• W2891688657 abstract "In situ micro-(TiCxNy–TiB2)/Ni cermets with different Co and V content (2,5 and 8 wt.%) were successfully fabricated by combustion synthesis and hot press consolidation in Ni–(V/Co)–Ti–B4C–BN systems. The results indicate that as Co content increased from 0 to 8 wt.%, the average sizes of the ceramic particles decreased, when the content of V increased from 0 to 8 wt.%, the size of the ceramic particles first decreased and then increased, and when the V content is 5%, the ceramic particle size is the smallest. The Co element did not participate in the SHS reaction and was a diluent; therefore, when the Co element was added, the combustion temperature continued to decrease. When the V content was no more than 5 wt.%, as the V content increased, the maximum combustion temperature decreased. When the content of V was less than 5 wt.%, the concentration of V was not sufficient to greatly promote the generation of VN. Therefore, V absorbed a large amount of heat during the reaction, resulting in a continuous decrease in the reaction temperature of the reaction system during the reaction. When the content of the added V continued to increase to 8 wt.%, V participated in the reaction, which was exothermic. The results indicate that as Co content increased from 0 to 8 wt.%, the average sizes of the ceramic particles decreased, and the cermets with 5 wt.% Co possessed the best comprehensive properties: the highest hardness (1967 Hv), superior compression strength (3.25 GPa) and higher fracture strain (3.3%). Correspondingly, when the V content was 8 wt.%, the ultimate compressive strength and hardness of the cermets reached 1823 Hv and 3.11 GPa, respectively, 262 Hv and 0.17 GPa higher than those of the unalloyed cermets, respectively. Furthermore, the effects of Co and V on strengthening mechanisms were analyzed." @default.
• W2891688657 created "2018-09-27" @default.
• W2891688657 creator A5022079382 @default.
• W2891688657 creator A5068440603 @default.
• W2891688657 creator A5072379029 @default.
• W2891688657 creator A5077293556 @default.
• W2891688657 creator A5087698403 @default.
• W2891688657 date "2018-09-17" @default.
• W2891688657 modified "2023-10-17" @default.
• W2891688657 title "Effects of V and Co Element Addition on Microstructures and the Mechanical Properties of In Situ Biphasic Hybrid (TiCxNy–TiB2)/Ni Cermets" @default.
• W2891688657 cites W1000418536 @default.
• W2891688657 cites W1168670139 @default.
• W2891688657 cites W1634605609 @default.
• W2891688657 cites W1936142363 @default.
• W2891688657 cites W1965267391 @default.
• W2891688657 cites W1965461542 @default.
• W2891688657 cites W1970388369 @default.
• W2891688657 cites W1979715858 @default.
• W2891688657 cites W1991085315 @default.
• W2891688657 cites W1993396398 @default.
• W2891688657 cites W1996499023 @default.
• W2891688657 cites W2010563483 @default.
• W2891688657 cites W2013758565 @default.
• W2891688657 cites W2018727820 @default.
• W2891688657 cites W2035102081 @default.
• W2891688657 cites W2040154054 @default.
• W2891688657 cites W2046241046 @default.
• W2891688657 cites W2078630159 @default.
• W2891688657 cites W2081569537 @default.
• W2891688657 cites W2091332337 @default.
• W2891688657 cites W2092447681 @default.
• W2891688657 cites W2136653541 @default.
• W2891688657 cites W2150982652 @default.
• W2891688657 cites W2214040863 @default.
• W2891688657 cites W2500959535 @default.
• W2891688657 cites W2510220573 @default.
• W2891688657 cites W2530842518 @default.
• W2891688657 cites W2562786139 @default.
• W2891688657 cites W2586463423 @default.
• W2891688657 cites W2735818533 @default.
• W2891688657 cites W2738782231 @default.
• W2891688657 cites W2739930707 @default.
• W2891688657 cites W2741902758 @default.
• W2891688657 cites W2742177411 @default.
• W2891688657 cites W2766007421 @default.
• W2891688657 cites W2770502796 @default.
• W2891688657 cites W2792015569 @default.
• W2891688657 cites W2794115067 @default.
• W2891688657 cites W2794418383 @default.
• W2891688657 cites W2799863732 @default.
• W2891688657 cites W2807150919 @default.
• W2891688657 cites W286860951 @default.
• W2891688657 cites W2883419067 @default.
• W2891688657 cites W296257371 @default.
• W2891688657 doi "https://doi.org/10.3390/ma11091750" @default.
• W2891688657 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/6163429" @default.
• W2891688657 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/30227661" @default.
• W2891688657 hasPublicationYear "2018" @default.
• W2891688657 type Work @default.
• W2891688657 sameAs 2891688657 @default.
• W2891688657 citedByCount "3" @default.
• W2891688657 countsByYear W28916886572020 @default.
• W2891688657 countsByYear W28916886572022 @default.
• W2891688657 crossrefType "journal-article" @default.
• W2891688657 hasAuthorship W2891688657A5022079382 @default.
• W2891688657 hasAuthorship W2891688657A5068440603 @default.
• W2891688657 hasAuthorship W2891688657A5072379029 @default.
• W2891688657 hasAuthorship W2891688657A5077293556 @default.
• W2891688657 hasAuthorship W2891688657A5087698403 @default.
• W2891688657 hasBestOaLocation W28916886571 @default.
• W2891688657 hasConcept C105923489 @default.
• W2891688657 hasConcept C127413603 @default.
• W2891688657 hasConcept C134132462 @default.
• W2891688657 hasConcept C134646822 @default.
• W2891688657 hasConcept C13965031 @default.
• W2891688657 hasConcept C175804951 @default.
• W2891688657 hasConcept C178790620 @default.
• W2891688657 hasConcept C185592680 @default.
• W2891688657 hasConcept C187530423 @default.
• W2891688657 hasConcept C191897082 @default.
• W2891688657 hasConcept C192562407 @default.
• W2891688657 hasConcept C42360764 @default.
• W2891688657 hasConcept C45119746 @default.
• W2891688657 hasConcept C87976508 @default.
• W2891688657 hasConceptScore W2891688657C105923489 @default.
• W2891688657 hasConceptScore W2891688657C127413603 @default.
• W2891688657 hasConceptScore W2891688657C134132462 @default.
• W2891688657 hasConceptScore W2891688657C134646822 @default.
• W2891688657 hasConceptScore W2891688657C13965031 @default.
• W2891688657 hasConceptScore W2891688657C175804951 @default.
• W2891688657 hasConceptScore W2891688657C178790620 @default.
• W2891688657 hasConceptScore W2891688657C185592680 @default.
• W2891688657 hasConceptScore W2891688657C187530423 @default.
• W2891688657 hasConceptScore W2891688657C191897082 @default.
• W2891688657 hasConceptScore W2891688657C192562407 @default.
• W2891688657 hasConceptScore W2891688657C42360764 @default.
• W2891688657 hasConceptScore W2891688657C45119746 @default.
• W2891688657 hasConceptScore W2891688657C87976508 @default.

• next