- W2889538086 endingPage "462" @default.
- W2889538086 startingPage "456" @default.
- W2889538086 abstract "Silica ceramics were fabricated via an additive manufacturing process based on stereolithography. Ceramic suspension with low viscosity and high solid loading is of importance to stereolithography based UV-curable. In this work, to meet the requirements of stereolithography, effects of temperature, additive content and ball-milling time on the viscosity of silica slurry were investigated, and properties of silica ceramics sintered at different temperature were also researched.The results show that increasing temperatures strongly decrease the viscosity unless when the temperature is above 70°C. The minimum of viscosity was observed for an appropriate addition of dispersant, which is corresponding to the best dispersion state of silica particles in the photopolymerizable monomer. And optimizing ball-milling time showed the lowest viscosity suitable for the stereolithography process. The appropriate temperature, additive content and ball-milling time facilitating stereolithography was 70°C, 2% and 60min respectively. The prepared ceramics sintered at 1220°C showed a density and flexural strength of 1.57g/cm 3 and 13.31MPa respectively." @default.
- W2889538086 created "2018-09-07" @default.
- W2889538086 creator A5003361209 @default.
- W2889538086 creator A5003416049 @default.
- W2889538086 creator A5007214539 @default.
- W2889538086 creator A5008036470 @default.
- W2889538086 creator A5040623421 @default.
- W2889538086 creator A5042886937 @default.
- W2889538086 creator A5084604854 @default.
- W2889538086 date "2018-08-01" @default.
- W2889538086 modified "2023-10-06" @default.
- W2889538086 title "Fabrication of Dense Silica Ceramics through a Stereo Lithography-Based Additive Manufacturing" @default.
- W2889538086 cites W2015955124 @default.
- W2889538086 cites W2048174558 @default.
- W2889538086 cites W2110695739 @default.
- W2889538086 cites W2120427003 @default.
- W2889538086 cites W2286879068 @default.
- W2889538086 cites W2303443611 @default.
- W2889538086 cites W2492188007 @default.
- W2889538086 cites W2512650113 @default.
- W2889538086 cites W67926984 @default.
- W2889538086 doi "https://doi.org/10.4028/www.scientific.net/ssp.281.456" @default.
- W2889538086 hasPublicationYear "2018" @default.
- W2889538086 type Work @default.
- W2889538086 sameAs 2889538086 @default.
- W2889538086 citedByCount "6" @default.
- W2889538086 countsByYear W28895380862020 @default.
- W2889538086 countsByYear W28895380862021 @default.
- W2889538086 countsByYear W28895380862022 @default.
- W2889538086 countsByYear W28895380862023 @default.
- W2889538086 crossrefType "journal-article" @default.
- W2889538086 hasAuthorship W2889538086A5003361209 @default.
- W2889538086 hasAuthorship W2889538086A5003416049 @default.
- W2889538086 hasAuthorship W2889538086A5007214539 @default.
- W2889538086 hasAuthorship W2889538086A5008036470 @default.
- W2889538086 hasAuthorship W2889538086A5040623421 @default.
- W2889538086 hasAuthorship W2889538086A5042886937 @default.
- W2889538086 hasAuthorship W2889538086A5084604854 @default.
- W2889538086 hasConcept C120665830 @default.
- W2889538086 hasConcept C121332964 @default.
- W2889538086 hasConcept C127172972 @default.
- W2889538086 hasConcept C132186339 @default.
- W2889538086 hasConcept C134132462 @default.
- W2889538086 hasConcept C136525101 @default.
- W2889538086 hasConcept C142724271 @default.
- W2889538086 hasConcept C145889102 @default.
- W2889538086 hasConcept C159985019 @default.
- W2889538086 hasConcept C177562468 @default.
- W2889538086 hasConcept C178405089 @default.
- W2889538086 hasConcept C192562407 @default.
- W2889538086 hasConcept C204787440 @default.
- W2889538086 hasConcept C2779154291 @default.
- W2889538086 hasConcept C71924100 @default.
- W2889538086 hasConcept C94293008 @default.
- W2889538086 hasConceptScore W2889538086C120665830 @default.
- W2889538086 hasConceptScore W2889538086C121332964 @default.
- W2889538086 hasConceptScore W2889538086C127172972 @default.
- W2889538086 hasConceptScore W2889538086C132186339 @default.
- W2889538086 hasConceptScore W2889538086C134132462 @default.
- W2889538086 hasConceptScore W2889538086C136525101 @default.
- W2889538086 hasConceptScore W2889538086C142724271 @default.
- W2889538086 hasConceptScore W2889538086C145889102 @default.
- W2889538086 hasConceptScore W2889538086C159985019 @default.
- W2889538086 hasConceptScore W2889538086C177562468 @default.
- W2889538086 hasConceptScore W2889538086C178405089 @default.
- W2889538086 hasConceptScore W2889538086C192562407 @default.
- W2889538086 hasConceptScore W2889538086C204787440 @default.
- W2889538086 hasConceptScore W2889538086C2779154291 @default.
- W2889538086 hasConceptScore W2889538086C71924100 @default.
- W2889538086 hasConceptScore W2889538086C94293008 @default.
- W2889538086 hasLocation W28895380861 @default.
- W2889538086 hasOpenAccess W2889538086 @default.
- W2889538086 hasPrimaryLocation W28895380861 @default.
- W2889538086 hasRelatedWork W1680857168 @default.
- W2889538086 hasRelatedWork W2025687592 @default.
- W2889538086 hasRelatedWork W2119161493 @default.
- W2889538086 hasRelatedWork W2281145519 @default.
- W2889538086 hasRelatedWork W2354611855 @default.
- W2889538086 hasRelatedWork W2369078514 @default.
- W2889538086 hasRelatedWork W2944045227 @default.
- W2889538086 hasRelatedWork W2981951137 @default.
- W2889538086 hasRelatedWork W4313256593 @default.
- W2889538086 hasRelatedWork W4366538280 @default.
- W2889538086 hasVolume "281" @default.
- W2889538086 isParatext "false" @default.
- W2889538086 isRetracted "false" @default.
- W2889538086 magId "2889538086" @default.
- W2889538086 workType "article" @default.