992442 sameAs 2802992442 @default.
- W2802992442 citedByCount "38" @default.
- W2802992442 countsByYear W28029924422019 @default.
- W2802992442 countsByYear W28029924422020 @default.
- W2802992442 countsByYear W28029924422021 @default.
- W2802992442 countsByYear W28029924422022 @default.
- W2802992442 countsByYear W28029924422023 @default.
- W2802992442 crossrefType "journal-article" @default.
- W2802992442 hasAuthorship W2802992442A5023978109 @default.
- W2802992442 hasAuthorship W2802992442A5024596976 @default.
- W2802992442 hasAuthorship W2802992442A5027915908 @default.
- W2802992442 hasAuthorship W2802992442A5041010892 @default.
- W2802992442 hasAuthorship W2802992442A5047201301 @default.
- W2802992442 hasAuthorship W2802992442A5056877271 @default.
- W2802992442 hasAuthorship W2802992442A5066527098 @default.
- W2802992442 hasAuthorship W2802992442A5069142813 @default.
- W2802992442 hasAuthorship W2802992442A5088214651 @default.
- W2802992442 hasBestOaLocation W28029924421 @default.
- W2802992442 hasConcept C107054158 @default.
- W2802992442 hasConcept C113196181 @default.
- W2802992442 hasConcept C121332964 @default.
- W2802992442 hasConcept C146088050 @default.
- W2802992442 hasConcept C153294291 @default.
- W2802992442 hasConcept C159985019 @default.
- W2802992442 hasConcept C171250308 @default.
- W2802992442 hasConcept C178790620 @default.
- W2802992442 hasConcept C185592680 @default.
- W2802992442 hasConcept C191897082 @default.
- W2802992442 hasConcept C192562407 @default.
- W2802992442 hasConcept C26771246 @default.
- W2802992442 hasConcept C27501479 @default.
- W2802992442 hasConcept C2777961443 @default.
- W2802992442 hasConcept C2780026712 @default.
- W2802992442 hasConcept C43617362 @default.
- W2802992442 hasConcept C44280652 @default.