• W2811389417 abstract "F82H reduced activation steel coated with vacuum plasma sprayed (VPS) tungsten is a candidate as a plasma facing material for main chamber components in future fusion reactors. Due to different coefficients of thermal expansion (CTE), significant thermal stresses are expected in these bimetallic materials. Thus, a major uncertainty in the performance of W/F82H components during the operation under high-heat fluxes is the effect of CTE mismatch. In this study, a high intensity plasma-arc lamp was used for high-heat flux cycling tests of W/F82H specimens. While no surface damage was observed for specimens tested for 100–200 cycles at a heat flux of 1.4 MW/m2 pulse when the backside surface temperature was maintained below 550 °C, significant cracking occurred at higher temperatures. A simple analytical model for bimetallic materials indicated that the stress in the VPS-W layer is likely to exceed its failure stress solely due to the bilayer thermal stress. A finite element analysis of the state of stress and deformation confirmed that a significant stress also would occur at the W surface due to the rigid-body like constraint imposed by the clamp, which can be the main cause of the cracking." @default.
• W2811389417 created "2018-07-10" @default.
• W2811389417 creator A5003495513 @default.
• W2811389417 creator A5023594840 @default.
• W2811389417 creator A5041445357 @default.
• W2811389417 creator A5053874039 @default.
• W2811389417 creator A5064672494 @default.
• W2811389417 creator A5072673584 @default.
• W2811389417 creator A5074761937 @default.
• W2811389417 creator A5087743456 @default.
• W2811389417 date "2018-08-01" @default.
• W2811389417 modified "2023-10-06" @default.
• W2811389417 title "Surface morphology of Tungsten-F82H after high-heat flux testing using plasma-arc lamps" @default.
• W2811389417 cites W1977813353 @default.
• W2811389417 cites W1988412885 @default.
• W2811389417 cites W1990496614 @default.
• W2811389417 cites W2015497179 @default.
• W2811389417 cites W2021902937 @default.
• W2811389417 cites W2035237169 @default.
• W2811389417 cites W2039086453 @default.
• W2811389417 cites W2040237314 @default.
• W2811389417 cites W2050536470 @default.
• W2811389417 cites W2065334197 @default.
• W2811389417 cites W2071716205 @default.
• W2811389417 cites W2077476311 @default.
• W2811389417 cites W2086475328 @default.
• W2811389417 cites W2086898733 @default.
• W2811389417 cites W2089104851 @default.
• W2811389417 cites W2591068548 @default.
• W2811389417 cites W412378384 @default.
• W2811389417 cites W78933142 @default.
• W2811389417 doi "https://doi.org/10.1016/j.nme.2018.06.015" @default.
• W2811389417 hasPublicationYear "2018" @default.
• W2811389417 type Work @default.
• W2811389417 sameAs 2811389417 @default.
• W2811389417 citedByCount "3" @default.
• W2811389417 countsByYear W28113894172019 @default.
• W2811389417 countsByYear W28113894172021 @default.
• W2811389417 countsByYear W28113894172023 @default.
• W2811389417 crossrefType "journal-article" @default.
• W2811389417 hasAuthorship W2811389417A5003495513 @default.
• W2811389417 hasAuthorship W2811389417A5023594840 @default.
• W2811389417 hasAuthorship W2811389417A5041445357 @default.
• W2811389417 hasAuthorship W2811389417A5053874039 @default.
• W2811389417 hasAuthorship W2811389417A5064672494 @default.
• W2811389417 hasAuthorship W2811389417A5072673584 @default.
• W2811389417 hasAuthorship W2811389417A5074761937 @default.
• W2811389417 hasAuthorship W2811389417A5087743456 @default.
• W2811389417 hasBestOaLocation W28113894171 @default.
• W2811389417 hasConcept C121332964 @default.
• W2811389417 hasConcept C138885662 @default.
• W2811389417 hasConcept C159188206 @default.
• W2811389417 hasConcept C159985019 @default.
• W2811389417 hasConcept C191897082 @default.
• W2811389417 hasConcept C192562407 @default.
• W2811389417 hasConcept C204366326 @default.
• W2811389417 hasConcept C21036866 @default.
• W2811389417 hasConcept C41895202 @default.
• W2811389417 hasConcept C43411465 @default.
• W2811389417 hasConcept C50517652 @default.
• W2811389417 hasConcept C542268612 @default.
• W2811389417 hasConcept C544153396 @default.
• W2811389417 hasConcept C57879066 @default.
• W2811389417 hasConcept C58396970 @default.
• W2811389417 hasConcept C62520636 @default.
• W2811389417 hasConcept C82706917 @default.
• W2811389417 hasConceptScore W2811389417C121332964 @default.
• W2811389417 hasConceptScore W2811389417C138885662 @default.
• W2811389417 hasConceptScore W2811389417C159188206 @default.
• W2811389417 hasConceptScore W2811389417C159985019 @default.
• W2811389417 hasConceptScore W2811389417C191897082 @default.
• W2811389417 hasConceptScore W2811389417C192562407 @default.
• W2811389417 hasConceptScore W2811389417C204366326 @default.
• W2811389417 hasConceptScore W2811389417C21036866 @default.
• W2811389417 hasConceptScore W2811389417C41895202 @default.
• W2811389417 hasConceptScore W2811389417C43411465 @default.
• W2811389417 hasConceptScore W2811389417C50517652 @default.
• W2811389417 hasConceptScore W2811389417C542268612 @default.
• W2811389417 hasConceptScore W2811389417C544153396 @default.
• W2811389417 hasConceptScore W2811389417C57879066 @default.
• W2811389417 hasConceptScore W2811389417C58396970 @default.
• W2811389417 hasConceptScore W2811389417C62520636 @default.
• W2811389417 hasConceptScore W2811389417C82706917 @default.
• W2811389417 hasFunder F4320306084 @default.
• W2811389417 hasLocation W28113894171 @default.
• W2811389417 hasLocation W28113894172 @default.
• W2811389417 hasLocation W28113894173 @default.
• W2811389417 hasOpenAccess W2811389417 @default.
• W2811389417 hasPrimaryLocation W28113894171 @default.
• W2811389417 hasRelatedWork W2061536903 @default.
• W2811389417 hasRelatedWork W2112842299 @default.
• W2811389417 hasRelatedWork W2268765215 @default.
• W2811389417 hasRelatedWork W2316719495 @default.
• W2811389417 hasRelatedWork W2494879891 @default.
• W2811389417 hasRelatedWork W2883395230 @default.
• W2811389417 hasRelatedWork W2949741386 @default.
• W2811389417 hasRelatedWork W3032796188 @default.
• W2811389417 hasRelatedWork W4361001398 @default.

• next