- W2891939297 abstract "In this study, Cr3C2-25NiCr cermet coating samples were prepared by atmospheric plasma spraying (APS) technique on 410 stainless steel substrate with different plasma spraying parameters, namely, the plasma current (500 and 600 A), and the powder feed rate (10 and 30 g/min). The erosion-corrosion behaviour of the coatings was studied by electrochemical measurements, salt spray and erosion-corrosion tests. The electrochemical tests were performed in 3.5 wt.% NaCl solution. During the erosion-corrosion test, the samples were immersed in 3.5 wt.% NaCl solution containing 0.25 wt.% SiO2 particles with a rotational speed of 950 rpm for 72 hours. The obtained results showed that the plasma sprayed coating sample at the plasma current of 600 A and the powder feed rate of 10 g/min has a best erosion-corrosion resistance. Red rust spots did not appear on surface of this coating after 120 hours of salt spray test. It was much slower than on the others (after only 24 hours salt spray test). The weight loss of this coating during the erosion-corrosion test was lower than the remaining samples. These results are consistent with the results of electrochemical tests." @default.
- W2891939297 created "2018-09-27" @default.
- W2891939297 creator A5003055898 @default.
- W2891939297 creator A5005647395 @default.
- W2891939297 creator A5019367099 @default.
- W2891939297 creator A5034706095 @default.
- W2891939297 creator A5051415663 @default.
- W2891939297 creator A5078863667 @default.
- W2891939297 creator A5085318333 @default.
- W2891939297 date "2018-09-13" @default.
- W2891939297 modified "2023-09-26" @default.
- W2891939297 title "A STUDY ON EROSION AND CORROSION BEHAVIOR OF Cr3C2-NiCr CERMET COATINGS" @default.
- W2891939297 doi "https://doi.org/10.15625/2525-2518/56/3b/12785" @default.
- W2891939297 hasPublicationYear "2018" @default.
- W2891939297 type Work @default.
- W2891939297 sameAs 2891939297 @default.
- W2891939297 citedByCount "5" @default.
- W2891939297 countsByYear W28919392972020 @default.
- W2891939297 countsByYear W28919392972021 @default.
- W2891939297 countsByYear W28919392972022 @default.
- W2891939297 crossrefType "journal-article" @default.
- W2891939297 hasAuthorship W2891939297A5003055898 @default.
- W2891939297 hasAuthorship W2891939297A5005647395 @default.
- W2891939297 hasAuthorship W2891939297A5019367099 @default.
- W2891939297 hasAuthorship W2891939297A5034706095 @default.
- W2891939297 hasAuthorship W2891939297A5051415663 @default.
- W2891939297 hasAuthorship W2891939297A5078863667 @default.
- W2891939297 hasAuthorship W2891939297A5085318333 @default.
- W2891939297 hasBestOaLocation W28919392971 @default.
- W2891939297 hasConcept C106303946 @default.
- W2891939297 hasConcept C134132462 @default.
- W2891939297 hasConcept C134646822 @default.
- W2891939297 hasConcept C140086010 @default.
- W2891939297 hasConcept C147789679 @default.
- W2891939297 hasConcept C149669645 @default.
- W2891939297 hasConcept C159985019 @default.
- W2891939297 hasConcept C17525397 @default.
- W2891939297 hasConcept C185592680 @default.
- W2891939297 hasConcept C191897082 @default.
- W2891939297 hasConcept C192562407 @default.
- W2891939297 hasConcept C20625102 @default.
- W2891939297 hasConcept C2777514341 @default.
- W2891939297 hasConcept C2781448156 @default.
- W2891939297 hasConcept C52859227 @default.
- W2891939297 hasConceptScore W2891939297C106303946 @default.
- W2891939297 hasConceptScore W2891939297C134132462 @default.
- W2891939297 hasConceptScore W2891939297C134646822 @default.
- W2891939297 hasConceptScore W2891939297C140086010 @default.
- W2891939297 hasConceptScore W2891939297C147789679 @default.
- W2891939297 hasConceptScore W2891939297C149669645 @default.
- W2891939297 hasConceptScore W2891939297C159985019 @default.
- W2891939297 hasConceptScore W2891939297C17525397 @default.
- W2891939297 hasConceptScore W2891939297C185592680 @default.
- W2891939297 hasConceptScore W2891939297C191897082 @default.
- W2891939297 hasConceptScore W2891939297C192562407 @default.
- W2891939297 hasConceptScore W2891939297C20625102 @default.
- W2891939297 hasConceptScore W2891939297C2777514341 @default.
- W2891939297 hasConceptScore W2891939297C2781448156 @default.
- W2891939297 hasConceptScore W2891939297C52859227 @default.
- W2891939297 hasIssue "3B" @default.
- W2891939297 hasLocation W28919392971 @default.
- W2891939297 hasOpenAccess W2891939297 @default.
- W2891939297 hasPrimaryLocation W28919392971 @default.
- W2891939297 hasRelatedWork W2044090191 @default.
- W2891939297 hasRelatedWork W2172234767 @default.
- W2891939297 hasRelatedWork W2353619313 @default.
- W2891939297 hasRelatedWork W2353793576 @default.
- W2891939297 hasRelatedWork W2384814742 @default.
- W2891939297 hasRelatedWork W244089715 @default.
- W2891939297 hasRelatedWork W2891939297 @default.
- W2891939297 hasRelatedWork W3007505409 @default.
- W2891939297 hasRelatedWork W3097783663 @default.
- W2891939297 hasRelatedWork W4299600895 @default.
- W2891939297 hasVolume "56" @default.
- W2891939297 isParatext "false" @default.
- W2891939297 isRetracted "false" @default.
- W2891939297 magId "2891939297" @default.
- W2891939297 workType "article" @default.