- W2891466675 abstract "Effects of the stirring time in TiO2 sol chemical on the optical transmittance of the spin-coated films over the visible-to-near-infrared region were studied. It was observed that the longer stirring time, from 12 hours to 48 hours could provide films with either observably higher or lower transmittance, depending on the solvent. In Isopropanol, or IPA, the longer stirring time of the sol chemical leaded to a lower optical transmittance. In hydrochloric acid, or HCl, the trend was reversed; the longer stirring time of the sol chemical would cause a higher optical transmittance. Effects in both solvent were more pronounced at lower wavelengths, i.e. the increasing or decreasing of the transmittance with the extended stirring time could be seen more noticeably at low wavelengths. We believed that these phenomena were caused by the change in dispersion of the TiO2 particle in the solvent over the stirring time. In HCl, which is an acid-based solvent, the particle could be better dispersed than that in IPA, resulting in a proportional relation between the stirring time and the transmittance of the spin-coated films. This assumption was supported when the transmittance of the films in IPA and HCL were compared as it could be seen that the transmittance of the former was lower. The results from this study could be used to help select an appropriate preparation time of the TiO2 sol chemicals in different solvents to obtain a spin-coated film with a required level of optical transmittance." @default.
- W2891466675 created "2018-09-27" @default.
- W2891466675 creator A5011382027 @default.
- W2891466675 creator A5027187408 @default.
- W2891466675 creator A5043211161 @default.
- W2891466675 creator A5050392330 @default.
- W2891466675 date "2018-01-01" @default.
- W2891466675 modified "2023-10-12" @default.
- W2891466675 title "Effects of spin-coating recipe on the transmittance of spin-coated TiO2 films" @default.
- W2891466675 cites W1967904330 @default.
- W2891466675 cites W2019903682 @default.
- W2891466675 cites W2073784682 @default.
- W2891466675 cites W2110011811 @default.
- W2891466675 cites W2116327492 @default.
- W2891466675 doi "https://doi.org/10.1063/1.5053178" @default.
- W2891466675 hasPublicationYear "2018" @default.
- W2891466675 type Work @default.
- W2891466675 sameAs 2891466675 @default.
- W2891466675 citedByCount "0" @default.
- W2891466675 crossrefType "proceedings-article" @default.
- W2891466675 hasAuthorship W2891466675A5011382027 @default.
- W2891466675 hasAuthorship W2891466675A5027187408 @default.
- W2891466675 hasAuthorship W2891466675A5043211161 @default.
- W2891466675 hasAuthorship W2891466675A5050392330 @default.
- W2891466675 hasBestOaLocation W28914666751 @default.
- W2891466675 hasConcept C113196181 @default.
- W2891466675 hasConcept C115196108 @default.
- W2891466675 hasConcept C120665830 @default.
- W2891466675 hasConcept C121332964 @default.
- W2891466675 hasConcept C147789679 @default.
- W2891466675 hasConcept C150493377 @default.
- W2891466675 hasConcept C159985019 @default.
- W2891466675 hasConcept C178790620 @default.
- W2891466675 hasConcept C185592680 @default.
- W2891466675 hasConcept C187530423 @default.
- W2891466675 hasConcept C191897082 @default.
- W2891466675 hasConcept C192562407 @default.
- W2891466675 hasConcept C2777436746 @default.
- W2891466675 hasConcept C2780471494 @default.
- W2891466675 hasConcept C2781448156 @default.
- W2891466675 hasConcept C43617362 @default.
- W2891466675 hasConcept C49040817 @default.
- W2891466675 hasConcept C6260449 @default.
- W2891466675 hasConceptScore W2891466675C113196181 @default.
- W2891466675 hasConceptScore W2891466675C115196108 @default.
- W2891466675 hasConceptScore W2891466675C120665830 @default.
- W2891466675 hasConceptScore W2891466675C121332964 @default.
- W2891466675 hasConceptScore W2891466675C147789679 @default.
- W2891466675 hasConceptScore W2891466675C150493377 @default.
- W2891466675 hasConceptScore W2891466675C159985019 @default.
- W2891466675 hasConceptScore W2891466675C178790620 @default.
- W2891466675 hasConceptScore W2891466675C185592680 @default.
- W2891466675 hasConceptScore W2891466675C187530423 @default.
- W2891466675 hasConceptScore W2891466675C191897082 @default.
- W2891466675 hasConceptScore W2891466675C192562407 @default.
- W2891466675 hasConceptScore W2891466675C2777436746 @default.
- W2891466675 hasConceptScore W2891466675C2780471494 @default.
- W2891466675 hasConceptScore W2891466675C2781448156 @default.
- W2891466675 hasConceptScore W2891466675C43617362 @default.
- W2891466675 hasConceptScore W2891466675C49040817 @default.
- W2891466675 hasConceptScore W2891466675C6260449 @default.
- W2891466675 hasLocation W28914666751 @default.
- W2891466675 hasOpenAccess W2891466675 @default.
- W2891466675 hasPrimaryLocation W28914666751 @default.
- W2891466675 hasRelatedWork W1972051230 @default.
- W2891466675 hasRelatedWork W2001881102 @default.
- W2891466675 hasRelatedWork W2008995181 @default.
- W2891466675 hasRelatedWork W2015313887 @default.
- W2891466675 hasRelatedWork W2015838393 @default.
- W2891466675 hasRelatedWork W2018919351 @default.
- W2891466675 hasRelatedWork W2034727234 @default.
- W2891466675 hasRelatedWork W2073101353 @default.
- W2891466675 hasRelatedWork W3008687060 @default.
- W2891466675 hasRelatedWork W3102188655 @default.
- W2891466675 isParatext "false" @default.
- W2891466675 isRetracted "false" @default.
- W2891466675 magId "2891466675" @default.
- W2891466675 workType "article" @default.