- W2896863666 abstract "Effect of joint thickness on Type IV cracking behaviour of modified 9Cr-1Mo steel weld joint has been investigated. Creep tests on multi-pass double-V cross weld joint flat specimens of the steel having thicknesses in the range 1–17 mm have been carried out at 923 K (650°C) and 50 MPa stress. Creep rupture life of the weld joint was found to increase with thickness and reached a maximum value around 10 mm of thickness followed by decrease with further increase in thickness. Failure in the weld joints occurred in the soft intercritical region of the heat-affected zone (HAZ). Creep strain localisation was observed at the fractured location and was more in the thinner weld joints than in the thicker weld joint. Creep cavitation in the intercritical region of HAZ close to the unaffected base metal was more extensive at the mid-location of the weld pass, where the HAZ width was relatively larger and hardness was lowest. The type IV cavitation in intercritical HAZ was more extensive in thicker joint, whereas creep strain concentration in the intercritical HAZ was more in thinner weld joint. Creep cavitation in the joint was more pronounced at near mid-thickness locations than those beneath the specimen surface. Joints of intermediate thickness possessed higher creep rupture life because of relatively less accumulation of creep deformation coupled with lower creep cavitation in the intercritical region of HAZ." @default.
- W2896863666 created "2018-10-26" @default.
- W2896863666 creator A5017773465 @default.
- W2896863666 creator A5052620602 @default.
- W2896863666 creator A5053734102 @default.
- W2896863666 creator A5087767252 @default.
- W2896863666 date "2018-10-18" @default.
- W2896863666 modified "2023-10-16" @default.
- W2896863666 title "Influence of joint thickness on Type IV cracking behaviour of modified 9Cr-1Mo steel weld joint" @default.
- W2896863666 cites W1964069811 @default.
- W2896863666 cites W1973547416 @default.
- W2896863666 cites W2001218522 @default.
- W2896863666 cites W2003935699 @default.
- W2896863666 cites W2016535721 @default.
- W2896863666 cites W2026899283 @default.
- W2896863666 cites W2032546848 @default.
- W2896863666 cites W2034183881 @default.
- W2896863666 cites W2035743570 @default.
- W2896863666 cites W2039491563 @default.
- W2896863666 cites W2049593548 @default.
- W2896863666 cites W2050599964 @default.
- W2896863666 cites W2065651279 @default.
- W2896863666 cites W2087506824 @default.
- W2896863666 cites W2089350257 @default.
- W2896863666 doi "https://doi.org/10.1080/09603409.2018.1536410" @default.
- W2896863666 hasPublicationYear "2018" @default.
- W2896863666 type Work @default.
- W2896863666 sameAs 2896863666 @default.
- W2896863666 citedByCount "3" @default.
- W2896863666 countsByYear W28968636662021 @default.
- W2896863666 countsByYear W28968636662022 @default.
- W2896863666 countsByYear W28968636662023 @default.
- W2896863666 crossrefType "journal-article" @default.
- W2896863666 hasAuthorship W2896863666A5017773465 @default.
- W2896863666 hasAuthorship W2896863666A5052620602 @default.
- W2896863666 hasAuthorship W2896863666A5053734102 @default.
- W2896863666 hasAuthorship W2896863666A5087767252 @default.
- W2896863666 hasConcept C121332964 @default.
- W2896863666 hasConcept C127413603 @default.
- W2896863666 hasConcept C146868986 @default.
- W2896863666 hasConcept C149912024 @default.
- W2896863666 hasConcept C159985019 @default.
- W2896863666 hasConcept C18555067 @default.
- W2896863666 hasConcept C191897082 @default.
- W2896863666 hasConcept C192562407 @default.
- W2896863666 hasConcept C19474535 @default.
- W2896863666 hasConcept C204366326 @default.
- W2896863666 hasConcept C207057113 @default.
- W2896863666 hasConcept C40241539 @default.
- W2896863666 hasConcept C57879066 @default.
- W2896863666 hasConcept C58396970 @default.
- W2896863666 hasConcept C66938386 @default.
- W2896863666 hasConceptScore W2896863666C121332964 @default.
- W2896863666 hasConceptScore W2896863666C127413603 @default.
- W2896863666 hasConceptScore W2896863666C146868986 @default.
- W2896863666 hasConceptScore W2896863666C149912024 @default.
- W2896863666 hasConceptScore W2896863666C159985019 @default.
- W2896863666 hasConceptScore W2896863666C18555067 @default.
- W2896863666 hasConceptScore W2896863666C191897082 @default.
- W2896863666 hasConceptScore W2896863666C192562407 @default.
- W2896863666 hasConceptScore W2896863666C19474535 @default.
- W2896863666 hasConceptScore W2896863666C204366326 @default.
- W2896863666 hasConceptScore W2896863666C207057113 @default.
- W2896863666 hasConceptScore W2896863666C40241539 @default.
- W2896863666 hasConceptScore W2896863666C57879066 @default.
- W2896863666 hasConceptScore W2896863666C58396970 @default.
- W2896863666 hasConceptScore W2896863666C66938386 @default.
- W2896863666 hasIssue "3" @default.
- W2896863666 hasLocation W28968636661 @default.
- W2896863666 hasOpenAccess W2896863666 @default.
- W2896863666 hasPrimaryLocation W28968636661 @default.
- W2896863666 hasRelatedWork W1982628048 @default.
- W2896863666 hasRelatedWork W2049047819 @default.
- W2896863666 hasRelatedWork W2357856192 @default.
- W2896863666 hasRelatedWork W2365888955 @default.
- W2896863666 hasRelatedWork W2373584126 @default.
- W2896863666 hasRelatedWork W2377244433 @default.
- W2896863666 hasRelatedWork W2386890856 @default.
- W2896863666 hasRelatedWork W2389951789 @default.
- W2896863666 hasRelatedWork W2899408359 @default.
- W2896863666 hasRelatedWork W3194361552 @default.
- W2896863666 hasVolume "36" @default.
- W2896863666 isParatext "false" @default.
- W2896863666 isRetracted "false" @default.
- W2896863666 magId "2896863666" @default.
- W2896863666 workType "article" @default.