- W2894640649 abstract "The study reveals the effect of Mn and Mg content on mechanical and technological properties during the bending of thin sheets of aluminum alloy 3005. For experimental research the ingots were cast through an out-of-furnace refining unit, homogenized at a temperature of 590°C, during 6 hours. Further ingots were hot rolled to a thickness of 3.5 mm and subsequently cold rolled into sheets of thickness 0.33 and 0.25 mm. Annealing of rolls was provided at temperatures 230...285°C for 1.5 hour in air-circulation annealing furnaces with a protective atmosphere and on a continuous heat treatment line. The change in the tensile strength, yield stress, elongation as a dependence on the content of alloying elements and annealing modes was shown. Technological properties were evaluated by performing bend tests. It has been established that an increased content of magnesium and manganese in the AA3005 alloy results in lower values of the elongation for all annealing temperatures. Annealing in the air-circulation annealing furnaces resulted to higher plasticity values and lower values of strength compared to annealing at continuous heat treatment line for all annealing temperatures and magnesium and manganese temperatures. The plasticity of samples 0.25 mm thick raises evenly throughout the annealing temperature range. For specimens 0.33 mm thick, the effect of the magnesium and manganese content, as well as the type of heat-treatment equipment on the samples’ plasticity during annealing is more pronounced than for samples 0.25 mm thick. In sheet samples from the AA3005 alloy annealed on continuous heat treatment line, with an increased content of magnesium and manganese, cracks are observed at the inflection point for both thicknesses. When annealing in air-circulation annealing furnaces, cracks are not observed for both increased and reduced magnesium and manganese content." @default.
- W2894640649 created "2018-10-12" @default.
- W2894640649 creator A5001404179 @default.
- W2894640649 creator A5061787904 @default.
- W2894640649 creator A5070752847 @default.
- W2894640649 date "2018-10-01" @default.
- W2894640649 modified "2023-09-27" @default.
- W2894640649 title "Effect of Manganese and Magnesium Content and Conditions of Annealing on Mechanical Properties and Cracking Formation during Bending of Aluminum Alloy AA3005" @default.
- W2894640649 cites W1965665368 @default.
- W2894640649 cites W1996358198 @default.
- W2894640649 cites W2013878321 @default.
- W2894640649 cites W2029156908 @default.
- W2894640649 cites W2089289981 @default.
- W2894640649 cites W2132258713 @default.
- W2894640649 cites W2341704603 @default.
- W2894640649 cites W2470127752 @default.
- W2894640649 cites W2605826498 @default.
- W2894640649 cites W2625109959 @default.
- W2894640649 cites W2743168213 @default.
- W2894640649 cites W2761388623 @default.
- W2894640649 cites W2767718836 @default.
- W2894640649 doi "https://doi.org/10.4028/www.scientific.net/ssp.284.476" @default.
- W2894640649 hasPublicationYear "2018" @default.
- W2894640649 type Work @default.
- W2894640649 sameAs 2894640649 @default.
- W2894640649 citedByCount "0" @default.
- W2894640649 crossrefType "journal-article" @default.
- W2894640649 hasAuthorship W2894640649A5001404179 @default.
- W2894640649 hasAuthorship W2894640649A5061787904 @default.
- W2894640649 hasAuthorship W2894640649A5070752847 @default.
- W2894640649 hasConcept C159985019 @default.
- W2894640649 hasConcept C191897082 @default.
- W2894640649 hasConcept C192562407 @default.
- W2894640649 hasConcept C2777855556 @default.
- W2894640649 hasConcept C2780026712 @default.
- W2894640649 hasConcept C513153333 @default.
- W2894640649 hasConcept C528890316 @default.
- W2894640649 hasConcept C543218039 @default.
- W2894640649 hasConcept C58396970 @default.
- W2894640649 hasConcept C87210426 @default.
- W2894640649 hasConceptScore W2894640649C159985019 @default.
- W2894640649 hasConceptScore W2894640649C191897082 @default.
- W2894640649 hasConceptScore W2894640649C192562407 @default.
- W2894640649 hasConceptScore W2894640649C2777855556 @default.
- W2894640649 hasConceptScore W2894640649C2780026712 @default.
- W2894640649 hasConceptScore W2894640649C513153333 @default.
- W2894640649 hasConceptScore W2894640649C528890316 @default.
- W2894640649 hasConceptScore W2894640649C543218039 @default.
- W2894640649 hasConceptScore W2894640649C58396970 @default.
- W2894640649 hasConceptScore W2894640649C87210426 @default.
- W2894640649 hasLocation W28946406491 @default.
- W2894640649 hasOpenAccess W2894640649 @default.
- W2894640649 hasPrimaryLocation W28946406491 @default.
- W2894640649 hasRelatedWork W162430308 @default.
- W2894640649 hasRelatedWork W1964533477 @default.
- W2894640649 hasRelatedWork W2005436806 @default.
- W2894640649 hasRelatedWork W2035275117 @default.
- W2894640649 hasRelatedWork W2056011122 @default.
- W2894640649 hasRelatedWork W2079988792 @default.
- W2894640649 hasRelatedWork W2089461902 @default.
- W2894640649 hasRelatedWork W2104483681 @default.
- W2894640649 hasRelatedWork W2141863061 @default.
- W2894640649 hasRelatedWork W2349988324 @default.
- W2894640649 hasRelatedWork W2361750904 @default.
- W2894640649 hasRelatedWork W2391359103 @default.
- W2894640649 hasRelatedWork W2606024948 @default.
- W2894640649 hasRelatedWork W2793415380 @default.
- W2894640649 hasRelatedWork W2903741364 @default.
- W2894640649 hasRelatedWork W2955938799 @default.
- W2894640649 hasRelatedWork W2988157579 @default.
- W2894640649 hasRelatedWork W3107167230 @default.
- W2894640649 hasRelatedWork W3128770494 @default.
- W2894640649 hasRelatedWork W2849540326 @default.
- W2894640649 isParatext "false" @default.
- W2894640649 isRetracted "false" @default.
- W2894640649 magId "2894640649" @default.
- W2894640649 workType "article" @default.