- W2893280741 abstract "Most materials for offshore applications are tested for brittle fracture resistance at a single temperature related to the minimum design temperature and by a single fracture test method. It is much rarer to perform tests at multiple temperatures to compare the fracture performance across a range of temperatures and testing methods. EWI recently compared the fracture toughness transition behaviors for an X70 steel pipe across Charpy V-notch (CVN), single-edge notched bending (SENB) crack-tip open displacement (CTOD), and single-edge notched tension (SENT) CTOD test geometries. This showed variability of the material behavior better described by the inhomogeneous behavior models considered for welded joints. It also suggested the possibility that near the ductile-to-brittle transition temperature, the toughness under SENT CTOD may be higher than for SENB CTOD testing where the failure mode is brittle fracture. The testing methods used full-size CVN and nearly full-thickness CTOD specimens in bending, as limited by the pipe curvature of the 219-mm diameter pipe with 35.4-mm wall thickness. The SENT CTOD specimens were pre-cracked in bending with the same dimensions as the SENB specimens, but are then cut down to place the pre-cracked crack tip at approximately one quarter of the thickness through the resulting specimen. This modification places the tip in the higher constraint region for the tension test. Girth welds in the same X70 pipe were prepared using a pulsed GMAW process with ER80S-D2 welding wire. Similar testing was performed with weld centerline notches for the CVN and CTOD specimens. The transition behavior was related between the three testing methods for the weld centerline at the mid-wall of the pipe thickness. Using representative values equivalent to the minimum of three tests, the SENT values were 4.8 to 4.9 times the values for the SENB tests." @default.
- W2893280741 created "2018-10-05" @default.
- W2893280741 creator A5074749542 @default.
- W2893280741 creator A5090550974 @default.
- W2893280741 date "2018-06-17" @default.
- W2893280741 modified "2023-09-25" @default.
- W2893280741 title "Comparing Fracture Toughness Transition Curves for Girth Welds in X70 Pipe" @default.
- W2893280741 doi "https://doi.org/10.1115/omae2018-78147" @default.
- W2893280741 hasPublicationYear "2018" @default.
- W2893280741 type Work @default.
- W2893280741 sameAs 2893280741 @default.
- W2893280741 citedByCount "0" @default.
- W2893280741 crossrefType "proceedings-article" @default.
- W2893280741 hasAuthorship W2893280741A5074749542 @default.
- W2893280741 hasAuthorship W2893280741A5090550974 @default.
- W2893280741 hasConcept C114614502 @default.
- W2893280741 hasConcept C127413603 @default.
- W2893280741 hasConcept C159985019 @default.
- W2893280741 hasConcept C192562407 @default.
- W2893280741 hasConcept C2777434295 @default.
- W2893280741 hasConcept C33923547 @default.
- W2893280741 hasConcept C43369102 @default.
- W2893280741 hasConcept C77595967 @default.
- W2893280741 hasConcept C97549433 @default.
- W2893280741 hasConcept C99595764 @default.
- W2893280741 hasConceptScore W2893280741C114614502 @default.
- W2893280741 hasConceptScore W2893280741C127413603 @default.
- W2893280741 hasConceptScore W2893280741C159985019 @default.
- W2893280741 hasConceptScore W2893280741C192562407 @default.
- W2893280741 hasConceptScore W2893280741C2777434295 @default.
- W2893280741 hasConceptScore W2893280741C33923547 @default.
- W2893280741 hasConceptScore W2893280741C43369102 @default.
- W2893280741 hasConceptScore W2893280741C77595967 @default.
- W2893280741 hasConceptScore W2893280741C97549433 @default.
- W2893280741 hasConceptScore W2893280741C99595764 @default.
- W2893280741 hasLocation W28932807411 @default.
- W2893280741 hasOpenAccess W2893280741 @default.
- W2893280741 hasPrimaryLocation W28932807411 @default.
- W2893280741 hasRelatedWork W1520140677 @default.
- W2893280741 hasRelatedWork W1622776839 @default.
- W2893280741 hasRelatedWork W1794962021 @default.
- W2893280741 hasRelatedWork W1845126375 @default.
- W2893280741 hasRelatedWork W1969563193 @default.
- W2893280741 hasRelatedWork W2033991299 @default.
- W2893280741 hasRelatedWork W2195610545 @default.
- W2893280741 hasRelatedWork W2359429082 @default.
- W2893280741 hasRelatedWork W2537294544 @default.
- W2893280741 hasRelatedWork W2554651267 @default.
- W2893280741 hasRelatedWork W2584333009 @default.
- W2893280741 hasRelatedWork W2591166585 @default.
- W2893280741 hasRelatedWork W2617655086 @default.
- W2893280741 hasRelatedWork W2790056933 @default.
- W2893280741 hasRelatedWork W2899576675 @default.
- W2893280741 hasRelatedWork W2990417123 @default.
- W2893280741 hasRelatedWork W3016067900 @default.
- W2893280741 hasRelatedWork W573512777 @default.
- W2893280741 hasRelatedWork W587560446 @default.
- W2893280741 hasRelatedWork W1565284869 @default.
- W2893280741 isParatext "false" @default.
- W2893280741 isRetracted "false" @default.
- W2893280741 magId "2893280741" @default.
- W2893280741 workType "article" @default.