- W2897312945 abstract "The effect of vacuum on weld penetration and porosity formation was investigated in high-power CW CO2 and YAG laser welding. It was consequently confirmed in welding with both lasers that the penetration was slightly deeper in aluminum alloys and was improved in austenitic stainless steel with a decrease in the ambient pressure. It was also revealed that no porosity was present in the materials welded at lower pressures. The reason for no porosity formation in vacuum was examined by observing keyhole behavior, bubble and porosity formation situation and liquid flow in the molten pool during high power YAG laser welding under various conditions through the microfocused X-ray real-time observation system. It was confirmed in the coaxial Ar or He shielding gas that a lot of bubbles were generated near the bottom part of molten pool from the tip of a fluctuated keyhole and resulted in large pores. On the other hand, under the vacuum conditions, no bubbles were formed in the melt pool from the keyhole, although the middle and bottom parts of the keyhole swelled in the molten pool probably because the evaporation of metals was so intense. Moreover, quite different liquid flows were observed between the normal and vacuum welding. Namely, there was a strong molten flow from the bottom of molten pool near the keyhole tip along the solidification interface to the upper rear part in the normal welding, while the liquid flowed upwards along the rear keyhole wall probably due to the strong stream of metallic vapors in vacuum. It is considered in vacuum welding that the liquid flow into the bottom part of the molten pool from the keyhole does not occur because of the direction of evaporated metals toward the upper keyhole outlet. This may exert a beneficial effect on the reduction or prevention of pores or porosity." @default.
- W2897312945 created "2018-10-26" @default.
- W2897312945 creator A5003081430 @default.
- W2897312945 creator A5005858451 @default.
- W2897312945 creator A5026944448 @default.
- W2897312945 creator A5040125207 @default.
- W2897312945 creator A5085862240 @default.
- W2897312945 date "2000-01-01" @default.
- W2897312945 modified "2023-10-05" @default.
- W2897312945 title "Effect of vacuum on penetration and defects in laser welding" @default.
- W2897312945 cites W1980381254 @default.
- W2897312945 cites W2008488713 @default.
- W2897312945 cites W2078352370 @default.
- W2897312945 cites W2897760089 @default.
- W2897312945 doi "https://doi.org/10.2351/1.5059435" @default.
- W2897312945 hasPublicationYear "2000" @default.
- W2897312945 type Work @default.
- W2897312945 sameAs 2897312945 @default.
- W2897312945 citedByCount "8" @default.
- W2897312945 crossrefType "proceedings-article" @default.
- W2897312945 hasAuthorship W2897312945A5003081430 @default.
- W2897312945 hasAuthorship W2897312945A5005858451 @default.
- W2897312945 hasAuthorship W2897312945A5026944448 @default.
- W2897312945 hasAuthorship W2897312945A5040125207 @default.
- W2897312945 hasAuthorship W2897312945A5085862240 @default.
- W2897312945 hasConcept C120665830 @default.
- W2897312945 hasConcept C121332964 @default.
- W2897312945 hasConcept C127413603 @default.
- W2897312945 hasConcept C146868986 @default.
- W2897312945 hasConcept C159985019 @default.
- W2897312945 hasConcept C177250429 @default.
- W2897312945 hasConcept C191897082 @default.
- W2897312945 hasConcept C192562407 @default.
- W2897312945 hasConcept C19474535 @default.
- W2897312945 hasConcept C20480867 @default.
- W2897312945 hasConcept C2776139624 @default.
- W2897312945 hasConcept C2776143536 @default.
- W2897312945 hasConcept C3450827 @default.
- W2897312945 hasConcept C42475967 @default.
- W2897312945 hasConcept C520434653 @default.
- W2897312945 hasConcept C6648577 @default.
- W2897312945 hasConcept C80107235 @default.
- W2897312945 hasConcept C89344249 @default.
- W2897312945 hasConceptScore W2897312945C120665830 @default.
- W2897312945 hasConceptScore W2897312945C121332964 @default.
- W2897312945 hasConceptScore W2897312945C127413603 @default.
- W2897312945 hasConceptScore W2897312945C146868986 @default.
- W2897312945 hasConceptScore W2897312945C159985019 @default.
- W2897312945 hasConceptScore W2897312945C177250429 @default.
- W2897312945 hasConceptScore W2897312945C191897082 @default.
- W2897312945 hasConceptScore W2897312945C192562407 @default.
- W2897312945 hasConceptScore W2897312945C19474535 @default.
- W2897312945 hasConceptScore W2897312945C20480867 @default.
- W2897312945 hasConceptScore W2897312945C2776139624 @default.
- W2897312945 hasConceptScore W2897312945C2776143536 @default.
- W2897312945 hasConceptScore W2897312945C3450827 @default.
- W2897312945 hasConceptScore W2897312945C42475967 @default.
- W2897312945 hasConceptScore W2897312945C520434653 @default.
- W2897312945 hasConceptScore W2897312945C6648577 @default.
- W2897312945 hasConceptScore W2897312945C80107235 @default.
- W2897312945 hasConceptScore W2897312945C89344249 @default.
- W2897312945 hasLocation W28973129451 @default.
- W2897312945 hasOpenAccess W2897312945 @default.
- W2897312945 hasPrimaryLocation W28973129451 @default.
- W2897312945 hasRelatedWork W1977031264 @default.
- W2897312945 hasRelatedWork W2050671190 @default.
- W2897312945 hasRelatedWork W2055938489 @default.
- W2897312945 hasRelatedWork W2359145746 @default.
- W2897312945 hasRelatedWork W2897050960 @default.
- W2897312945 hasRelatedWork W3197485671 @default.
- W2897312945 hasRelatedWork W4239794220 @default.
- W2897312945 hasRelatedWork W4241051546 @default.
- W2897312945 hasRelatedWork W4308153491 @default.
- W2897312945 hasRelatedWork W744322550 @default.
- W2897312945 isParatext "false" @default.
- W2897312945 isRetracted "false" @default.
- W2897312945 magId "2897312945" @default.
- W2897312945 workType "article" @default.