• W2808889085 abstract "Microstructure and mechanical properties of extruded Mg–6Zn–xY–0.5Ce–0.4Zr sheets were systematically investigated. Mg–Zn–Ce, I-phase (Mg3Zn6Y) and W-phase (Mg3Zn3Y2) with different morphologies were observed in as-cast and extruded conditions. Numerous nano-precipitates were found along grain boundaries and inside grains in both dynamically recrystallized (DRXed) and unDRXed regions after hot extrusion. The area fraction of DRXed regions increases with Y additions mainly due to particle stimulated nucleation (PSN). An extruded fiber texture was observed after hot extrusion. The texture is strengthened firstly and then weakened. The extruded alloys with 0.5–1 wt% Y and 0.5 wt% Ce exhibit much better mechanical properties compared with other Mg alloys such as Mg–5Zn–1Y–1Zr (wt.%) and Mg–6Zn–1Ce–0.5Zr (wt.%) alloys under the same extrusion ratio. The extruded alloy with 0.2 wt% Y and 0.5 wt% Ce has the yield strength of 322 MPa, ultimate tensile strength of 378 MPa and elongation of 8.6%, which is the highest value among the studied alloys. Grain boundary strengthening and precipitation strengthening are the two most important factors for improving yield strength of Mg–6Zn–xY–0.5Ce–0.4Zr alloys. The addition of Y is an effective way in significantly improving the mechanical properties of Mg–6Zn–xY–0.5Ce–0.4Zr alloys." @default.
• W2808889085 created "2018-06-29" @default.
• W2808889085 creator A5014051457 @default.
• W2808889085 creator A5017512846 @default.
• W2808889085 creator A5035811517 @default.
• W2808889085 creator A5058647130 @default.
• W2808889085 creator A5059834892 @default.
• W2808889085 creator A5060014296 @default.
• W2808889085 creator A5081070909 @default.
• W2808889085 date "2018-09-01" @default.
• W2808889085 modified "2023-10-17" @default.
• W2808889085 title "The effect of Y addition on recrystallization and mechanical properties of Mg–6Zn–xY–0.5Ce–0.4Zr alloys" @default.
• W2808889085 cites W1938553421 @default.
• W2808889085 cites W1968163182 @default.
• W2808889085 cites W1988039863 @default.
• W2808889085 cites W1990798956 @default.
• W2808889085 cites W1993376572 @default.
• W2808889085 cites W2000457392 @default.
• W2808889085 cites W2003587592 @default.
• W2808889085 cites W2029152841 @default.
• W2808889085 cites W2043241036 @default.
• W2808889085 cites W2045466533 @default.
• W2808889085 cites W2048213271 @default.
• W2808889085 cites W2048588156 @default.
• W2808889085 cites W2053300417 @default.
• W2808889085 cites W2060157621 @default.
• W2808889085 cites W2144094673 @default.
• W2808889085 cites W2247455966 @default.
• W2808889085 cites W2288253576 @default.
• W2808889085 cites W2399973193 @default.
• W2808889085 cites W2465760293 @default.
• W2808889085 cites W2472085884 @default.
• W2808889085 cites W2495995036 @default.
• W2808889085 cites W2497704593 @default.
• W2808889085 cites W2512300812 @default.
• W2808889085 cites W2555743597 @default.
• W2808889085 cites W2563955856 @default.
• W2808889085 cites W2589648753 @default.
• W2808889085 cites W2604824910 @default.
• W2808889085 cites W2615480434 @default.
• W2808889085 cites W2743280656 @default.
• W2808889085 cites W2749644330 @default.
• W2808889085 cites W2759027428 @default.
• W2808889085 cites W2774676965 @default.
• W2808889085 cites W2794112419 @default.
• W2808889085 cites W2794153752 @default.
• W2808889085 cites W862386976 @default.
• W2808889085 cites W984856741 @default.
• W2808889085 doi "https://doi.org/10.1016/j.vacuum.2018.06.048" @default.
• W2808889085 hasPublicationYear "2018" @default.
• W2808889085 type Work @default.
• W2808889085 sameAs 2808889085 @default.
• W2808889085 citedByCount "39" @default.
• W2808889085 countsByYear W28088890852018 @default.
• W2808889085 countsByYear W28088890852019 @default.
• W2808889085 countsByYear W28088890852020 @default.
• W2808889085 countsByYear W28088890852021 @default.
• W2808889085 countsByYear W28088890852022 @default.
• W2808889085 countsByYear W28088890852023 @default.
• W2808889085 crossrefType "journal-article" @default.
• W2808889085 hasAuthorship W2808889085A5014051457 @default.
• W2808889085 hasAuthorship W2808889085A5017512846 @default.
• W2808889085 hasAuthorship W2808889085A5035811517 @default.
• W2808889085 hasAuthorship W2808889085A5058647130 @default.
• W2808889085 hasAuthorship W2808889085A5059834892 @default.
• W2808889085 hasAuthorship W2808889085A5060014296 @default.
• W2808889085 hasAuthorship W2808889085A5081070909 @default.
• W2808889085 hasConcept C107054158 @default.
• W2808889085 hasConcept C112950240 @default.
• W2808889085 hasConcept C121332964 @default.
• W2808889085 hasConcept C151730666 @default.
• W2808889085 hasConcept C153294291 @default.
• W2808889085 hasConcept C154634170 @default.
• W2808889085 hasConcept C159985019 @default.
• W2808889085 hasConcept C169010117 @default.
• W2808889085 hasConcept C172658604 @default.
• W2808889085 hasConcept C178790620 @default.
• W2808889085 hasConcept C185592680 @default.
• W2808889085 hasConcept C191897082 @default.
• W2808889085 hasConcept C192191005 @default.
• W2808889085 hasConcept C192562407 @default.
• W2808889085 hasConcept C195702682 @default.
• W2808889085 hasConcept C2778958987 @default.
• W2808889085 hasConcept C2780026712 @default.
• W2808889085 hasConcept C33947775 @default.
• W2808889085 hasConcept C44280652 @default.
• W2808889085 hasConcept C47908070 @default.
• W2808889085 hasConcept C61048295 @default.
• W2808889085 hasConcept C86803240 @default.
• W2808889085 hasConcept C87976508 @default.
• W2808889085 hasConcept C97355855 @default.
• W2808889085 hasConceptScore W2808889085C107054158 @default.
• W2808889085 hasConceptScore W2808889085C112950240 @default.
• W2808889085 hasConceptScore W2808889085C121332964 @default.
• W2808889085 hasConceptScore W2808889085C151730666 @default.
• W2808889085 hasConceptScore W2808889085C153294291 @default.
• W2808889085 hasConceptScore W2808889085C154634170 @default.
• W2808889085 hasConceptScore W2808889085C159985019 @default.

• next