- W2891937393 abstract "It was proposed that amorphous alloys may be more resistant to radiation damage than crystalline metals. In crystalline metals neutron induced transmutations lead to the formation of inert gas bubbles. These preferentially nucleate near line defects and result in embrittlement. Amorphous alloys do not contain sites where nucleation can occur preferentially. In this work the growth of argon bubbles in amorphous Cu[50]Zr[50] has been induced by implanting thin specimens with 80keV argon ions at room temperature. The bubble size distribution was obtained over the dose range 5x10[16] to 3x10[17] Ar[+] cm[-2]. Larger bubbles grew in the amorphous alloy than would have been expected to grow in a crystalline metal implanted under the same conditions. It was found that ion bombardment caused surface atoms to be sputtered away from the specimens at a rate of 2.3at.ion[-1]. The sputtering process led to saturation in the amount of argon retained by the material and caused the formation of copper rich near-surface layer. This layer also contained significant amounts of oxygen. Blister formation was induced at the surface of the amorphous alloy by implanting it with 100keV helium ions. At a critical dose of 3x10[17] He[+]cm[-2] a population of very small blisters was formed. These were the result of large bubbles forming just below the specimen surface. As higher doses were used the features joined up to produce large, thin-lidded blisters at a dose of 10[18] He[+] cm[-2]. These observations could not be completely explained in terms of the two popular models of blister formation, where interbubble fracture or lateral stress result in surface deformation." @default.
- W2891937393 created "2018-09-27" @default.
- W2891937393 creator A5007338144 @default.
- W2891937393 date "1987-01-01" @default.
- W2891937393 modified "2023-09-27" @default.
- W2891937393 title "Inert gas implantation of amorphous CuZr." @default.
- W2891937393 hasPublicationYear "1987" @default.
- W2891937393 type Work @default.
- W2891937393 sameAs 2891937393 @default.
- W2891937393 citedByCount "0" @default.
- W2891937393 crossrefType "dissertation" @default.
- W2891937393 hasAuthorship W2891937393A5007338144 @default.
- W2891937393 hasConcept C113196181 @default.
- W2891937393 hasConcept C123266363 @default.
- W2891937393 hasConcept C145148216 @default.
- W2891937393 hasConcept C159985019 @default.
- W2891937393 hasConcept C171250308 @default.
- W2891937393 hasConcept C178790620 @default.
- W2891937393 hasConcept C185592680 @default.
- W2891937393 hasConcept C19067145 @default.
- W2891937393 hasConcept C191897082 @default.
- W2891937393 hasConcept C192562407 @default.
- W2891937393 hasConcept C22423302 @default.
- W2891937393 hasConcept C2779227376 @default.
- W2891937393 hasConcept C2780026712 @default.
- W2891937393 hasConcept C2780949179 @default.
- W2891937393 hasConcept C41823505 @default.
- W2891937393 hasConcept C43617362 @default.
- W2891937393 hasConcept C547737533 @default.
- W2891937393 hasConcept C56052488 @default.
- W2891937393 hasConcept C61048295 @default.
- W2891937393 hasConcept C61427134 @default.
- W2891937393 hasConcept C8010536 @default.
- W2891937393 hasConceptScore W2891937393C113196181 @default.
- W2891937393 hasConceptScore W2891937393C123266363 @default.
- W2891937393 hasConceptScore W2891937393C145148216 @default.
- W2891937393 hasConceptScore W2891937393C159985019 @default.
- W2891937393 hasConceptScore W2891937393C171250308 @default.
- W2891937393 hasConceptScore W2891937393C178790620 @default.
- W2891937393 hasConceptScore W2891937393C185592680 @default.
- W2891937393 hasConceptScore W2891937393C19067145 @default.
- W2891937393 hasConceptScore W2891937393C191897082 @default.
- W2891937393 hasConceptScore W2891937393C192562407 @default.
- W2891937393 hasConceptScore W2891937393C22423302 @default.
- W2891937393 hasConceptScore W2891937393C2779227376 @default.
- W2891937393 hasConceptScore W2891937393C2780026712 @default.
- W2891937393 hasConceptScore W2891937393C2780949179 @default.
- W2891937393 hasConceptScore W2891937393C41823505 @default.
- W2891937393 hasConceptScore W2891937393C43617362 @default.
- W2891937393 hasConceptScore W2891937393C547737533 @default.
- W2891937393 hasConceptScore W2891937393C56052488 @default.
- W2891937393 hasConceptScore W2891937393C61048295 @default.
- W2891937393 hasConceptScore W2891937393C61427134 @default.
- W2891937393 hasConceptScore W2891937393C8010536 @default.
- W2891937393 hasLocation W28919373931 @default.
- W2891937393 hasOpenAccess W2891937393 @default.
- W2891937393 hasPrimaryLocation W28919373931 @default.
- W2891937393 hasRelatedWork W1975696148 @default.
- W2891937393 hasRelatedWork W1997450959 @default.
- W2891937393 hasRelatedWork W2014194003 @default.
- W2891937393 hasRelatedWork W2018382845 @default.
- W2891937393 hasRelatedWork W2028631120 @default.
- W2891937393 hasRelatedWork W2032326986 @default.
- W2891937393 hasRelatedWork W2034347818 @default.
- W2891937393 hasRelatedWork W2040766677 @default.
- W2891937393 hasRelatedWork W2040944240 @default.
- W2891937393 hasRelatedWork W2042167156 @default.
- W2891937393 hasRelatedWork W2056869452 @default.
- W2891937393 hasRelatedWork W2059045823 @default.
- W2891937393 hasRelatedWork W2061163856 @default.
- W2891937393 hasRelatedWork W2075251711 @default.
- W2891937393 hasRelatedWork W2121534495 @default.
- W2891937393 hasRelatedWork W2127197892 @default.
- W2891937393 hasRelatedWork W2172246005 @default.
- W2891937393 hasRelatedWork W2801880809 @default.
- W2891937393 hasRelatedWork W898709438 @default.
- W2891937393 hasRelatedWork W2502611634 @default.
- W2891937393 isParatext "false" @default.
- W2891937393 isRetracted "false" @default.
- W2891937393 magId "2891937393" @default.
- W2891937393 workType "dissertation" @default.