- W286991963 abstract "An investigation of the performance of asphalt binders of identical grade but varied chemistries was conducted to determine if binder performance is captured by the Superpave binder specification. The emphasis of this effort was on polymer modification of asphalt binders and their type and mode of incorporation. A single crude was used in the production of nine modified binders that included air blowing, chemical modification (e.g., polymer grafting), and polymer blending. Both plastomeric and elastomeric polymers were evaluated in this study. The materials selected represented a divergent group of modifiers that have been placed in pavements. The initial target grade was a PG 76-28. The modified asphalts came within 1 degree C of the high temperature target and 2 degrees C of the low temperature target. Continuous grading specification values were determined on all the materials in addition to generating rheological mastercurves, and Black Diagrams. The rut resistance of mixes containing these binders was tested using the French Pavement Rut Tester at 70 degrees C and Superpave Shear Tester (SST) at 50 and 70 degrees C. Fatigue testing was conducted using the Four Point Bending Beam Test at 19 degrees C and 500 and 1000 microstrains. Moisture sensitivity of the mixes was evaluated using the Hamburg Wheel Tracking Device at 58 degrees C. The relationships between binder characteristics and mix results were evaluated. The performance of these systems with respect to fatigue and moisture sensitivity is markedly different, whereas the rutting and low temperature cracking tendencies were quite similar. Validation of these results is currently being conducted on pavements incorporating a number of these modified binders at our Accelerated Loading Facility. For the covering abstract see ITRD E121480." @default.
- W286991963 created "2016-06-24" @default.
- W286991963 creator A5005895076 @default.
- W286991963 creator A5051251495 @default.
- W286991963 creator A5081756517 @default.
- W286991963 creator A5084319063 @default.
- W286991963 date "2004-01-01" @default.
- W286991963 modified "2023-09-23" @default.
- W286991963 title "UNDERSTANDING THE PERFORMANCE OF POLYMER MODIFIED BINDERS" @default.
- W286991963 cites W1978872566 @default.
- W286991963 cites W1988147327 @default.
- W286991963 cites W384428954 @default.
- W286991963 cites W580568500 @default.
- W286991963 cites W655514996 @default.
- W286991963 cites W656276915 @default.
- W286991963 cites W855060444 @default.
- W286991963 cites W2008978965 @default.
- W286991963 cites W785399350 @default.
- W286991963 hasPublicationYear "2004" @default.
- W286991963 type Work @default.
- W286991963 sameAs 286991963 @default.
- W286991963 citedByCount "3" @default.
- W286991963 countsByYear W2869919632012 @default.
- W286991963 countsByYear W2869919632013 @default.
- W286991963 countsByYear W2869919632015 @default.
- W286991963 crossrefType "journal-article" @default.
- W286991963 hasAuthorship W286991963A5005895076 @default.
- W286991963 hasAuthorship W286991963A5051251495 @default.
- W286991963 hasAuthorship W286991963A5081756517 @default.
- W286991963 hasAuthorship W286991963A5084319063 @default.
- W286991963 hasConcept C159985019 @default.
- W286991963 hasConcept C168056786 @default.
- W286991963 hasConcept C176864760 @default.
- W286991963 hasConcept C192562407 @default.
- W286991963 hasConcept C200990466 @default.
- W286991963 hasConcept C2778477904 @default.
- W286991963 hasConcept C521977710 @default.
- W286991963 hasConcept C58396970 @default.
- W286991963 hasConcept C76893819 @default.
- W286991963 hasConceptScore W286991963C159985019 @default.
- W286991963 hasConceptScore W286991963C168056786 @default.
- W286991963 hasConceptScore W286991963C176864760 @default.
- W286991963 hasConceptScore W286991963C192562407 @default.
- W286991963 hasConceptScore W286991963C200990466 @default.
- W286991963 hasConceptScore W286991963C2778477904 @default.
- W286991963 hasConceptScore W286991963C521977710 @default.
- W286991963 hasConceptScore W286991963C58396970 @default.
- W286991963 hasConceptScore W286991963C76893819 @default.
- W286991963 hasLocation W2869919631 @default.
- W286991963 hasOpenAccess W286991963 @default.
- W286991963 hasPrimaryLocation W2869919631 @default.
- W286991963 hasRelatedWork W1601841926 @default.
- W286991963 hasRelatedWork W1603872337 @default.
- W286991963 hasRelatedWork W1988368618 @default.
- W286991963 hasRelatedWork W2033698077 @default.
- W286991963 hasRelatedWork W2067642907 @default.
- W286991963 hasRelatedWork W2100006762 @default.
- W286991963 hasRelatedWork W2187348315 @default.
- W286991963 hasRelatedWork W3046457188 @default.
- W286991963 hasRelatedWork W331333890 @default.
- W286991963 hasRelatedWork W562667001 @default.
- W286991963 hasRelatedWork W564879775 @default.
- W286991963 hasRelatedWork W571246903 @default.
- W286991963 hasRelatedWork W581234954 @default.
- W286991963 hasRelatedWork W589420584 @default.
- W286991963 hasRelatedWork W596165465 @default.
- W286991963 hasRelatedWork W596363753 @default.
- W286991963 hasRelatedWork W621206408 @default.
- W286991963 hasRelatedWork W622172795 @default.
- W286991963 hasRelatedWork W637599721 @default.
- W286991963 hasRelatedWork W651294220 @default.
- W286991963 hasVolume "2" @default.
- W286991963 isParatext "false" @default.
- W286991963 isRetracted "false" @default.
- W286991963 magId "286991963" @default.
- W286991963 workType "article" @default.