• W2896729525 abstract "The first object of this work was to develop YBa2Cu3O7-x (YBCO) thin films. Initially, Y, BaF2 and Cu were coevaporated with the substrate temperature (TS) 400 °C and the oxygen pressure (pO2) 5 x 10-5 mbar on SrTiO3 substrates with a subsequent high temperature annealing at 890 °C for 15 min in flowing wet oxygen. These films had critical temperatures (Tc) above 90 K and critical current densities (jc) around 5 x 105 A/cm2. The critical current density increased for thinner YBCO films. This corresponded to a decrease in the density of a-axis oriented rods on the c-axis oriented bottom layer. This was also confirmed by x-ray diffraction. Laser deposition was the preferred choice of growth method during the latter application period. Films with a thickness of ~50 nm were grown on LaAlO3, NdGaO3, MgO and SrTiO3 at TS between 760 °C and 830 °C and pO2 at 0.4 mbar or 0.8 mbar. These films had Tc around 90 K, superconducting transition widths of 1-2 K (0.4 K for LaAlO3) and jc above 1 x 106 A/cm2 at 77 K. The second task of this work was to develop a processing method suitable for linewidths down to 1 µm in YBCO films of ~50 nm thickness resulting in reproducible samples with long lifetimes and low contact resistances (.rho.c). A new patterning method was developed where the pattern was made by ion milling through an yttria-stabilized zirconia (YSZ) lift-off mask defined by electron beam lithography. The YBCO film was thus protected by a YSZ layer during processing and as a completed sample. The passivation layer provided a long lifetime of the samples. In situ laser deposited Au contacts resulted in low .rho.c <= 1 x 10-4 .OMEGA.cm2. Both wet etching and ion milling through masks defined by photolithography were also used for patterning of coevaporated and laser deposited films. Thirdly, the photoresponse of the patterned YBCO thin films was investigated. The voltage transient of a current biased sample was studied. For films thicker than the optical penetration depth (> 100 nm), short AlGaAs laser pulses (~50 ps full width at half maximum, FWHM) with .lambda. = 0.8 µm and a laser fluence of 200 nJ/cm2 resulted in photoresponse in the nanosecond regime, characteristic to the bolometric response. For the 50 nm thick patterned laser deposited films, 17 ps (FWHM) laser pulses with .lambda. = 0.8 µm resulted in response times down to 30 ps (FWHM). High frequency resolution was obtained in amplitude modulated laser measurements at .lambda. = 0.8 µm and .lambda. = 10.6 µm (CO2 laser). The photoresponse was observed in the current bias induced resistive state and the normal state. The fast response was followed by a slower bolometric response characterized by the phonon escape from the YBCO film to the substrate and heat diffusion in the substrate. The phonon escape time was estimated to 2-4 ns from both the pulsed laser and amplitude modulated laser measurements. The heat diffusion in the substrate followed a f-n relation. The low laser fluence minimized kinetic inductance contributions to the response. An electron heating model can be used to explain the results. The electron-phonon scattering time was calculated to 1.8 ps. The responsivity at 1 GHz was 1.2 V/W and the noise equivalent power was estimated to 1.5 x 10 -9 W/(Hz1/2)." @default.
• W2896729525 created "2018-10-26" @default.
• W2896729525 creator A5024566940 @default.
• W2896729525 date "1994-01-01" @default.
• W2896729525 modified "2023-09-27" @default.
• W2896729525 title "Photoresponse of Patterned YBa2Cu3O7-x Thin Films" @default.
• W2896729525 hasPublicationYear "1994" @default.
• W2896729525 type Work @default.
• W2896729525 sameAs 2896729525 @default.
• W2896729525 citedByCount "0" @default.
• W2896729525 crossrefType "journal-article" @default.
• W2896729525 hasAuthorship W2896729525A5024566940 @default.
• W2896729525 hasConcept C109613756 @default.
• W2896729525 hasConcept C111368507 @default.
• W2896729525 hasConcept C113196181 @default.
• W2896729525 hasConcept C121332964 @default.
• W2896729525 hasConcept C123609680 @default.
• W2896729525 hasConcept C127313418 @default.
• W2896729525 hasConcept C134132462 @default.
• W2896729525 hasConcept C159985019 @default.
• W2896729525 hasConcept C171250308 @default.
• W2896729525 hasConcept C185592680 @default.
• W2896729525 hasConcept C19067145 @default.
• W2896729525 hasConcept C192562407 @default.
• W2896729525 hasConcept C26873012 @default.
• W2896729525 hasConcept C2777289219 @default.
• W2896729525 hasConcept C2777855556 @default.
• W2896729525 hasConcept C2987373456 @default.
• W2896729525 hasConcept C37982897 @default.
• W2896729525 hasConcept C43617362 @default.
• W2896729525 hasConcept C47542005 @default.
• W2896729525 hasConcept C54101563 @default.
• W2896729525 hasConcept C96410337 @default.
• W2896729525 hasConceptScore W2896729525C109613756 @default.
• W2896729525 hasConceptScore W2896729525C111368507 @default.
• W2896729525 hasConceptScore W2896729525C113196181 @default.
• W2896729525 hasConceptScore W2896729525C121332964 @default.
• W2896729525 hasConceptScore W2896729525C123609680 @default.
• W2896729525 hasConceptScore W2896729525C127313418 @default.
• W2896729525 hasConceptScore W2896729525C134132462 @default.
• W2896729525 hasConceptScore W2896729525C159985019 @default.
• W2896729525 hasConceptScore W2896729525C171250308 @default.
• W2896729525 hasConceptScore W2896729525C185592680 @default.
• W2896729525 hasConceptScore W2896729525C19067145 @default.
• W2896729525 hasConceptScore W2896729525C192562407 @default.
• W2896729525 hasConceptScore W2896729525C26873012 @default.
• W2896729525 hasConceptScore W2896729525C2777289219 @default.
• W2896729525 hasConceptScore W2896729525C2777855556 @default.
• W2896729525 hasConceptScore W2896729525C2987373456 @default.
• W2896729525 hasConceptScore W2896729525C37982897 @default.
• W2896729525 hasConceptScore W2896729525C43617362 @default.
• W2896729525 hasConceptScore W2896729525C47542005 @default.
• W2896729525 hasConceptScore W2896729525C54101563 @default.
• W2896729525 hasConceptScore W2896729525C96410337 @default.
• W2896729525 hasLocation W28967295251 @default.
• W2896729525 hasOpenAccess W2896729525 @default.
• W2896729525 hasPrimaryLocation W28967295251 @default.
• W2896729525 hasRelatedWork W153662291 @default.
• W2896729525 hasRelatedWork W1983336783 @default.
• W2896729525 hasRelatedWork W1997607431 @default.
• W2896729525 hasRelatedWork W1998672177 @default.
• W2896729525 hasRelatedWork W2000705880 @default.
• W2896729525 hasRelatedWork W2011150681 @default.
• W2896729525 hasRelatedWork W2034497661 @default.
• W2896729525 hasRelatedWork W2050839653 @default.
• W2896729525 hasRelatedWork W2088800384 @default.
• W2896729525 hasRelatedWork W2094007548 @default.
• W2896729525 hasRelatedWork W2114423344 @default.
• W2896729525 hasRelatedWork W2137714772 @default.
• W2896729525 hasRelatedWork W2145820371 @default.
• W2896729525 hasRelatedWork W2239977778 @default.
• W2896729525 hasRelatedWork W2253192530 @default.
• W2896729525 hasRelatedWork W2530333531 @default.
• W2896729525 hasRelatedWork W3084523459 @default.
• W2896729525 hasRelatedWork W617439770 @default.
• W2896729525 hasRelatedWork W2183063685 @default.
• W2896729525 hasRelatedWork W252228200 @default.
• W2896729525 isParatext "false" @default.
• W2896729525 isRetracted "false" @default.
• W2896729525 magId "2896729525" @default.
• W2896729525 workType "article" @default.