- W2896437095 endingPage "706" @default.
- W2896437095 startingPage "698" @default.
- W2896437095 abstract "Abstract The microstructures and mechanical properties of 60NiTi alloys after solution treated at 980 °C, 1005 °C, 1030 °C and 1055 °C for 2 h, 4 h, 8 h were studied. The results showed that there was undissolved Ni3Ti phase in the specimens after heat treated at 980 °C and 1005 °C for 8 h, and the specimens consisted of Ni3Ti, B2 NiTi and Ni4Ti3 phase. The volume fraction of the Ni4Ti3 phase was about 36% and 46% respectively. After heated at 1030 °C and 1055 °C for 8 h, specimens consisted of B2 NiTi and Ni4Ti3 phase, and the Ni3Ti phase was totally dissolved into the matrix. As a result, the volume fraction of Ni4Ti3 phase increased to 69% and 64%. Higher density of the Ni4Ti3 phase contributed to the higher hardness and higher ultimate compressive strength. The fracture modes of samples after solution treated were mainly quasi-cleavage fracture. The undissolved Ni3Ti phase improved the fracture toughness of the binary alloy. Crack propagation path in Ni3Ti rich area was featured by a zigzag mode, which indicated that Ni3Ti phase displayed positive effect on fracture toughness. The toughening mechanism of 60NiTi with Ni3Ti phase is emphasized." @default.
- W2896437095 created "2018-10-26" @default.
- W2896437095 creator A5018505454 @default.
- W2896437095 creator A5032028908 @default.
- W2896437095 creator A5070429730 @default.
- W2896437095 creator A5073578212 @default.
- W2896437095 date "2019-02-01" @default.
- W2896437095 modified "2023-10-17" @default.
- W2896437095 title "Influence of solution heat treatment on the microstructural evolution and mechanical behavior of 60NiTi" @default.
- W2896437095 cites W1981105108 @default.
- W2896437095 cites W1982793662 @default.
- W2896437095 cites W1994903161 @default.
- W2896437095 cites W2025550622 @default.
- W2896437095 cites W2032093899 @default.
- W2896437095 cites W2035099572 @default.
- W2896437095 cites W2077219775 @default.
- W2896437095 cites W2080959049 @default.
- W2896437095 cites W2093149696 @default.
- W2896437095 cites W2115049183 @default.
- W2896437095 cites W2167409104 @default.
- W2896437095 cites W2189707081 @default.
- W2896437095 cites W2334502136 @default.
- W2896437095 cites W2477547618 @default.
- W2896437095 cites W2559350841 @default.
- W2896437095 cites W2618626847 @default.
- W2896437095 cites W2752565301 @default.
- W2896437095 cites W2761019813 @default.
- W2896437095 cites W340193161 @default.
- W2896437095 cites W630667535 @default.
- W2896437095 doi "https://doi.org/10.1016/j.jallcom.2018.10.015" @default.
- W2896437095 hasPublicationYear "2019" @default.
- W2896437095 type Work @default.
- W2896437095 sameAs 2896437095 @default.
- W2896437095 citedByCount "24" @default.
- W2896437095 countsByYear W28964370952019 @default.
- W2896437095 countsByYear W28964370952020 @default.
- W2896437095 countsByYear W28964370952021 @default.
- W2896437095 countsByYear W28964370952022 @default.
- W2896437095 countsByYear W28964370952023 @default.
- W2896437095 crossrefType "journal-article" @default.
- W2896437095 hasAuthorship W2896437095A5018505454 @default.
- W2896437095 hasAuthorship W2896437095A5032028908 @default.
- W2896437095 hasAuthorship W2896437095A5070429730 @default.
- W2896437095 hasAuthorship W2896437095A5073578212 @default.
- W2896437095 hasConcept C191897082 @default.
- W2896437095 hasConcept C192562407 @default.
- W2896437095 hasConceptScore W2896437095C191897082 @default.
- W2896437095 hasConceptScore W2896437095C192562407 @default.
- W2896437095 hasFunder F4320321001 @default.
- W2896437095 hasLocation W28964370951 @default.
- W2896437095 hasOpenAccess W2896437095 @default.
- W2896437095 hasPrimaryLocation W28964370951 @default.
- W2896437095 hasRelatedWork W2022507789 @default.
- W2896437095 hasRelatedWork W2038064646 @default.
- W2896437095 hasRelatedWork W2070338356 @default.
- W2896437095 hasRelatedWork W2312389078 @default.
- W2896437095 hasRelatedWork W2322722469 @default.
- W2896437095 hasRelatedWork W2937808965 @default.
- W2896437095 hasRelatedWork W3046190049 @default.
- W2896437095 hasRelatedWork W3094131129 @default.
- W2896437095 hasRelatedWork W4231413117 @default.
- W2896437095 hasRelatedWork W4253328832 @default.
- W2896437095 hasVolume "775" @default.
- W2896437095 isParatext "false" @default.
- W2896437095 isRetracted "false" @default.
- W2896437095 magId "2896437095" @default.
- W2896437095 workType "article" @default.