- W2811480799 abstract "The emergence of a new class of cellular solids, i.e., nano- and micro-architected materials, poses the question of whether they can be characterized as a continuum solid. Extensive research has shown that these ultralight and strong structural metamaterials are particularly attractive for mechanically-demanding applications; yet their susceptibility to flaws, fracture behavior, and discrete-continuum duality remains relatively unexplored. In the course of this work, we report the fabrication and tensile-to-failure response of three-dimensional ceramic nanolattices, comprised of 50nm-thick alumina tubes that are arranged into periodic 5um-wide octet-truss unit cells, with and without pre-fabricated through-thickness center notches oriented at different angles to the loading direction. In-situ uniaxial tensile experiments revealed that for all notch orientations, failure always initiated at the notch root, as would be in a monolithic material, with the tube walls at nodal junctions fracturing first, followed by instantaneous crack propagation through the discrete lattice architecture along nodal planes orthogonal to the loading direction. Measured tensile strength of 27.4 MPa was highest for the unnotched samples and decreased systematically with the increase of notch orientation to its minimum of 7.2 MPa in the orthogonally-notched samples. We found the specific tensile strength of hollow-tube octet alumina nanolattices to be 4 times higher than what has been reported for architected and bulk materials at similar low densities. Three-dimensional finite element simulations closely reproduce the observed failure mechanism and trends in failure strength. A direct comparison is made between the experimental measurements, finite element simulations, and predictions of linear elastic fracture mechanics for a self-similar monolithic tensile samples made out of an ideally-brittle solid. Results are in good agreement with the scaling of failure strengths from classical mode I fracture criteria and suggest that trajectory of crack propagation can be adequately explained by considering the connectivity of the lattice architecture. These findings imply that the continuum nature of nano-architected materials offers predictability of failure stresses, which helps enable the development of advanced materials through informed architectural design." @default.
- W2811480799 created "2018-07-10" @default.
- W2811480799 creator A5080351252 @default.
- W2811480799 creator A5080442140 @default.
- W2811480799 date "2018-01-01" @default.
- W2811480799 modified "2023-09-27" @default.
- W2811480799 title "Tensile Failure and Fracture of Three-Dimensional Brittle Nanolattices" @default.
- W2811480799 doi "https://doi.org/10.7907/azxg-nb17." @default.
- W2811480799 hasPublicationYear "2018" @default.
- W2811480799 type Work @default.
- W2811480799 sameAs 2811480799 @default.
- W2811480799 citedByCount "0" @default.
- W2811480799 crossrefType "dissertation" @default.
- W2811480799 hasAuthorship W2811480799A5080351252 @default.
- W2811480799 hasAuthorship W2811480799A5080442140 @default.
- W2811480799 hasConcept C112950240 @default.
- W2811480799 hasConcept C127413603 @default.
- W2811480799 hasConcept C134132462 @default.
- W2811480799 hasConcept C136478896 @default.
- W2811480799 hasConcept C159985019 @default.
- W2811480799 hasConcept C173534245 @default.
- W2811480799 hasConcept C192562407 @default.
- W2811480799 hasConcept C59085676 @default.
- W2811480799 hasConcept C66938386 @default.
- W2811480799 hasConceptScore W2811480799C112950240 @default.
- W2811480799 hasConceptScore W2811480799C127413603 @default.
- W2811480799 hasConceptScore W2811480799C134132462 @default.
- W2811480799 hasConceptScore W2811480799C136478896 @default.
- W2811480799 hasConceptScore W2811480799C159985019 @default.
- W2811480799 hasConceptScore W2811480799C173534245 @default.
- W2811480799 hasConceptScore W2811480799C192562407 @default.
- W2811480799 hasConceptScore W2811480799C59085676 @default.
- W2811480799 hasConceptScore W2811480799C66938386 @default.
- W2811480799 hasLocation W28114807991 @default.
- W2811480799 hasOpenAccess W2811480799 @default.
- W2811480799 hasPrimaryLocation W28114807991 @default.
- W2811480799 hasRelatedWork W1828966660 @default.
- W2811480799 hasRelatedWork W1972068669 @default.
- W2811480799 hasRelatedWork W1996670224 @default.
- W2811480799 hasRelatedWork W1997218740 @default.
- W2811480799 hasRelatedWork W2031010992 @default.
- W2811480799 hasRelatedWork W2068614026 @default.
- W2811480799 hasRelatedWork W2083908160 @default.
- W2811480799 hasRelatedWork W2109216826 @default.
- W2811480799 hasRelatedWork W2790438411 @default.
- W2811480799 hasRelatedWork W2792758624 @default.
- W2811480799 hasRelatedWork W2808849715 @default.
- W2811480799 hasRelatedWork W2904002089 @default.
- W2811480799 hasRelatedWork W2966084771 @default.
- W2811480799 hasRelatedWork W2993755849 @default.
- W2811480799 hasRelatedWork W3048820943 @default.
- W2811480799 hasRelatedWork W3107213189 @default.
- W2811480799 hasRelatedWork W3155054514 @default.
- W2811480799 hasRelatedWork W3203461963 @default.
- W2811480799 hasRelatedWork W83081164 @default.
- W2811480799 hasRelatedWork W3142593678 @default.
- W2811480799 isParatext "false" @default.
- W2811480799 isRetracted "false" @default.
- W2811480799 magId "2811480799" @default.
- W2811480799 workType "dissertation" @default.