- W2892731680 abstract "In the present study, micro-milling of aluminium 6061 alloy and copper was undertaken. TiAlN coated two-flute flat end milling cutters of 0.5 mm diameter were used for conducting micro-channel milling experiments with minimum quantity lubrication (MQL) as the cutting environment. The effect of process parameters namely cutting velocity (vc) and feed per flute (fz) on the cutting forces, surface roughness and burr width are reported. RMS values of longitudinal feed force (FX), transverse cutting force (FY) and vertical thrust force (FZ) were measured and the maximum values for Al 6061 are 0.33 N, 0.16 N and 0.21 N respectively, and the same for copper are measured to be 0.11 N, 0.17 N and 0.22 N respectively. Average surface roughness along the milling direction (Ra) at the bottom surface of the micro-channel was measured. Smoother surfaces were generated at lower feed per flute in both the materials. Ra is found to be varying from 28.2 nm to 86.9 nm for Al 6061, and for copper, the range is from 4.9 nm to 32.7 nm. SEM images of the micro-channels were analysed and top burr width was measured in both up-milling and down-milling directions. Higher feed per flute produced smaller burrs in both up-milling and down-milling directions. Maximum burr width for Al 6061 is measured to be 12.86 μm and 15.28 μm in up-milling and down-milling direction respectively, and for copper, the same are measured to be 12.84 μm and 20.46 μm respectively." @default.
- W2892731680 created "2018-10-05" @default.
- W2892731680 creator A5040503693 @default.
- W2892731680 creator A5051405905 @default.
- W2892731680 creator A5084660848 @default.
- W2892731680 date "2018-06-18" @default.
- W2892731680 modified "2023-10-17" @default.
- W2892731680 title "A Study on Micro-Milling of Aluminium 6061 and Copper With Respect to Cutting Forces, Surface Roughness and Burr Formation" @default.
- W2892731680 doi "https://doi.org/10.1115/msec2018-6570" @default.
- W2892731680 hasPublicationYear "2018" @default.
- W2892731680 type Work @default.
- W2892731680 sameAs 2892731680 @default.
- W2892731680 citedByCount "1" @default.
- W2892731680 countsByYear W28927316802019 @default.
- W2892731680 crossrefType "proceedings-article" @default.
- W2892731680 hasAuthorship W2892731680A5040503693 @default.
- W2892731680 hasAuthorship W2892731680A5051405905 @default.
- W2892731680 hasAuthorship W2892731680A5084660848 @default.
- W2892731680 hasConcept C107365816 @default.
- W2892731680 hasConcept C159985019 @default.
- W2892731680 hasConcept C191897082 @default.
- W2892731680 hasConcept C192562407 @default.
- W2892731680 hasConcept C2780026712 @default.
- W2892731680 hasConcept C2780033417 @default.
- W2892731680 hasConcept C513153333 @default.
- W2892731680 hasConcept C523214423 @default.
- W2892731680 hasConcept C544778455 @default.
- W2892731680 hasConcept C71039073 @default.
- W2892731680 hasConceptScore W2892731680C107365816 @default.
- W2892731680 hasConceptScore W2892731680C159985019 @default.
- W2892731680 hasConceptScore W2892731680C191897082 @default.
- W2892731680 hasConceptScore W2892731680C192562407 @default.
- W2892731680 hasConceptScore W2892731680C2780026712 @default.
- W2892731680 hasConceptScore W2892731680C2780033417 @default.
- W2892731680 hasConceptScore W2892731680C513153333 @default.
- W2892731680 hasConceptScore W2892731680C523214423 @default.
- W2892731680 hasConceptScore W2892731680C544778455 @default.
- W2892731680 hasConceptScore W2892731680C71039073 @default.
- W2892731680 hasLocation W28927316801 @default.
- W2892731680 hasOpenAccess W2892731680 @default.
- W2892731680 hasPrimaryLocation W28927316801 @default.
- W2892731680 hasRelatedWork W1133291142 @default.
- W2892731680 hasRelatedWork W12917432 @default.
- W2892731680 hasRelatedWork W129373164 @default.
- W2892731680 hasRelatedWork W1365056 @default.
- W2892731680 hasRelatedWork W2039859539 @default.
- W2892731680 hasRelatedWork W2066755951 @default.
- W2892731680 hasRelatedWork W2082515351 @default.
- W2892731680 hasRelatedWork W2488861322 @default.
- W2892731680 hasRelatedWork W2626341897 @default.
- W2892731680 hasRelatedWork W2481981524 @default.
- W2892731680 isParatext "false" @default.
- W2892731680 isRetracted "false" @default.
- W2892731680 magId "2892731680" @default.
- W2892731680 workType "article" @default.