- W2890849154 abstract "Due to resemblance of mineral components of bones and human hard tissue, hydroxyapatite, HA with chemical formula Ca10(PO4)6(OH)2 has been widely used in medical field especially as bone replacement. All the waste materials such as chicken eggshells (CHA), duck eggshells (DHA) and cockle shells (SHA) are mainly composed of calcium carbonate, CaCO3. In this study, HA was fabricated from CaCO3 of the waste materials and diammonium hydrogen solution via microwave irradiation technique. Under the effect of microwave irradiation for 15 min, HA was produced directly in the solution and involved in crystallographic transformation. X-ray diffraction, XRD pattern revealed that no impurities other than HA was produced and the peaks were complement with standard HA (JCPDS file- 00-024-0033). All HA characteristics were evident in Fourier Transform Infra-Red, FTIR spectrum such as chemical groups of PO43-, OH- and a weak spectra of CO32-. As microwave power increased from 550W to 900W, Field Emission Scanning Electron Microscopy, FESEM micrographs showed a transition of HA particles shape from needle-like to mixture of needle-like and spherical to spherical shape. Energy Dispersive X-ray, EDX results showed that non-stoichiometric HA was produced for all samples except for SHA900 where the Ca/P ratio is 1.66 under microwave irradiation of 900W. CHA and DHA samples showed an abundance of Ca with a decreasing Ca/P ratio while Ca/P ratio of SHA increased as the microwave power increased (550-900W). Compression test showed a decreasing trend in compressive strength as the microwave power increased for all types of samples. CHA550 has the highest value of compressive strength (71.61 MPa) under the irradiation of 550W. In conclusion, the production of HA powder is reproducible, fast and environmentally friendly. The optimum microwave power to fabricate non-stoichiometric HA was 550W and 700W." @default.
- W2890849154 created "2018-09-27" @default.
- W2890849154 creator A5005623148 @default.
- W2890849154 date "2017-07-01" @default.
- W2890849154 modified "2023-09-27" @default.
- W2890849154 title "Synthesis and characterization of hydroxyapatite from waste materials / Nor Adzliana Sajahan" @default.
- W2890849154 hasPublicationYear "2017" @default.
- W2890849154 type Work @default.
- W2890849154 sameAs 2890849154 @default.
- W2890849154 citedByCount "0" @default.
- W2890849154 crossrefType "dissertation" @default.
- W2890849154 hasAuthorship W2890849154A5005623148 @default.
- W2890849154 hasConcept C113196181 @default.
- W2890849154 hasConcept C121332964 @default.
- W2890849154 hasConcept C127413603 @default.
- W2890849154 hasConcept C13965031 @default.
- W2890849154 hasConcept C159985019 @default.
- W2890849154 hasConcept C160892712 @default.
- W2890849154 hasConcept C178790620 @default.
- W2890849154 hasConcept C185592680 @default.
- W2890849154 hasConcept C192562407 @default.
- W2890849154 hasConcept C199289684 @default.
- W2890849154 hasConcept C26771246 @default.
- W2890849154 hasConcept C2776275140 @default.
- W2890849154 hasConcept C30407753 @default.
- W2890849154 hasConcept C42360764 @default.
- W2890849154 hasConcept C43617362 @default.
- W2890849154 hasConcept C44838205 @default.
- W2890849154 hasConcept C62520636 @default.
- W2890849154 hasConcept C71987851 @default.
- W2890849154 hasConceptScore W2890849154C113196181 @default.
- W2890849154 hasConceptScore W2890849154C121332964 @default.
- W2890849154 hasConceptScore W2890849154C127413603 @default.
- W2890849154 hasConceptScore W2890849154C13965031 @default.
- W2890849154 hasConceptScore W2890849154C159985019 @default.
- W2890849154 hasConceptScore W2890849154C160892712 @default.
- W2890849154 hasConceptScore W2890849154C178790620 @default.
- W2890849154 hasConceptScore W2890849154C185592680 @default.
- W2890849154 hasConceptScore W2890849154C192562407 @default.
- W2890849154 hasConceptScore W2890849154C199289684 @default.
- W2890849154 hasConceptScore W2890849154C26771246 @default.
- W2890849154 hasConceptScore W2890849154C2776275140 @default.
- W2890849154 hasConceptScore W2890849154C30407753 @default.
- W2890849154 hasConceptScore W2890849154C42360764 @default.
- W2890849154 hasConceptScore W2890849154C43617362 @default.
- W2890849154 hasConceptScore W2890849154C44838205 @default.
- W2890849154 hasConceptScore W2890849154C62520636 @default.
- W2890849154 hasConceptScore W2890849154C71987851 @default.
- W2890849154 hasLocation W28908491541 @default.
- W2890849154 hasOpenAccess W2890849154 @default.
- W2890849154 hasPrimaryLocation W28908491541 @default.
- W2890849154 hasRelatedWork W1589920690 @default.
- W2890849154 hasRelatedWork W1967335581 @default.
- W2890849154 hasRelatedWork W2015704401 @default.
- W2890849154 hasRelatedWork W2027277704 @default.
- W2890849154 hasRelatedWork W2073308623 @default.
- W2890849154 hasRelatedWork W2082787077 @default.
- W2890849154 hasRelatedWork W2108763200 @default.
- W2890849154 hasRelatedWork W2112218804 @default.
- W2890849154 hasRelatedWork W2901776574 @default.
- W2890849154 hasRelatedWork W2972968501 @default.
- W2890849154 hasRelatedWork W2981006854 @default.
- W2890849154 hasRelatedWork W3108374683 @default.
- W2890849154 hasRelatedWork W3112089627 @default.
- W2890849154 hasRelatedWork W3146088284 @default.
- W2890849154 hasRelatedWork W3189981968 @default.
- W2890849154 hasRelatedWork W3212728835 @default.
- W2890849154 hasRelatedWork W994120 @default.
- W2890849154 hasRelatedWork W1903460908 @default.
- W2890849154 hasRelatedWork W2524148204 @default.
- W2890849154 hasRelatedWork W3097436717 @default.
- W2890849154 isParatext "false" @default.
- W2890849154 isRetracted "false" @default.
- W2890849154 magId "2890849154" @default.
- W2890849154 workType "dissertation" @default.