- W2808576538 abstract "Recent work has highlighted unusual effects of vanadium when used in conjunction with other microalloying additions on the hardenability of steels. Positive and negative synergistic effects have been observed, but studies into the mechanisms have been limited. To investigate the effects, vanadium interactions with aluminium, molybdenum, niobium and titanium were studied in low (0.1%) and medium (0.4%) carbon steels, containing normal (0.008%) and enhanced (0.020%) nitrogen. Utilising standard jominy test conditions of 950°C for one hour resulted in classical hardenability responses being obtained, where increasing quantities of microalloying additions in solution increase the hardenability.However, when the jominy test conditions were varied unexpected effects were observed. Extending the austenitising time to eight hours showed that the hardenability was dependent upon kinetic effects such as the rate of solution of the alloy carbides/nitrides and the rate at which the microalloying elements in solution segregated to the austenite grain boundaries. It was also observed that if the austenitising temperature was increased to 1200°C a decrease in hardenability could be obtained by increasing the quantity of vanadium, niobium or titanium. These effects were attributed to a combination of thermal dispersion of microalloying clusters from the austenite grain boundaries, preferrential transformation on large alloy carbides/nitrides and migration of the austenite grain boundaries. Therefore it was considered inadequate to explain hardenablity solely in terms of the carbon concentration, austenite grain size and amount of other alloying elements present. Additional factors such as cluster formation, grain boundary pinning etc., were identified and applied to the results to successfully explain the effects of the alloy interactions on hardenability.Recent studies on vanadium alloyed pearlitic steels showed significant increases in strength could be obtained by precipitation within the pearlitic ferrite. Mechanical property investigations of two steels indicated that a maximum precipitation effect was obtained at an isothermal transformation temperature of 600°C." @default.
- W2808576538 created "2018-06-21" @default.
- W2808576538 creator A5008991855 @default.
- W2808576538 date "1988-01-01" @default.
- W2808576538 modified "2023-09-27" @default.
- W2808576538 title "Hardenability, transformation and precipitation effects in vanadium steels." @default.
- W2808576538 hasPublicationYear "1988" @default.
- W2808576538 type Work @default.
- W2808576538 sameAs 2808576538 @default.
- W2808576538 citedByCount "0" @default.
- W2808576538 crossrefType "dissertation" @default.
- W2808576538 hasAuthorship W2808576538A5008991855 @default.
- W2808576538 hasConcept C107054158 @default.
- W2808576538 hasConcept C121332964 @default.
- W2808576538 hasConcept C153294291 @default.
- W2808576538 hasConcept C191897082 @default.
- W2808576538 hasConcept C192562407 @default.
- W2808576538 hasConcept C195678695 @default.
- W2808576538 hasConcept C2778547858 @default.
- W2808576538 hasConcept C2780026712 @default.
- W2808576538 hasConcept C47908070 @default.
- W2808576538 hasConcept C504678139 @default.
- W2808576538 hasConcept C506065880 @default.
- W2808576538 hasConcept C507968137 @default.
- W2808576538 hasConcept C5335593 @default.
- W2808576538 hasConcept C87976508 @default.
- W2808576538 hasConcept C96288455 @default.
- W2808576538 hasConceptScore W2808576538C107054158 @default.
- W2808576538 hasConceptScore W2808576538C121332964 @default.
- W2808576538 hasConceptScore W2808576538C153294291 @default.
- W2808576538 hasConceptScore W2808576538C191897082 @default.
- W2808576538 hasConceptScore W2808576538C192562407 @default.
- W2808576538 hasConceptScore W2808576538C195678695 @default.
- W2808576538 hasConceptScore W2808576538C2778547858 @default.
- W2808576538 hasConceptScore W2808576538C2780026712 @default.
- W2808576538 hasConceptScore W2808576538C47908070 @default.
- W2808576538 hasConceptScore W2808576538C504678139 @default.
- W2808576538 hasConceptScore W2808576538C506065880 @default.
- W2808576538 hasConceptScore W2808576538C507968137 @default.
- W2808576538 hasConceptScore W2808576538C5335593 @default.
- W2808576538 hasConceptScore W2808576538C87976508 @default.
- W2808576538 hasConceptScore W2808576538C96288455 @default.
- W2808576538 hasLocation W28085765381 @default.
- W2808576538 hasOpenAccess W2808576538 @default.
- W2808576538 hasPrimaryLocation W28085765381 @default.
- W2808576538 hasRelatedWork W141615173 @default.
- W2808576538 hasRelatedWork W1968622631 @default.
- W2808576538 hasRelatedWork W1973205113 @default.
- W2808576538 hasRelatedWork W2007443886 @default.
- W2808576538 hasRelatedWork W2007733101 @default.
- W2808576538 hasRelatedWork W2011778230 @default.
- W2808576538 hasRelatedWork W2026992217 @default.
- W2808576538 hasRelatedWork W2043556191 @default.
- W2808576538 hasRelatedWork W2065126789 @default.
- W2808576538 hasRelatedWork W2154758950 @default.
- W2808576538 hasRelatedWork W2334612011 @default.
- W2808576538 hasRelatedWork W2335468928 @default.
- W2808576538 hasRelatedWork W2714675758 @default.
- W2808576538 hasRelatedWork W2808118074 @default.
- W2808576538 hasRelatedWork W2902629452 @default.
- W2808576538 hasRelatedWork W2917555743 @default.
- W2808576538 hasRelatedWork W3133663470 @default.
- W2808576538 hasRelatedWork W3145316553 @default.
- W2808576538 hasRelatedWork W93989200 @default.
- W2808576538 hasRelatedWork W3140929814 @default.
- W2808576538 isParatext "false" @default.
- W2808576538 isRetracted "false" @default.
- W2808576538 magId "2808576538" @default.
- W2808576538 workType "dissertation" @default.