- W2898885178 endingPage "396" @default.
- W2898885178 startingPage "392" @default.
- W2898885178 abstract "Abstract The titanium surface was laser-nitrided to form a TiN intermediate layer and then a bonding porcelain layer was laser fused on it. The specimens were studied by XRD, FE-SEM and EDS tests. A porous titanium nitride layer about 20 μm was synthesized on Ti surface, and the main phases of which were c-TiN and TiN0.3. The Vickers hardness of the TiN layer was 618.68 HV, which is about 3 times of the titanium (202.9 HV). The EDS results showed the TiN layer prepared at 300W was a non-stoichiometri compound with mole ratio of Ti to N about 1:0.621. The porcelain coating laser fused on the TiN layer inherited the columnar structure of TiN, which had a rhombus-like intersecting surface. The highest scratching bonding strength (193.21 ± 23.33 MPa) between TiN layer and Ti was obtained at nitriding power of 300W. The porcelain coating laser fused on the TiN layer inherited the columnar structure of TiN, which had a rhombus-like intersecting surface. The bonding strength between coating and titanium (67.28 MPa) were much higher than the regular bonding strength between the porcelain and Ti (only about 35–40 MPa), which could be ascribed to the good chemical reactivity and wettability between the TiN layer and porcelain." @default.
- W2898885178 created "2018-11-09" @default.
- W2898885178 creator A5010546296 @default.
- W2898885178 creator A5020303601 @default.
- W2898885178 creator A5034558455 @default.
- W2898885178 creator A5038881638 @default.
- W2898885178 creator A5045934605 @default.
- W2898885178 creator A5047431952 @default.
- W2898885178 creator A5062950866 @default.
- W2898885178 date "2019-03-01" @default.
- W2898885178 modified "2023-10-16" @default.
- W2898885178 title "Laser nitriding and fusion of bonding porcelain coating on Ti surface" @default.
- W2898885178 cites W1056064863 @default.
- W2898885178 cites W2031502214 @default.
- W2898885178 cites W2049041323 @default.
- W2898885178 cites W2056203782 @default.
- W2898885178 cites W2109140846 @default.
- W2898885178 cites W2109758852 @default.
- W2898885178 cites W2157721173 @default.
- W2898885178 cites W2210253588 @default.
- W2898885178 cites W2522106937 @default.
- W2898885178 cites W2593050603 @default.
- W2898885178 cites W2594845472 @default.
- W2898885178 cites W2602893313 @default.
- W2898885178 cites W2791379834 @default.
- W2898885178 cites W2795766003 @default.
- W2898885178 cites W2799960220 @default.
- W2898885178 cites W2808607020 @default.
- W2898885178 doi "https://doi.org/10.1016/j.jallcom.2018.10.391" @default.
- W2898885178 hasPublicationYear "2019" @default.
- W2898885178 type Work @default.
- W2898885178 sameAs 2898885178 @default.
- W2898885178 citedByCount "5" @default.
- W2898885178 countsByYear W28988851782019 @default.
- W2898885178 countsByYear W28988851782021 @default.
- W2898885178 countsByYear W28988851782022 @default.
- W2898885178 countsByYear W28988851782023 @default.
- W2898885178 crossrefType "journal-article" @default.
- W2898885178 hasAuthorship W2898885178A5010546296 @default.
- W2898885178 hasAuthorship W2898885178A5020303601 @default.
- W2898885178 hasAuthorship W2898885178A5034558455 @default.
- W2898885178 hasAuthorship W2898885178A5038881638 @default.
- W2898885178 hasAuthorship W2898885178A5045934605 @default.
- W2898885178 hasAuthorship W2898885178A5047431952 @default.
- W2898885178 hasAuthorship W2898885178A5062950866 @default.
- W2898885178 hasConcept C120665830 @default.
- W2898885178 hasConcept C121332964 @default.
- W2898885178 hasConcept C13862629 @default.
- W2898885178 hasConcept C138885662 @default.
- W2898885178 hasConcept C158525013 @default.
- W2898885178 hasConcept C159985019 @default.
- W2898885178 hasConcept C191897082 @default.
- W2898885178 hasConcept C192562407 @default.
- W2898885178 hasConcept C2779227376 @default.
- W2898885178 hasConcept C2781448156 @default.
- W2898885178 hasConcept C41895202 @default.
- W2898885178 hasConcept C520434653 @default.
- W2898885178 hasConceptScore W2898885178C120665830 @default.
- W2898885178 hasConceptScore W2898885178C121332964 @default.
- W2898885178 hasConceptScore W2898885178C13862629 @default.
- W2898885178 hasConceptScore W2898885178C138885662 @default.
- W2898885178 hasConceptScore W2898885178C158525013 @default.
- W2898885178 hasConceptScore W2898885178C159985019 @default.
- W2898885178 hasConceptScore W2898885178C191897082 @default.
- W2898885178 hasConceptScore W2898885178C192562407 @default.
- W2898885178 hasConceptScore W2898885178C2779227376 @default.
- W2898885178 hasConceptScore W2898885178C2781448156 @default.
- W2898885178 hasConceptScore W2898885178C41895202 @default.
- W2898885178 hasConceptScore W2898885178C520434653 @default.
- W2898885178 hasFunder F4320322769 @default.
- W2898885178 hasLocation W28988851781 @default.
- W2898885178 hasOpenAccess W2898885178 @default.
- W2898885178 hasPrimaryLocation W28988851781 @default.
- W2898885178 hasRelatedWork W2043582978 @default.
- W2898885178 hasRelatedWork W2044770104 @default.
- W2898885178 hasRelatedWork W2909514759 @default.
- W2898885178 hasRelatedWork W2937808965 @default.
- W2898885178 hasRelatedWork W2969156832 @default.
- W2898885178 hasRelatedWork W3042175851 @default.
- W2898885178 hasRelatedWork W3097783663 @default.
- W2898885178 hasRelatedWork W3141449356 @default.
- W2898885178 hasRelatedWork W3171862826 @default.
- W2898885178 hasRelatedWork W4294487021 @default.
- W2898885178 hasVolume "777" @default.
- W2898885178 isParatext "false" @default.
- W2898885178 isRetracted "false" @default.
- W2898885178 magId "2898885178" @default.
- W2898885178 workType "article" @default.