• W2890675455 abstract "A study has been made of the influence of titanium carbide and boron nitride precipitates on the texture and formability of high purity iron-based alloy sheet. Four Fe-Ti-C alloys with the following compositions were investigated: Fe - 0. 011% Ti - 0.004% C, Fe - 0.09% Ti - 0.018%C, Fe - 0.47% Ti - 0.09% C and Fe - 0.48% Ti - 0.011%C. The ratio of titanium to carbon in the first three alloys was approximately 4:1, the stoichiometric ratio for the formation of titanium carbide. The latter alloy was used to study the effect of excess titanium in solution. An Fe - 0.01%B - 0.015%N alloy was also studied to investigate the effect of boron nitride on texture and formability. The alloys were hot rolled and given various heat treatments to produce a range of precipitate dispersions. The materials were then cold rolled 85% and annealed, using a heating rate of 50°C/hour. Plastic strain ratio (R) and mechanical property measurements were made on the annealed sheet at 0°, 45° and 90° to the rolling direction, using a uniaxial tensile test. The Erichsen test was used to assess stretch-formability, and inverse pole figure data were determined on selected specimens. The presence of titanium carbide precipitates usually led to a small improvement in the average plastic strain rate (R) of each of the Fe-Ti-C alloys after recrystallisation. The presence of titanium in solution resulted in a further small increase in R in the recrystallised condition. Grain growth after primary recrystallisation led to increases in R in both high purity iron and the Fe-Ti-C alloys. The greatest rates of increase in R with grain growth were exhibited by those materials with the highest values of R in the just recrystallised condition, and an R value of 2. 4 was obtained on the Fe - 0.48% Ti - 0.011% C alloy after annealing at 830°C. The coarse boron nitride precipitates in the Fe-B-N alloy had little effect on R. High R values were favoured by the presence of {222}, {332} and {211} orientations and by the absence of {200}, {310} and {420} orientations. The results indicated that the recrystallisation textures developed by a combined oriented nucleation and growth mechanism. The Erichsen values exhibited by the Fe-Ti-C alloys were generally higher than those for high purity iron, while those for the Fe-B-N alloy were very low. The correlation between Erichsen value and mechanical properties was quite poor." @default.
• W2890675455 created "2018-09-27" @default.
• W2890675455 creator A5052405584 @default.
• W2890675455 date "1971-01-01" @default.
• W2890675455 modified "2023-09-23" @default.
• W2890675455 title "The influence of precipitates on the texture and formability of high purity iron-based alloy sheet." @default.
• W2890675455 hasPublicationYear "1971" @default.
• W2890675455 type Work @default.
• W2890675455 sameAs 2890675455 @default.
• W2890675455 citedByCount "0" @default.
• W2890675455 crossrefType "dissertation" @default.
• W2890675455 hasAuthorship W2890675455A5052405584 @default.
• W2890675455 hasConcept C112950240 @default.
• W2890675455 hasConcept C115961682 @default.
• W2890675455 hasConcept C154945302 @default.
• W2890675455 hasConcept C159985019 @default.
• W2890675455 hasConcept C191897082 @default.
• W2890675455 hasConcept C192562407 @default.
• W2890675455 hasConcept C194760766 @default.
• W2890675455 hasConcept C2779227376 @default.
• W2890675455 hasConcept C2780026712 @default.
• W2890675455 hasConcept C2781195486 @default.
• W2890675455 hasConcept C41008148 @default.
• W2890675455 hasConcept C506065880 @default.
• W2890675455 hasConcept C5335593 @default.
• W2890675455 hasConcept C79127381 @default.
• W2890675455 hasConceptScore W2890675455C112950240 @default.
• W2890675455 hasConceptScore W2890675455C115961682 @default.
• W2890675455 hasConceptScore W2890675455C154945302 @default.
• W2890675455 hasConceptScore W2890675455C159985019 @default.
• W2890675455 hasConceptScore W2890675455C191897082 @default.
• W2890675455 hasConceptScore W2890675455C192562407 @default.
• W2890675455 hasConceptScore W2890675455C194760766 @default.
• W2890675455 hasConceptScore W2890675455C2779227376 @default.
• W2890675455 hasConceptScore W2890675455C2780026712 @default.
• W2890675455 hasConceptScore W2890675455C2781195486 @default.
• W2890675455 hasConceptScore W2890675455C41008148 @default.
• W2890675455 hasConceptScore W2890675455C506065880 @default.
• W2890675455 hasConceptScore W2890675455C5335593 @default.
• W2890675455 hasConceptScore W2890675455C79127381 @default.
• W2890675455 hasLocation W28906754551 @default.
• W2890675455 hasOpenAccess W2890675455 @default.
• W2890675455 hasPrimaryLocation W28906754551 @default.
• W2890675455 hasRelatedWork W171682140 @default.
• W2890675455 hasRelatedWork W2001995140 @default.
• W2890675455 hasRelatedWork W2042192596 @default.
• W2890675455 hasRelatedWork W2058852182 @default.
• W2890675455 hasRelatedWork W2065482775 @default.
• W2890675455 hasRelatedWork W2315525882 @default.
• W2890675455 hasRelatedWork W2323821651 @default.
• W2890675455 hasRelatedWork W2327059825 @default.
• W2890675455 hasRelatedWork W2556474467 @default.
• W2890675455 hasRelatedWork W2600490536 @default.
• W2890675455 hasRelatedWork W2740715947 @default.
• W2890675455 hasRelatedWork W2793035594 @default.
• W2890675455 hasRelatedWork W3013995521 @default.
• W2890675455 hasRelatedWork W3112084243 @default.
• W2890675455 hasRelatedWork W994770087 @default.
• W2890675455 hasRelatedWork W2776295974 @default.
• W2890675455 hasRelatedWork W2826981926 @default.
• W2890675455 hasRelatedWork W2851242831 @default.
• W2890675455 hasRelatedWork W2934660479 @default.
• W2890675455 hasRelatedWork W3146146620 @default.
• W2890675455 isParatext "false" @default.
• W2890675455 isRetracted "false" @default.
• W2890675455 magId "2890675455" @default.
• W2890675455 workType "dissertation" @default.