- W2893212003 abstract "In this study we demonstrate a new method for depositing thick reactive multilayer films (RMFs) (thickness > 14 μm) by using Ti interlayer integration and substrate preheating during fabrication. These two adjustments are designed to alleviate internal planar stresses that cause delamination between deposited layers and peeling off the substrate. Decreasing the distance between Ti interlayers helps to eliminate delamination between deposited layers. Through high speed camera measurements, the reaction propagation speed of an RMF sample with preheating is 42% slower than the same RMF that was not preheated, indicating a slower heat release rate. The preliminary experiments on brazing Ti-6Al-4V coated with BAlSi-4 brazing material revealed dendritic structure branching out from the RMF surface into the brazing material. The dendrite structures most likely form because of rapid melting and solidification of the brazing material. However, this rapid melting and solidification cycle does not appear to occur uniformly across the BAlSi-4RMF interface which is linked to its low bonding strength. When the Ti-6Al-4V substrate is heated to 150 °C prior to ignition, the strength increases to 0.47 MPa when the total RMF thickness is 84 μm and 15 MPa of pressure is applied." @default.
- W2893212003 created "2018-10-05" @default.
- W2893212003 creator A5011457149 @default.
- W2893212003 creator A5024082679 @default.
- W2893212003 creator A5039534428 @default.
- W2893212003 creator A5040733858 @default.
- W2893212003 creator A5076887431 @default.
- W2893212003 creator A5080679080 @default.
- W2893212003 creator A5082766305 @default.
- W2893212003 creator A5084637102 @default.
- W2893212003 creator A5085279559 @default.
- W2893212003 creator A5090639230 @default.
- W2893212003 date "2018-06-18" @default.
- W2893212003 modified "2023-10-03" @default.
- W2893212003 title "Preparation of Thick Ni/Al Reactive Multilayer Films and Prospective Use for Self-Powered Brazing of Ti-6Al-4V" @default.
- W2893212003 doi "https://doi.org/10.1115/msec2018-6627" @default.
- W2893212003 hasPublicationYear "2018" @default.
- W2893212003 type Work @default.
- W2893212003 sameAs 2893212003 @default.
- W2893212003 citedByCount "0" @default.
- W2893212003 crossrefType "proceedings-article" @default.
- W2893212003 hasAuthorship W2893212003A5011457149 @default.
- W2893212003 hasAuthorship W2893212003A5024082679 @default.
- W2893212003 hasAuthorship W2893212003A5039534428 @default.
- W2893212003 hasAuthorship W2893212003A5040733858 @default.
- W2893212003 hasAuthorship W2893212003A5076887431 @default.
- W2893212003 hasAuthorship W2893212003A5080679080 @default.
- W2893212003 hasAuthorship W2893212003A5082766305 @default.
- W2893212003 hasAuthorship W2893212003A5084637102 @default.
- W2893212003 hasAuthorship W2893212003A5085279559 @default.
- W2893212003 hasAuthorship W2893212003A5090639230 @default.
- W2893212003 hasConcept C159985019 @default.
- W2893212003 hasConcept C191897082 @default.
- W2893212003 hasConcept C192562407 @default.
- W2893212003 hasConcept C2780026712 @default.
- W2893212003 hasConcept C86171150 @default.
- W2893212003 hasConceptScore W2893212003C159985019 @default.
- W2893212003 hasConceptScore W2893212003C191897082 @default.
- W2893212003 hasConceptScore W2893212003C192562407 @default.
- W2893212003 hasConceptScore W2893212003C2780026712 @default.
- W2893212003 hasConceptScore W2893212003C86171150 @default.
- W2893212003 hasLocation W28932120031 @default.
- W2893212003 hasOpenAccess W2893212003 @default.
- W2893212003 hasPrimaryLocation W28932120031 @default.
- W2893212003 hasRelatedWork W1989948324 @default.
- W2893212003 hasRelatedWork W1995130985 @default.
- W2893212003 hasRelatedWork W2005145549 @default.
- W2893212003 hasRelatedWork W2037607514 @default.
- W2893212003 hasRelatedWork W2349258142 @default.
- W2893212003 hasRelatedWork W2353489384 @default.
- W2893212003 hasRelatedWork W2359836145 @default.
- W2893212003 hasRelatedWork W2361032053 @default.
- W2893212003 hasRelatedWork W2377911134 @default.
- W2893212003 hasRelatedWork W2476123354 @default.
- W2893212003 hasRelatedWork W2520389091 @default.
- W2893212003 hasRelatedWork W2545668507 @default.
- W2893212003 hasRelatedWork W2808063196 @default.
- W2893212003 hasRelatedWork W3109085028 @default.
- W2893212003 hasRelatedWork W2611690045 @default.
- W2893212003 hasRelatedWork W2818484523 @default.
- W2893212003 hasRelatedWork W2825805717 @default.
- W2893212003 hasRelatedWork W2832522549 @default.
- W2893212003 hasRelatedWork W2958982725 @default.
- W2893212003 hasRelatedWork W2978307675 @default.
- W2893212003 isParatext "false" @default.
- W2893212003 isRetracted "false" @default.
- W2893212003 magId "2893212003" @default.
- W2893212003 workType "article" @default.