- W2894121649 abstract "A fine grained Ti(C, N) cermet tool material was prepared by two-step spark plasma sintering. Microstructure evolution and densification mechanisms of Ti(C, N) during spark plasma sintering were studied. Effect of two-step sintering process and Ni content on microstructure and mechanical properties were also investigated. The critical activated densification temperature of Ti(C, N) is about 1300 ℃, and the rapidest densification rate takes place at 1300 ℃~1400 ℃. Grains are in the size of 1 µm when the Ti(C, N) cermet was prepared by two-step spark plasma sintering. The optimal flexural strength, fracture toughness and Vickers hardness are 1094 ± 42 MPa, 7.2 ± 0.5 MPa m1/2 and 18.3 ± 0.4 GPa, respectively. The Ti(C, N) cermets containing more content of Ni have higher toughness, which is due to the remarkable toughening effect of crack bridging by large grains." @default.
- W2894121649 created "2018-10-05" @default.
- W2894121649 creator A5009789631 @default.
- W2894121649 creator A5029021551 @default.
- W2894121649 creator A5034806491 @default.
- W2894121649 creator A5036233074 @default.
- W2894121649 creator A5052506541 @default.
- W2894121649 creator A5055069263 @default.
- W2894121649 date "2019-01-01" @default.
- W2894121649 modified "2023-10-14" @default.
- W2894121649 title "Improvement in microstructure and mechanical properties of Ti(C, N) cermet prepared by two-step spark plasma sintering" @default.
- W2894121649 cites W146482523 @default.
- W2894121649 cites W1841168719 @default.
- W2894121649 cites W1982782227 @default.
- W2894121649 cites W1995127628 @default.
- W2894121649 cites W2011015540 @default.
- W2894121649 cites W2020799431 @default.
- W2894121649 cites W2022479570 @default.
- W2894121649 cites W2107182943 @default.
- W2894121649 cites W2122972324 @default.
- W2894121649 cites W2125913371 @default.
- W2894121649 cites W2136653541 @default.
- W2894121649 cites W2274581081 @default.
- W2894121649 cites W2378567826 @default.
- W2894121649 cites W2519633453 @default.
- W2894121649 cites W2523162392 @default.
- W2894121649 cites W2527769841 @default.
- W2894121649 cites W2529527931 @default.
- W2894121649 cites W2560960989 @default.
- W2894121649 cites W2592859450 @default.
- W2894121649 cites W2595650588 @default.
- W2894121649 cites W2601804284 @default.
- W2894121649 cites W2607361258 @default.
- W2894121649 cites W2735664911 @default.
- W2894121649 cites W2737908138 @default.
- W2894121649 cites W2743906206 @default.
- W2894121649 cites W2769761108 @default.
- W2894121649 cites W2793454994 @default.
- W2894121649 cites W2793626501 @default.
- W2894121649 cites W2807966445 @default.
- W2894121649 cites W4211191043 @default.
- W2894121649 cites W620476111 @default.
- W2894121649 cites W639558604 @default.
- W2894121649 doi "https://doi.org/10.1016/j.ceramint.2018.09.241" @default.
- W2894121649 hasPublicationYear "2019" @default.
- W2894121649 type Work @default.
- W2894121649 sameAs 2894121649 @default.
- W2894121649 citedByCount "15" @default.
- W2894121649 countsByYear W28941216492019 @default.
- W2894121649 countsByYear W28941216492020 @default.
- W2894121649 countsByYear W28941216492021 @default.
- W2894121649 countsByYear W28941216492022 @default.
- W2894121649 countsByYear W28941216492023 @default.
- W2894121649 crossrefType "journal-article" @default.
- W2894121649 hasAuthorship W2894121649A5009789631 @default.
- W2894121649 hasAuthorship W2894121649A5029021551 @default.
- W2894121649 hasAuthorship W2894121649A5034806491 @default.
- W2894121649 hasAuthorship W2894121649A5036233074 @default.
- W2894121649 hasAuthorship W2894121649A5052506541 @default.
- W2894121649 hasAuthorship W2894121649A5055069263 @default.
- W2894121649 hasConcept C133392424 @default.
- W2894121649 hasConcept C134132462 @default.
- W2894121649 hasConcept C134646822 @default.
- W2894121649 hasConcept C159985019 @default.
- W2894121649 hasConcept C178405089 @default.
- W2894121649 hasConcept C191897082 @default.
- W2894121649 hasConcept C192562407 @default.
- W2894121649 hasConcept C2776014600 @default.
- W2894121649 hasConcept C2777581544 @default.
- W2894121649 hasConcept C87976508 @default.
- W2894121649 hasConcept C97549433 @default.
- W2894121649 hasConcept C99595764 @default.
- W2894121649 hasConceptScore W2894121649C133392424 @default.
- W2894121649 hasConceptScore W2894121649C134132462 @default.
- W2894121649 hasConceptScore W2894121649C134646822 @default.
- W2894121649 hasConceptScore W2894121649C159985019 @default.
- W2894121649 hasConceptScore W2894121649C178405089 @default.
- W2894121649 hasConceptScore W2894121649C191897082 @default.
- W2894121649 hasConceptScore W2894121649C192562407 @default.
- W2894121649 hasConceptScore W2894121649C2776014600 @default.
- W2894121649 hasConceptScore W2894121649C2777581544 @default.
- W2894121649 hasConceptScore W2894121649C87976508 @default.
- W2894121649 hasConceptScore W2894121649C97549433 @default.
- W2894121649 hasConceptScore W2894121649C99595764 @default.
- W2894121649 hasFunder F4320321001 @default.
- W2894121649 hasFunder F4320322769 @default.
- W2894121649 hasFunder F4320335787 @default.
- W2894121649 hasIssue "1" @default.
- W2894121649 hasLocation W28941216491 @default.
- W2894121649 hasOpenAccess W2894121649 @default.
- W2894121649 hasPrimaryLocation W28941216491 @default.
- W2894121649 hasRelatedWork W1965024206 @default.
- W2894121649 hasRelatedWork W2086627128 @default.
- W2894121649 hasRelatedWork W2087582432 @default.
- W2894121649 hasRelatedWork W2363152197 @default.
- W2894121649 hasRelatedWork W2383592386 @default.
- W2894121649 hasRelatedWork W2789571739 @default.
- W2894121649 hasRelatedWork W2902107089 @default.