- W2883572886 abstract "Polymer nanocomposites based on polypropylene (PP) reinforced with carbon nanofibers (CNFs) at a fixed concentration of 0.5% w/w were prepared by precipitation from liquid solutions of PP and CNFs. Ultrasonic processing was used as the primary process for mixing both PP and CNFs in the the solvent, while mechanical stirring was also used as a control process to prepare similar samples. Thermogravimetric analysis (TGA) shows that the ultrasonic processing influences little on the thermal stability of the polymer material. Moreover, ultrasonically-processed PP shows higher tensile strength and better ductility, compared to those of the neat PP. Although the mechanically-processed PP has about 10% higher tensile strength than the ultrasonically-processed one, it is observed that there is a significant deterioration in its ductility due to the dissolution of calcium carbonate which is used as an additive for the neat PP. The advantage of significantly reduced material processing time, increased mixing efficiency, and increase in thermal stability and mechanical properties of ultrasonically-processed PPs indicated that the ultrasonic processing is relatively more effective and efficient mixing process compared to mechanical stirring for preparation of the polymer and its nanocomposite. Tensile tests were also conducted using quasi-static strain rates from 10-4 to 10-1 s-1 in order to obtain the tensile strength, elongation at fracture, and the elastic modulus of injection molded polymer and its nanocomposite. PP-CNF nanocomposites exhibited higher strain-rate sensitivity within the tested strain range, compared to the neat PP. Both the neat PP and PP-CNF nanocomposite exhibited strain-rate dependent material properties, showing an increase in tensile strength, and decrease in elongation with increasing strain rates." @default.
- W2883572886 created "2018-08-03" @default.
- W2883572886 creator A5010381151 @default.
- W2883572886 creator A5020305038 @default.
- W2883572886 creator A5066267685 @default.
- W2883572886 date "2020-01-01" @default.
- W2883572886 modified "2023-10-11" @default.
- W2883572886 title "Study about the Effect of Addition of Carbon Nanofibers on the Strain-Rate Sensitivity of Thermoplastic Polymer Matrix Nanocomposites Manufactured by Ultrasonic Processing" @default.
- W2883572886 cites W1964188236 @default.
- W2883572886 cites W1969404392 @default.
- W2883572886 cites W1989390726 @default.
- W2883572886 cites W1989774993 @default.
- W2883572886 cites W2008853072 @default.
- W2883572886 cites W2010885751 @default.
- W2883572886 cites W2031193021 @default.
- W2883572886 cites W2033798285 @default.
- W2883572886 cites W2047797405 @default.
- W2883572886 cites W2076818411 @default.
- W2883572886 cites W2080488246 @default.
- W2883572886 cites W2148728324 @default.
- W2883572886 cites W2231744117 @default.
- W2883572886 cites W2252622118 @default.
- W2883572886 cites W2501267621 @default.
- W2883572886 cites W2611793107 @default.
- W2883572886 cites W2731585574 @default.
- W2883572886 cites W2810712243 @default.
- W2883572886 cites W2981674716 @default.
- W2883572886 doi "https://doi.org/10.1016/j.promfg.2020.05.062" @default.
- W2883572886 hasPublicationYear "2020" @default.
- W2883572886 type Work @default.
- W2883572886 sameAs 2883572886 @default.
- W2883572886 citedByCount "1" @default.
- W2883572886 countsByYear W28835728862022 @default.
- W2883572886 crossrefType "journal-article" @default.
- W2883572886 hasAuthorship W2883572886A5010381151 @default.
- W2883572886 hasAuthorship W2883572886A5020305038 @default.
- W2883572886 hasAuthorship W2883572886A5066267685 @default.
- W2883572886 hasBestOaLocation W28835728861 @default.
- W2883572886 hasConcept C112950240 @default.
- W2883572886 hasConcept C127413603 @default.
- W2883572886 hasConcept C149912024 @default.
- W2883572886 hasConcept C15920480 @default.
- W2883572886 hasConcept C159985019 @default.
- W2883572886 hasConcept C192562407 @default.
- W2883572886 hasConcept C2776512210 @default.
- W2883572886 hasConcept C2777973245 @default.
- W2883572886 hasConcept C42360764 @default.
- W2883572886 hasConcept C521977710 @default.
- W2883572886 hasConcept C59061564 @default.
- W2883572886 hasConcept C60100273 @default.
- W2883572886 hasConcept C92328351 @default.
- W2883572886 hasConcept C92880739 @default.
- W2883572886 hasConceptScore W2883572886C112950240 @default.
- W2883572886 hasConceptScore W2883572886C127413603 @default.
- W2883572886 hasConceptScore W2883572886C149912024 @default.
- W2883572886 hasConceptScore W2883572886C15920480 @default.
- W2883572886 hasConceptScore W2883572886C159985019 @default.
- W2883572886 hasConceptScore W2883572886C192562407 @default.
- W2883572886 hasConceptScore W2883572886C2776512210 @default.
- W2883572886 hasConceptScore W2883572886C2777973245 @default.
- W2883572886 hasConceptScore W2883572886C42360764 @default.
- W2883572886 hasConceptScore W2883572886C521977710 @default.
- W2883572886 hasConceptScore W2883572886C59061564 @default.
- W2883572886 hasConceptScore W2883572886C60100273 @default.
- W2883572886 hasConceptScore W2883572886C92328351 @default.
- W2883572886 hasConceptScore W2883572886C92880739 @default.
- W2883572886 hasLocation W28835728861 @default.
- W2883572886 hasOpenAccess W2883572886 @default.
- W2883572886 hasPrimaryLocation W28835728861 @default.
- W2883572886 hasRelatedWork W2021956006 @default.
- W2883572886 hasRelatedWork W2079852693 @default.
- W2883572886 hasRelatedWork W2089085266 @default.
- W2883572886 hasRelatedWork W2174588401 @default.
- W2883572886 hasRelatedWork W2290271039 @default.
- W2883572886 hasRelatedWork W2729932191 @default.
- W2883572886 hasRelatedWork W2795554382 @default.
- W2883572886 hasRelatedWork W2947669971 @default.
- W2883572886 hasRelatedWork W3032645088 @default.
- W2883572886 hasRelatedWork W385517348 @default.
- W2883572886 hasVolume "48" @default.
- W2883572886 isParatext "false" @default.
- W2883572886 isRetracted "false" @default.
- W2883572886 magId "2883572886" @default.
- W2883572886 workType "article" @default.