- W2887660090 abstract "In this study, four manganites series with starting compositions La₀.₈₅₋ₓSMₓAG₀.₁₅ (x=0 -0 .2), La₀.₈₋ₓMₓAg₀.₂MnO₃ (M=Dy³⁺, Sm³⁺, x=0-0.15), (l-y) La₀.₈AG₀.₂MnO₃‚/yBiFe0₃ (y=0wt%-3.5wt%) and Pr₀.₆Ca₀.₄₋ₓBaₓMnO₃ (x=0-0.3) were prepared by solid-state reaction method in order to elucidate their physical properties. For La₀.₈₅₋ₓSMₓAG₀.₁₅MnO₃ (x=0-0.2) and La₀.₈₋ₓMₓAg₀.₂MnO₃ (M=Sm3+, Dy³⁺, x=0-0.15) series, the resistivity and magnetic measurements showed all samples exhibit transition from insulating to metallic behavior accompanying a paramagnetic to ferromagnetic transition as the temperatures was decreased. For x=0, two metal-insulator, MI transition peaks were observed at Tᴘ₁ and Tᴘ₂ in the resistivity curves. Both peaks and Curie temperature, Tc shifted to lower temperatures with increasing Dy³⁺ and Sm³⁺, indicating that the substitution weakened the double exchange process and enhanced the Jahn-Teller effect. The magnetoresistance peak was observed around Tᴘ₁ for all samples. The observed double peak behavior in the p(T) curve is suggested to be due magnetic inhomogeneity of the samples. Our result also showed that the inhomogeneity was strongly influenced by the lattice effect. For (l-v)La₀.₈Ag₀.₂MnO₃/yBiFe0 3 (y=Owt%-3.5wt%) composite series, the resistivity and susceptibility measurements showed both metal-insulator transition temperatures, Tᴍ₁ and paramagnetic-ferromagnetic transition temperature, Tc decreased with increasing BFO content indicating weakening of the double exchange, DE mechanism. The MR peak was observed around Tᴍ₁ for all samples which is ascribed to the intrinsic MR effect. Below the peak, the MR increased almost linearly with decreasing temperature for all samples and this ascribed to the phenomena of extrinsic MR. The highest MR% ( at 40 K) was observed for the x=1.5% sample which showed a MR of more than twice that of the undoped (x=0%) sample. This extrinsic effect is suggested to be related to improved spin polarize tunneling of conduction electrons between grains under external field as a result of improved spin alignment. It is suggested that BFO induced some kind of magnetoelectric coupling between BFO and LAMO leading to the enhancement of the process. For Pr₀.₆Ca₀.₄₋ₓABaₓMnO₃ (x=0-0.3) series, the electrical and magnetic measurements showed that the x=0 sample exhibit insulating behavior and an antiferromagnetic to paramagnetic transition behavior. On the other hand, Ba-doped samples exhibit transition from insulating to metallic behavior accompanying a paramagnetic to ferromagnetic transition as the temperatures were decreased. Both Tc and Tᴍ₁ of samples increase with increasing Ba concentration. Magnetoresistance, MR behavior indicates intrinsic MR mechanism for x=0.1 which changed to extrinsic MR for x> 0.2 as a result of Ba substitution. The weakening of charge ordering and inducement of ferromagnetic-metallic (FMM) state as well as increased in both Tc and Tᴍ₁ indicating enhancement of double exchange mechanism which is suggested to be related to the increase of tolerance factor, x and increase of eg₋electron bandwidth as increase with Ba substitution." @default.
- W2887660090 created "2018-08-22" @default.
- W2887660090 creator A5088358651 @default.
- W2887660090 date "2014-01-01" @default.
- W2887660090 modified "2023-09-27" @default.
- W2887660090 title "Effects of doping on magnetic and transport properties of La₀.₈₅₋ₓSMₓAG₀.₁₅MnO₃‚La₀.₈₋ₓMₓAg₀.₂MnO₃ (M=Sm³⁺, Dy³⁺), (1x)La₀.₈Ag₀.₂MnO₃/xBiFeO₃ and Pr₀.₆Ca₀.₄₋ₓBaₓMnO₃ Manganites / Norazila Ibrahim" @default.
- W2887660090 hasPublicationYear "2014" @default.
- W2887660090 type Work @default.
- W2887660090 sameAs 2887660090 @default.
- W2887660090 citedByCount "0" @default.
- W2887660090 crossrefType "dissertation" @default.
- W2887660090 hasAuthorship W2887660090A5088358651 @default.
- W2887660090 hasConcept C113196181 @default.
- W2887660090 hasConcept C115260700 @default.
- W2887660090 hasConcept C117958382 @default.
- W2887660090 hasConcept C121332964 @default.
- W2887660090 hasConcept C121545928 @default.
- W2887660090 hasConcept C124712363 @default.
- W2887660090 hasConcept C179936367 @default.
- W2887660090 hasConcept C185592680 @default.
- W2887660090 hasConcept C191897082 @default.
- W2887660090 hasConcept C192562407 @default.
- W2887660090 hasConcept C26873012 @default.
- W2887660090 hasConcept C43617362 @default.
- W2887660090 hasConcept C49040817 @default.
- W2887660090 hasConcept C544153396 @default.
- W2887660090 hasConcept C57863236 @default.
- W2887660090 hasConcept C62520636 @default.
- W2887660090 hasConcept C63648874 @default.
- W2887660090 hasConcept C69990965 @default.
- W2887660090 hasConcept C82217956 @default.
- W2887660090 hasConceptScore W2887660090C113196181 @default.
- W2887660090 hasConceptScore W2887660090C115260700 @default.
- W2887660090 hasConceptScore W2887660090C117958382 @default.
- W2887660090 hasConceptScore W2887660090C121332964 @default.
- W2887660090 hasConceptScore W2887660090C121545928 @default.
- W2887660090 hasConceptScore W2887660090C124712363 @default.
- W2887660090 hasConceptScore W2887660090C179936367 @default.
- W2887660090 hasConceptScore W2887660090C185592680 @default.
- W2887660090 hasConceptScore W2887660090C191897082 @default.
- W2887660090 hasConceptScore W2887660090C192562407 @default.
- W2887660090 hasConceptScore W2887660090C26873012 @default.
- W2887660090 hasConceptScore W2887660090C43617362 @default.
- W2887660090 hasConceptScore W2887660090C49040817 @default.
- W2887660090 hasConceptScore W2887660090C544153396 @default.
- W2887660090 hasConceptScore W2887660090C57863236 @default.
- W2887660090 hasConceptScore W2887660090C62520636 @default.
- W2887660090 hasConceptScore W2887660090C63648874 @default.
- W2887660090 hasConceptScore W2887660090C69990965 @default.
- W2887660090 hasConceptScore W2887660090C82217956 @default.
- W2887660090 hasLocation W28876600901 @default.
- W2887660090 hasOpenAccess W2887660090 @default.
- W2887660090 hasPrimaryLocation W28876600901 @default.
- W2887660090 hasRelatedWork W170369052 @default.
- W2887660090 hasRelatedWork W2020603316 @default.
- W2887660090 hasRelatedWork W2080507458 @default.
- W2887660090 hasRelatedWork W2115839349 @default.
- W2887660090 hasRelatedWork W2235518705 @default.
- W2887660090 hasRelatedWork W2258529060 @default.
- W2887660090 hasRelatedWork W2373865689 @default.
- W2887660090 hasRelatedWork W2389895878 @default.
- W2887660090 hasRelatedWork W2500041993 @default.
- W2887660090 hasRelatedWork W2734144793 @default.
- W2887660090 hasRelatedWork W2770779457 @default.
- W2887660090 hasRelatedWork W2784003703 @default.
- W2887660090 hasRelatedWork W2889708618 @default.
- W2887660090 hasRelatedWork W2900496203 @default.
- W2887660090 hasRelatedWork W2968393623 @default.
- W2887660090 hasRelatedWork W2984947522 @default.
- W2887660090 hasRelatedWork W3010872353 @default.
- W2887660090 hasRelatedWork W3048791612 @default.
- W2887660090 hasRelatedWork W67114327 @default.
- W2887660090 hasRelatedWork W2289111684 @default.
- W2887660090 isParatext "false" @default.
- W2887660090 isRetracted "false" @default.
- W2887660090 magId "2887660090" @default.
- W2887660090 workType "dissertation" @default.