- W2896040303 abstract "In order to suppress the formation of intermetallic compounds, the welding-brazing of aluminum to steel was realized by fiber laser. The interfacial microstructure of the joints was analyzed by OM, SEM, EDS and XRD. The results showed that two kinds of intermetallic compounds were formed along the interface. One is Fe2Al5, strip like, close to the steel side. The other is FeAl3, needle like, close to the aluminum base material. The thickness of the formed intermetallic compounds layer increased with heat input increasing and decreased with the defocus amount increasing. With the increase of heat input, the loading ability of the joints increased firstly and then decreased. Under the given welding heat input condition, a higher loading ability could be obtained at a larger defocus amount, the biggest value reached 58N/mm under the laser output power of 3500W, welding speed of 20mm/s and a defocus amount of 40mm.In order to suppress the formation of intermetallic compounds, the welding-brazing of aluminum to steel was realized by fiber laser. The interfacial microstructure of the joints was analyzed by OM, SEM, EDS and XRD. The results showed that two kinds of intermetallic compounds were formed along the interface. One is Fe2Al5, strip like, close to the steel side. The other is FeAl3, needle like, close to the aluminum base material. The thickness of the formed intermetallic compounds layer increased with heat input increasing and decreased with the defocus amount increasing. With the increase of heat input, the loading ability of the joints increased firstly and then decreased. Under the given welding heat input condition, a higher loading ability could be obtained at a larger defocus amount, the biggest value reached 58N/mm under the laser output power of 3500W, welding speed of 20mm/s and a defocus amount of 40mm." @default.
- W2896040303 created "2018-10-26" @default.
- W2896040303 creator A5004957541 @default.
- W2896040303 creator A5073562923 @default.
- W2896040303 creator A5083148043 @default.
- W2896040303 date "2014-01-01" @default.
- W2896040303 modified "2023-09-28" @default.
- W2896040303 title "Laser welding-brazing joint for aluminum/steel dissimilar metals" @default.
- W2896040303 doi "https://doi.org/10.2351/1.5063040" @default.
- W2896040303 hasPublicationYear "2014" @default.
- W2896040303 type Work @default.
- W2896040303 sameAs 2896040303 @default.
- W2896040303 citedByCount "0" @default.
- W2896040303 crossrefType "proceedings-article" @default.
- W2896040303 hasAuthorship W2896040303A5004957541 @default.
- W2896040303 hasAuthorship W2896040303A5073562923 @default.
- W2896040303 hasAuthorship W2896040303A5083148043 @default.
- W2896040303 hasConcept C120665830 @default.
- W2896040303 hasConcept C121332964 @default.
- W2896040303 hasConcept C127413603 @default.
- W2896040303 hasConcept C146868986 @default.
- W2896040303 hasConcept C159985019 @default.
- W2896040303 hasConcept C18555067 @default.
- W2896040303 hasConcept C191897082 @default.
- W2896040303 hasConcept C192562407 @default.
- W2896040303 hasConcept C19474535 @default.
- W2896040303 hasConcept C27501479 @default.
- W2896040303 hasConcept C2779227376 @default.
- W2896040303 hasConcept C2780026712 @default.
- W2896040303 hasConcept C513153333 @default.
- W2896040303 hasConcept C520434653 @default.
- W2896040303 hasConcept C66938386 @default.
- W2896040303 hasConcept C86171150 @default.
- W2896040303 hasConcept C87976508 @default.
- W2896040303 hasConcept C89344249 @default.
- W2896040303 hasConceptScore W2896040303C120665830 @default.
- W2896040303 hasConceptScore W2896040303C121332964 @default.
- W2896040303 hasConceptScore W2896040303C127413603 @default.
- W2896040303 hasConceptScore W2896040303C146868986 @default.
- W2896040303 hasConceptScore W2896040303C159985019 @default.
- W2896040303 hasConceptScore W2896040303C18555067 @default.
- W2896040303 hasConceptScore W2896040303C191897082 @default.
- W2896040303 hasConceptScore W2896040303C192562407 @default.
- W2896040303 hasConceptScore W2896040303C19474535 @default.
- W2896040303 hasConceptScore W2896040303C27501479 @default.
- W2896040303 hasConceptScore W2896040303C2779227376 @default.
- W2896040303 hasConceptScore W2896040303C2780026712 @default.
- W2896040303 hasConceptScore W2896040303C513153333 @default.
- W2896040303 hasConceptScore W2896040303C520434653 @default.
- W2896040303 hasConceptScore W2896040303C66938386 @default.
- W2896040303 hasConceptScore W2896040303C86171150 @default.
- W2896040303 hasConceptScore W2896040303C87976508 @default.
- W2896040303 hasConceptScore W2896040303C89344249 @default.
- W2896040303 hasLocation W28960403031 @default.
- W2896040303 hasOpenAccess W2896040303 @default.
- W2896040303 hasPrimaryLocation W28960403031 @default.
- W2896040303 hasRelatedWork W1978334134 @default.
- W2896040303 hasRelatedWork W2032649819 @default.
- W2896040303 hasRelatedWork W2172430649 @default.
- W2896040303 hasRelatedWork W2180339497 @default.
- W2896040303 hasRelatedWork W2256819854 @default.
- W2896040303 hasRelatedWork W2281511177 @default.
- W2896040303 hasRelatedWork W2354865234 @default.
- W2896040303 hasRelatedWork W2368799101 @default.
- W2896040303 hasRelatedWork W2370090133 @default.
- W2896040303 hasRelatedWork W2389015403 @default.
- W2896040303 hasRelatedWork W2393785988 @default.
- W2896040303 hasRelatedWork W2531076410 @default.
- W2896040303 hasRelatedWork W2566976653 @default.
- W2896040303 hasRelatedWork W2609744359 @default.
- W2896040303 hasRelatedWork W2774823767 @default.
- W2896040303 hasRelatedWork W2778414945 @default.
- W2896040303 hasRelatedWork W2887147832 @default.
- W2896040303 hasRelatedWork W2898050412 @default.
- W2896040303 hasRelatedWork W2945099397 @default.
- W2896040303 hasRelatedWork W2091856860 @default.
- W2896040303 isParatext "false" @default.
- W2896040303 isRetracted "false" @default.
- W2896040303 magId "2896040303" @default.
- W2896040303 workType "article" @default.