- W2804768669 abstract "The effects of Sr addition on microstructure and mechanical properties of ADC12/nano Al2O3 composite has been studied. In this research ADC12 as a matrix was added by 0.3 vf% nano Al2O3 as a reinforcement and Al-5Sr varied from 0.00 wt% to 0.05 wt% to modify the eutectic structure of the matrix. The composites were further characterized both microstructural analysis and mechanical properties. The results showed that the intermetallic phases including β-Al5FeSi and Al2Cu were detected using scanning electron microscope and α-Al(Mn,Fe)Si or α-cubic phases was possible to form due to high content of Mn in the composites. The Mg2Si primary, binary, and ternary phases were detected in this composites by metallographic examination. Then, MgAl2O4 (spinnel) were found by XRD analysis. The higher of Sr content from 0,00 to 0.02 the lower SDAS formation from 15 µm to 14 µm as well as porosity content reduced from 4% to 3%. The ultimate tensile strength increased from 115 MPa to 137 MPa as well as in impact toughness from 0.016 J/mm2 to 0.025 J/mm2. The highest hardness and the lowest wear rate were obtained with the addition of 0.05 wt% Sr with 46 HRB and 1.04 10−5 mm3/m respectively due to the changed of chinese script became refined fibrous type." @default.
- W2804768669 created "2018-06-01" @default.
- W2804768669 creator A5006022357 @default.
- W2804768669 creator A5028273433 @default.
- W2804768669 creator A5057983087 @default.
- W2804768669 creator A5075898337 @default.
- W2804768669 date "2018-01-01" @default.
- W2804768669 modified "2023-10-16" @default.
- W2804768669 title "Effect of Sr addition on the microstructure and mechanical properties of ADC12/nano Al2O3 composites produced by stir casting method" @default.
- W2804768669 cites W1967279700 @default.
- W2804768669 cites W1972032878 @default.
- W2804768669 cites W1978671862 @default.
- W2804768669 cites W1984740052 @default.
- W2804768669 cites W1989804521 @default.
- W2804768669 cites W1997323407 @default.
- W2804768669 cites W1999060118 @default.
- W2804768669 cites W2042254447 @default.
- W2804768669 cites W2046642581 @default.
- W2804768669 cites W2051980727 @default.
- W2804768669 cites W2076530905 @default.
- W2804768669 cites W2091732911 @default.
- W2804768669 cites W2093925699 @default.
- W2804768669 cites W2283302239 @default.
- W2804768669 cites W4210963906 @default.
- W2804768669 cites W4248926426 @default.
- W2804768669 doi "https://doi.org/10.1063/1.5038297" @default.
- W2804768669 hasPublicationYear "2018" @default.
- W2804768669 type Work @default.
- W2804768669 sameAs 2804768669 @default.
- W2804768669 citedByCount "1" @default.
- W2804768669 countsByYear W28047686692020 @default.
- W2804768669 crossrefType "proceedings-article" @default.
- W2804768669 hasAuthorship W2804768669A5006022357 @default.
- W2804768669 hasAuthorship W2804768669A5028273433 @default.
- W2804768669 hasAuthorship W2804768669A5057983087 @default.
- W2804768669 hasAuthorship W2804768669A5075898337 @default.
- W2804768669 hasBestOaLocation W28047686691 @default.
- W2804768669 hasConcept C104779481 @default.
- W2804768669 hasConcept C112950240 @default.
- W2804768669 hasConcept C159985019 @default.
- W2804768669 hasConcept C16635281 @default.
- W2804768669 hasConcept C18168003 @default.
- W2804768669 hasConcept C191897082 @default.
- W2804768669 hasConcept C192562407 @default.
- W2804768669 hasConcept C26771246 @default.
- W2804768669 hasConcept C27501479 @default.
- W2804768669 hasConcept C2780026712 @default.
- W2804768669 hasConcept C6648577 @default.
- W2804768669 hasConcept C87976508 @default.
- W2804768669 hasConcept C99595764 @default.
- W2804768669 hasConceptScore W2804768669C104779481 @default.
- W2804768669 hasConceptScore W2804768669C112950240 @default.
- W2804768669 hasConceptScore W2804768669C159985019 @default.
- W2804768669 hasConceptScore W2804768669C16635281 @default.
- W2804768669 hasConceptScore W2804768669C18168003 @default.
- W2804768669 hasConceptScore W2804768669C191897082 @default.
- W2804768669 hasConceptScore W2804768669C192562407 @default.
- W2804768669 hasConceptScore W2804768669C26771246 @default.
- W2804768669 hasConceptScore W2804768669C27501479 @default.
- W2804768669 hasConceptScore W2804768669C2780026712 @default.
- W2804768669 hasConceptScore W2804768669C6648577 @default.
- W2804768669 hasConceptScore W2804768669C87976508 @default.
- W2804768669 hasConceptScore W2804768669C99595764 @default.
- W2804768669 hasLocation W28047686691 @default.
- W2804768669 hasOpenAccess W2804768669 @default.
- W2804768669 hasPrimaryLocation W28047686691 @default.
- W2804768669 hasRelatedWork W1987487801 @default.
- W2804768669 hasRelatedWork W2054718878 @default.
- W2804768669 hasRelatedWork W2057024573 @default.
- W2804768669 hasRelatedWork W2089251307 @default.
- W2804768669 hasRelatedWork W2362720846 @default.
- W2804768669 hasRelatedWork W2373097621 @default.
- W2804768669 hasRelatedWork W2528998499 @default.
- W2804768669 hasRelatedWork W2766515653 @default.
- W2804768669 hasRelatedWork W4210374666 @default.
- W2804768669 hasRelatedWork W4214530935 @default.
- W2804768669 isParatext "false" @default.
- W2804768669 isRetracted "false" @default.
- W2804768669 magId "2804768669" @default.
- W2804768669 workType "article" @default.