• W2890141064 abstract "A silicone-based elastomer filled with vinyl-silane treated aluminum hydroxide was used to replace conventional polyurethane-based adhesive to provide a flame-retardant adhesive for plywood. The shear strength and fire performance of such a silicone-based (SI) adhesive glued plywood (SI/plywood) were investigated and compared to those of the polyurethane-based (PU) adhesive glued plywood (PU/plywood). The shear strength of the SI/plywood [(0.92 ± 0.09) MPa] was about 63% lower than that of the PU/plywood at room temperature, but it was less sensitive to water (62% reduction for the PU/plywood and 30% reduction for the SI/plywood after hot-water immersion at 63 °C for 3 h). The fire performance of plywood was assessed by a simulated match-flame ignition test (Mydrin test), lateral ignition and flame spread test, cone calorimetry, and thermocouple measurements. With a higher burn-though resistance and thermal barrier efficiency, and lower flame spread and heat release rate, the SI/plywood exhibited a superior fire-resistance and reaction-to-fire performance and improved fire-resistance as compared to the PU/plywood. The SI adhesive generated an inorganic protective layer on the sample surface that visibly suppressed glowing and smoldering of the plywood during combustion. The SI adhesive was also combined and reinforced with cellulosic fabric (CF) or glass fabric (GF) to prepare composite plywood (SI/CF/plywood and SI/GF/plywood) with improved fire performance. The cone calorimetry and thermocouple measurements indicated that the use of CF or GF in SI/CF/plywood and SI/GF/plywood, respectively, suppressed the delamination and cracking of the composite plywood and promoted the formation of an effective thermal barrier during smoldering and flaming combustion. Particularly, the SI/GF/plywood exhibited the most effective fire barrier with no crack formation, and the lowest heat release rate among the plywood types investigated in this study." @default.
• W2890141064 created "2018-09-27" @default.
• W2890141064 creator A5003535413 @default.
• W2890141064 creator A5022536474 @default.
• W2890141064 creator A5029193760 @default.
• W2890141064 creator A5043691782 @default.
• W2890141064 creator A5049242358 @default.
• W2890141064 creator A5056910387 @default.
• W2890141064 creator A5070199489 @default.
• W2890141064 creator A5086659403 @default.
• W2890141064 date "2018-11-01" @default.
• W2890141064 modified "2023-09-28" @default.
• W2890141064 title "A novel application of silicone-based flame-retardant adhesive in plywood" @default.
• W2890141064 cites W1504281967 @default.
• W2890141064 cites W1937003908 @default.
• W2890141064 cites W1965117350 @default.
• W2890141064 cites W1966993500 @default.
• W2890141064 cites W1970648125 @default.
• W2890141064 cites W1981077321 @default.
• W2890141064 cites W1984100364 @default.
• W2890141064 cites W1990810258 @default.
• W2890141064 cites W1997423283 @default.
• W2890141064 cites W2020847739 @default.
• W2890141064 cites W2021881985 @default.
• W2890141064 cites W2032029842 @default.
• W2890141064 cites W2040808523 @default.
• W2890141064 cites W2044600012 @default.
• W2890141064 cites W2049325854 @default.
• W2890141064 cites W2050519561 @default.
• W2890141064 cites W2059749508 @default.
• W2890141064 cites W2060238162 @default.
• W2890141064 cites W2065878323 @default.
• W2890141064 cites W2078050573 @default.
• W2890141064 cites W2080753939 @default.
• W2890141064 cites W2080974761 @default.
• W2890141064 cites W2092694765 @default.
• W2890141064 cites W2099552907 @default.
• W2890141064 cites W2099739685 @default.
• W2890141064 cites W2152862499 @default.
• W2890141064 cites W2158412820 @default.
• W2890141064 cites W2158742851 @default.
• W2890141064 cites W2296834794 @default.
• W2890141064 cites W2317783008 @default.
• W2890141064 cites W2328615110 @default.
• W2890141064 cites W2492426125 @default.
• W2890141064 cites W2546575770 @default.
• W2890141064 cites W2615740032 @default.
• W2890141064 cites W2884040690 @default.
• W2890141064 cites W33851366 @default.
• W2890141064 doi "https://doi.org/10.1016/j.conbuildmat.2018.08.214" @default.
• W2890141064 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/6459615" @default.
• W2890141064 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/30983679" @default.
• W2890141064 hasPublicationYear "2018" @default.
• W2890141064 type Work @default.
• W2890141064 sameAs 2890141064 @default.
• W2890141064 citedByCount "42" @default.
• W2890141064 countsByYear W28901410642019 @default.
• W2890141064 countsByYear W28901410642020 @default.
• W2890141064 countsByYear W28901410642021 @default.
• W2890141064 countsByYear W28901410642022 @default.
• W2890141064 countsByYear W28901410642023 @default.
• W2890141064 crossrefType "journal-article" @default.
• W2890141064 hasAuthorship W2890141064A5003535413 @default.
• W2890141064 hasAuthorship W2890141064A5022536474 @default.
• W2890141064 hasAuthorship W2890141064A5029193760 @default.
• W2890141064 hasAuthorship W2890141064A5043691782 @default.
• W2890141064 hasAuthorship W2890141064A5049242358 @default.
• W2890141064 hasAuthorship W2890141064A5056910387 @default.
• W2890141064 hasAuthorship W2890141064A5070199489 @default.
• W2890141064 hasAuthorship W2890141064A5086659403 @default.
• W2890141064 hasBestOaLocation W28901410641 @default.
• W2890141064 hasConcept C105923489 @default.
• W2890141064 hasConcept C159985019 @default.
• W2890141064 hasConcept C178790620 @default.
• W2890141064 hasConcept C185592680 @default.
• W2890141064 hasConcept C192562407 @default.
• W2890141064 hasConcept C205474432 @default.
• W2890141064 hasConcept C2778024649 @default.
• W2890141064 hasConcept C2779227376 @default.
• W2890141064 hasConcept C2779578285 @default.
• W2890141064 hasConcept C2779769944 @default.
• W2890141064 hasConcept C2779970684 @default.
• W2890141064 hasConcept C2781465349 @default.
• W2890141064 hasConcept C2987912017 @default.
• W2890141064 hasConcept C33374538 @default.
• W2890141064 hasConcept C68928338 @default.
• W2890141064 hasConceptScore W2890141064C105923489 @default.
• W2890141064 hasConceptScore W2890141064C159985019 @default.
• W2890141064 hasConceptScore W2890141064C178790620 @default.
• W2890141064 hasConceptScore W2890141064C185592680 @default.
• W2890141064 hasConceptScore W2890141064C192562407 @default.
• W2890141064 hasConceptScore W2890141064C205474432 @default.
• W2890141064 hasConceptScore W2890141064C2778024649 @default.
• W2890141064 hasConceptScore W2890141064C2779227376 @default.
• W2890141064 hasConceptScore W2890141064C2779578285 @default.
• W2890141064 hasConceptScore W2890141064C2779769944 @default.
• W2890141064 hasConceptScore W2890141064C2779970684 @default.
• W2890141064 hasConceptScore W2890141064C2781465349 @default.

• next