- W2888160844 abstract "Dense Ti3AlC2 components with a complex shape were fabricated using gel casting followed by pressure-less sintering. Low viscosity slurry was prepared using an aqueous based acrylamide (AM) monomer with a 50% solid loading. Homogeneous and crack free Ti3AlC2 green bodies were obtained. The sintering temperatures were set at 1500, 1550 and 1600 °C, highest relative density of 93% was achieved at 1550 °C. Surprisingly, samples sintered at 1600 °C resulted in a drop of relative density because of the abnormal grain growth and entrapped porosity. The pressure-less sintered samples had mechanical properties comparable to hot pressed counterparts with Vickers hardness of 3.1 ± 0.2 GPa, fracture toughness of 4.2 ± 0.2 MPa m1/2 and flexural strength of 302.3 ± 25.0 MPa. Final machining was still required to obtain a net shape components free from surface defects." @default.
- W2888160844 created "2018-08-31" @default.
- W2888160844 creator A5020686943 @default.
- W2888160844 creator A5045923205 @default.
- W2888160844 creator A5064485771 @default.
- W2888160844 creator A5074770403 @default.
- W2888160844 date "2018-12-01" @default.
- W2888160844 modified "2023-10-17" @default.
- W2888160844 title "Microstructure and mechanical properties of gel casted Ti3AlC2" @default.
- W2888160844 cites W1969007941 @default.
- W2888160844 cites W1982216995 @default.
- W2888160844 cites W1983152887 @default.
- W2888160844 cites W1989554193 @default.
- W2888160844 cites W2007203774 @default.
- W2888160844 cites W2017391869 @default.
- W2888160844 cites W2027027450 @default.
- W2888160844 cites W2065460947 @default.
- W2888160844 cites W2080210126 @default.
- W2888160844 cites W2087690365 @default.
- W2888160844 cites W2101614336 @default.
- W2888160844 cites W2143179383 @default.
- W2888160844 cites W2277327873 @default.
- W2888160844 cites W2417627910 @default.
- W2888160844 cites W2792691259 @default.
- W2888160844 doi "https://doi.org/10.1016/j.ceramint.2018.08.269" @default.
- W2888160844 hasPublicationYear "2018" @default.
- W2888160844 type Work @default.
- W2888160844 sameAs 2888160844 @default.
- W2888160844 citedByCount "13" @default.
- W2888160844 countsByYear W28881608442020 @default.
- W2888160844 countsByYear W28881608442021 @default.
- W2888160844 countsByYear W28881608442022 @default.
- W2888160844 countsByYear W28881608442023 @default.
- W2888160844 crossrefType "journal-article" @default.
- W2888160844 hasAuthorship W2888160844A5020686943 @default.
- W2888160844 hasAuthorship W2888160844A5045923205 @default.
- W2888160844 hasAuthorship W2888160844A5064485771 @default.
- W2888160844 hasAuthorship W2888160844A5074770403 @default.
- W2888160844 hasConcept C133392424 @default.
- W2888160844 hasConcept C134132462 @default.
- W2888160844 hasConcept C159985019 @default.
- W2888160844 hasConcept C178405089 @default.
- W2888160844 hasConcept C192562407 @default.
- W2888160844 hasConcept C2777581544 @default.
- W2888160844 hasConcept C6648577 @default.
- W2888160844 hasConcept C82455628 @default.
- W2888160844 hasConcept C87976508 @default.
- W2888160844 hasConcept C94293008 @default.
- W2888160844 hasConcept C97549433 @default.
- W2888160844 hasConceptScore W2888160844C133392424 @default.
- W2888160844 hasConceptScore W2888160844C134132462 @default.
- W2888160844 hasConceptScore W2888160844C159985019 @default.
- W2888160844 hasConceptScore W2888160844C178405089 @default.
- W2888160844 hasConceptScore W2888160844C192562407 @default.
- W2888160844 hasConceptScore W2888160844C2777581544 @default.
- W2888160844 hasConceptScore W2888160844C6648577 @default.
- W2888160844 hasConceptScore W2888160844C82455628 @default.
- W2888160844 hasConceptScore W2888160844C87976508 @default.
- W2888160844 hasConceptScore W2888160844C94293008 @default.
- W2888160844 hasConceptScore W2888160844C97549433 @default.
- W2888160844 hasFunder F4320321001 @default.
- W2888160844 hasFunder F4320322720 @default.
- W2888160844 hasFunder F4320335787 @default.
- W2888160844 hasIssue "18" @default.
- W2888160844 hasLocation W28881608441 @default.
- W2888160844 hasOpenAccess W2888160844 @default.
- W2888160844 hasPrimaryLocation W28881608441 @default.
- W2888160844 hasRelatedWork W1504566435 @default.
- W2888160844 hasRelatedWork W1969962577 @default.
- W2888160844 hasRelatedWork W2036955125 @default.
- W2888160844 hasRelatedWork W2118707158 @default.
- W2888160844 hasRelatedWork W2335131106 @default.
- W2888160844 hasRelatedWork W2370309317 @default.
- W2888160844 hasRelatedWork W2377834100 @default.
- W2888160844 hasRelatedWork W2385903672 @default.
- W2888160844 hasRelatedWork W3034984046 @default.
- W2888160844 hasRelatedWork W4313418304 @default.
- W2888160844 hasVolume "44" @default.
- W2888160844 isParatext "false" @default.
- W2888160844 isRetracted "false" @default.
- W2888160844 magId "2888160844" @default.
- W2888160844 workType "article" @default.